ABSTRACT
Improved OLED systems have great potential for next-generation display applications. Carbon nanotubes (CNTs) and the conductive polymers poly (3,4-ethylenedioxythiophene): poly (styrene sulfonate) (PEDOT: PSS) have attracted great interest for advanced applications, such as optoelectronic products. In this paper, the simultaneous enhancement of the conductivity, roughness, and adhesion properties of transparent conductive films with PEDOT: PSS/CNTs is reported. These films prepared by a simple spin-coating process were successfully used to produce high-performance organic light-emitting diodes (OLEDs) with an improved lifetime. Addition of PEDOT: PSS lowered the film sheet resistance and CNTs helped to enhance the stability and maintain the lifetime of the OLEDs. In addition, treatment with methanol and nitric acid changed the morphology of the polymer film, which led to greatly reduced sheet resistance, enhanced substrate adhesion, and reduced film roughness. The best performance of the film (PEDOT: PSS: CNT = 110: 1, W/W) was 100.34 Ω/sq.@ 90.1 T%. High transmittance, low sheet resistance, excellent adhesion, and low roughness (3.11 nm) were achieved synchronously. The fabricated OLED demonstrated a low minimum operating voltage (3 V) and could endure high voltage (20 V), at which its luminance reached 2973 cd/m2. Thus, the incorporation of CNTs within PEDOT: PSS electrodes has great potential for the improvement of the performance of OLED devices.
ABSTRACT
Graphene oxide (GO), reduced graphene oxide (rGO) and carbon nanotubes (CNTs) have their own advantages in electrical, optical, thermal and mechanical properties. An effective combination of these materials is ideal for preparing transparent conductive films to replace the traditional indium tin oxide films. At present, the preparation conditions of rGO are usually harsh and some of them have toxic effects. In this paper, an SnCl2/ethanol solution was selected as the reductant because it requires mild reaction conditions and no harmful products are produced. The whole process of rGO preparation was convenient, fast and environmentally friendly. Then, SEM, XPS, Raman, and XRD were used to verify the high reduction efficiency. CNTs were introduced to improve the film conductive property. The transmittance and sheet resistance were the criteria used to choose the reduction time and the content ratios of GO/CNT. Thanks to the post-treatment of nitric acid, not only the by-product (SnO2) and dispersant in the film are removed, but also the doping effect occurs, which are all conducive to reducing the sheet resistances of films. Ultimately, by combining rGO, GO and CNTs, transparent conductive films with a bilayer and three-dimensional structure were prepared, and they exhibited high transmittance and low sheet resistance (58.8 Ω/sq. at 83.45 T%, 47.5 Ω/sq. at 79.07 T%), with corresponding [Formula: see text] values of 33.8 and 31.8, respectively. In addition, GO and rGO can modify the surface and reduce the film surface roughness. The transparent conductive films are expected to be used in photoelectric devices.
ABSTRACT
In this paper, we used tannic acid (TA) functionalized carbon nanotubes (TCNTs), and silver nanowires (AgNWs) to construct a new type of transparent conductive film (TCF) with a double-layered conductive network structure. The hybrid film exhibits excellent light transmittance, high electrical conductivity, ultra-flexibility, and strong adhesion. These outstanding performances benefit from the filling and adhesion of hydrophilic TCNT layers to the AgNW networks. Besides, we introduced the post-treatment process of mechanical pressing and covering polymer conductive polymer PEDOT:PSS, which obtained three layers of TCNT/AgNW/PEDOT hybrid film and greatly improved the comprehensive properties. The hybrid film can reach a sheet resistance of 9.2 Ω sq-1 with a transmittance of 83.4% at 550 nm wavelength, and a low root mean square (RMS) roughness (approximately 3.8 nm). After 10 000 bends and tape testing, the conductivity and transmittance of the hybrid film remain stable. The resistance of the film has no significant degradation after 14 d of exposure to high temperature of 85 °C and humidity of 85%, indicating excellent stability. The organic light-emitting diodes (OLEDs) with TCNT/AgNW/PEDOT hybrid film as anode exhibit high current density and luminosity, confirming this process has considerable potential application in photovoltaic devices.
ABSTRACT
The amphiphilic graphene derivative was prepared by covalent grafting of graphene oxide (GO) with isophorone diisocyanate and N,N-dimethylethanolamine and then noncovalent grafting of GO with sodium dodecylbenzenesulfonate. The results obtained from infrared spectroscopy, X-ray photoelectron spectroscopy, thermal gravimetric analysis, and X-ray diffraction analysis revealed that the short chains were successfully grafted onto the surface of GO. Subsequently, scanning electron microscopy and optical microscopy results showed that the modified GO (IP-GO) has the best dispersibility and compatibility than GO and reduced GO in the waterborne polyurethane matrix. The relationship between the corrosion resistance of composite coatings and the dispersibility of the graphene derivative and the compatibility of the graphene derivative with a polymer matrix were discussed. The anticorrosive properties were characterized by electrochemical impedance spectroscopy analysis and salt spray tests. Through a series of anticorrosion tests, it is concluded that the anticorrosion performance of a composite coating with 0.3 wt % IP-GO is significantly improved. The excellent anticorrosion performance is due to the perfect dispersion and good compatibility of IP-GO in waterborne polyurethane.