Biodegradation of Poly(3-hydroxybutyrate- co-3-hydroxyhexanoate) Plastic under Anaerobic Sludge and Aerobic Seawater Conditions: Gas Evolution and Microbial Diversity.

Poly(3-hydroxybutyrate- co-3-hydroxyhexanoate) (poly(3HB- co-3HHx)) thermoplastics are a promising biodegradable alternative to traditional plastics for many consumer applications. Biodegradation measured by gaseous carbon loss of several types of poly(3HB- co-3HHx) plastic was investigated under anaerobic conditions and aerobic seawater environments. Under anaerobic conditions, the biodegradation levels of a manufactured sheet of poly(3HB- co-3HHx) and cellulose powder were not significantly different from one another over 85 days with 77.1 ± 6.1 and 62.9 ± 19.7% of the carbon converted to gas, respectively. However, the sheet of poly(3HB- co-3HHx) had significantly higher methane yield ( p ≤ 0.05), 483.8 ± 35.2 mL·g-1 volatile solid (VS), compared to cellulose controls, 290.1 ± 92.7 mL·g-1 VS, which is attributed to a greater total carbon content. Under aerobic seawater conditions (148-195 days at room temperature), poly(3HB- co-3HHx) sheets were statistically similar to cellulose for biodegradation as gaseous carbon loss (up to 83% loss in about 6 months), although the degradation rate was lower than that for cellulose. The microbial diversity was investigated in both experiments to explore the dominant bacteria associated with biodegradation of poly(3HB- co-3HHx) plastic. For poly(3HB- co-3HHx) treatments, Cloacamonales and Thermotogales were enriched under anaerobic sludge conditions, while Clostridiales, Gemmatales, Phycisphaerales, and Chlamydiales were the most enriched under aerobic seawater conditions.

Degradable Polycaprolactone and Polylactide Homopolymer and Block Copolymer Brushes Prepared by Surface-Initiated Polymerization with Triazabicyclodecene and Zirconium Catalysts.

Surface-initiated ring-opening polymerization (SI-ROP) of polycaprolactone (PCL) and polylactide (PLA) polymer brushes with controlled degradation rates were prepared on oxide substrates. PCL brushes were polymerized from hydroxyl-terminated monolayers utilizing triazabicyclodecene (TBD) as the polymerization catalyst. A consistent brush thickness of 40 nm could be achieved with a reproducible unique crystalline morphology. The organocatalyzed PCL brushes were chain extended using lactide in the presence of zirconium n-butoxide to successfully grow PCL/PLA block copolymer (PCL-b-PLA) brushes with a final thickness of 55 nm. The degradation properties of "grafted from" PCL brush and the PCL-b-PLA brush were compared to "grafted to" PCL brushes, and we observed that the brush density plays a major role in degradation kinetics. Solutions of methanol/water at pH 14 were used to better solvate the brushes and increase the kinetics of degradation. This framework enables a control of degradation that allows for the precise removal of these coatings.