ABSTRACT
A dual-emission ratio-fluorescent sensing nanohybrid based on Radix Hedysari green-synthesized carbon quantum dots (CDs) and glutathione-functionalized gold nanoclusters (GSH-AuNCs) had been developed for the determination of cefodizime sodium (CDZM). The designed fluorescence nanohybrid had two significant fluorescence emission peaks at 458 nm and 569 nm when excited at 360 nm, which was attributed to the CDs and GSH-AuNCs. With the addition of CDZM, the fluorescence at 458 nm was slightly weakened while the fluorescence at 569 nm was enhanced obviously. Based on the relationship between the I569/I458 fluorescence intensity ratio and the concentration of CDZM, the designed nanohybrid exhibited a good linearity range of 1.0-1000.0 µM and the limit of detection (LOD) was 0.19 µM. The method was finally applied in the detection of CDZM in urine, showing the potential applications in complicated biological samples.
Subject(s)
Glutathione , Gold , Metal Nanoparticles , Quantum Dots , Quantum Dots/chemistry , Humans , Gold/chemistry , Metal Nanoparticles/chemistry , Glutathione/urine , Glutathione/chemistry , Limit of Detection , Spectrometry, Fluorescence/methods , Carbon/chemistry , Cephalosporins/urine , Cephalosporins/chemistry , FluorescenceABSTRACT
Seeking novel high-performance elastocaloric materials with low critical stress plays a crucial role in advancing the development of elastocaloric refrigeration technology. Here, as a first attempt, the elastocaloric effect of TiZrNbAl shape memory alloy at both room temperature and finite temperatures ranging from 245 K to 405 K, is studied systematically. Composition optimization shows that Ti-19Zr-14Nb-1Al (at.%), possessing excellent room-temperature superelasticity with a critical stress of around 100 MPa and a small stress hysteresis of around 70 MPa and outstanding fracture resistance with a compressive strain of 20% and stress of 1.7 GPa, demonstrates a substantial advantage as an elastocaloric refrigerant. At room temperature, a large adiabatic temperature change (ΔTad) of -6.7 K is detected, which is comparable to the highest value reported in the Ti-based alloys. A high elastocaloric cyclic stability, with almost no degradation of ΔTad after 4000 cycles, is observed. Furthermore, the sizeable elastocaloric effect can be steadily expanded from 255 K to 395 K with a temperature window of as large as 140 K. A maximum ΔTad of -7.9 K appears at 355 K. The present work demonstrates a promising potential of TiZrNbAl as a low critical stress and low hysteresis elastocaloric refrigerant.