Recycling of Flexible Polyurethane Foams by Regrinding Scraps into Powder to Replace Polyol for Re-Foaming.

In the context of protecting the ecological environment and carbon neutrality, high-value recycling of flexible polyurethane foam (F-PUF) scraps, generated in the production process, is of great significance to save petroleum raw materials and reduce energy consumption. In the present study, F-PUF scraps were ground into powder by strong shear regrinding using two-roll mill and then reused as a partial replacement of polyol for re-foaming. A series of characterizations were employed to investigate the effect of milling cycles, roller temperatures, and content of the powder on the properties of the powder and F-PUF containing powder. It was revealed that the mechanochemical effect induced breaking of the cross-linking structure and increased activity of the powder. The volume mean diameter (VMD) of powder prepared with 7 milling cycles, at room temperature, is about 97.73 µm. The microstructure and density of the F-PUF containing powder prepared in the above-mentioned manner to replace up to 15 wt.% polyol, is similar to the original F-PUF, with resilience 49.08% and compression set 7.8%, which indicates that the recycling method will play an important role in industrial applications.

Low-Temperature Mechano-Chemical Rubber Reclamation Using Terpinene as a Swelling Agent to Enhance Bond-Breaking Selectivity.

Common swelling agents used in the mechano-chemical rubber devulcanization process usually require high temperatures to achieve satisfactory swelling effects, which results in severe production of pollutants and reduces the selectivity of bond scissions. This work presents an environmentally friendly swelling agent, terpinene, which can swell the rubber crosslink structures at low temperatures. Both a rubber swelling experiment and a rubber reclaiming experiment with a mechano-chemical devulcanization method are conducted to explore the swelling effects of terpinene. After soaking in terpinene at 60 °C for 90 min, the length elongation of the rubber sample reaches 1.55, which is much higher than that in naphthenic oil and is comparable to that in toluene. When adding 3 phr of terpinene for every 100 phr of waste rubber during the reclaiming process, the bond scissions exhibit high selectivity. After revulcanization, the reclaimed rubbers have a tensile strength of 17 MPa and a breaking elongation of 400%. Consequently, the application of terpinene as the swelling agent in the LTMD method can greatly improve the properties of reclaimed rubbers, thereby enhancing the dual value for the economy and environment.