Synthesis and Characterization of Triticale Starch-Based Hydrogel for pH Responsive Controlled Diffusion.

Considering the FAO perspectives for agriculture toward 2030, many natural sources will be no longer profitable for the synthesis of many biomaterials. Triticale (X Triticosecale Wittmack) is a cereal crop synthesized to withstand those marginal conditions; however, it is primarily used as fodder worldwide. We reported for the first time the synthesis of a natural anionic hydrogel with gastrointestinal pH stimulus-response as a new alternative of smart material, based on Eronga triticale starch as sustainable biomass, using citrate (pK a ∼3.1, 4.7, and 6.4) as cross-linking agent. The scanning electron microscopy and X-ray diffraction exhibited A and B-type starch granules, and semicrystallinity A-type. The presence of the anionic sensing group (COOH) was verified by infrared spectroscopy, the interactions by hydrogen bonds between starch and glycerol and esterification between starch and citric acid were identified by 1H NMR spectra, and through thermal analysis hydrogels exhibited four endothermic curves (179-319 °C, ∼0.711-39 kJ/mol E a). The results showed that the slight addition of glycerol increases the thermal stability, but a higher amount of glycerol decreases the intermolecular forces affecting the thermal stability contrary, the mechanical properties could be benefited. The rheological analyses showed viscoelastic tendency (G' > G″) with high stability (Tanδ < 1) in frequency, time, and strain sweeps. Gastrointestinal pH sensitivity (∼2-7.8) was verified (α ≤ 0.01) following Fick's diffusive parameters, which resulted in a tendency to gradually release BSA with increasing pH ∼3-7 by anomalous and case-II diffusion, showing greater release at pH ∼7.8/3.5 h (80-96%). We aim to expand the biomaterials area focusing on triticale starch due to its limited reported investigations, low-cost, green modification, and its rheological performance as plastic.

Electrospun Cellulose Acetate Membranes Coated with Polypyrrole and Their Potential Application in the Recovery of Metals.

The purpose of this paper is to study the effect of polypyrrole (PPy) on cellulose acetate (CA) membranes prepared by the electrospinning technique (controlled variables) in the recovery of gold complexes of aqueous solutions that are environmentally ecofriendly. CA-PPy membranes were characterized by SEM, EDS, FTIR spectroscopy, contact angle measurements, electrical conductivity, and mechanical tests. They were submerged in two aqueous solutions using two gold complexes, AuI2 - and AuBr4 -, at room temperature. The recovery percentage was evaluated for several hours using the atomic adsorption technique for both complexes. The main findings indicate that the percentage of recovery in the first hours of the test was very high (>80%). The adsorption efficiency maxima were similar for both complexes (91%). The Langmuir model suggests the formation of a monolayer on the surface. The electrical conductivity did not change over time, and the mechanical properties indicate reuse in several experiments. Furthermore, the theoretical analysis showed that the system is helpful at acidic pH, funding its minimum energy. It is shown in this study that the used CA-PPy membranes show adsorption, absorption, and reusable properties with the effective recovery of the complexes in the first hours. These membranes could substitute for materials that are not environmentally ecofriendly.