An Ionic Liquid Supramolecular Gel Electrolyte with Unique Wide Operating Temperature Range Properties for Zinc-Ion Batteries.

Zinc-ion batteries are promising candidates for large-scale energy storage. The side reactions of the hydrogen evolution reaction (HER) and zinc dendrite growth are major challenges for developing high-performance zinc-ion batteries. In this paper, a supramolecular gel electrolyte (BLO-ILZE) was self-assembled in an ionic liquid (EMIMBF4) with zinc tetrafluoroborate (Zn(BF4)2) on the separator in situ to obtain a gel electrolyte used in zinc-ion batteries. BLO-ILZE is demonstrated to significantly enhance conductivity over a broad temperature range between -70 and 100 °C. Interestingly, through testing and fitting, it is found that the supramolecular gel electrolyte satisfies the liquid state law over a wide temperature range, and even achieves high conductivity (2.12 mS cm-1) at -40 °C. It is equivalent to the conductivity of aqueous zinc-ion batteries (ZnSO4/H2O) at -10 °C, which is 2.33 mS cm-1. Moreover, the supramolecular gel electrolyte can effectively inhibit the HER, thus exhibiting a longer lifetime in Zn/Zn cells for 3470 h at 1 mA cm-2 compared to the aqueous zinc-ion batteries with the Zn(BF4)2 aqueous electrolyte (400 h at 1 mA cm-2). The assembled V2O5/BLO-ILZE/Zn full cells also showed cycling performance, with 5000 cycles at 0.5 mA g-1 at room temperature, a capacity of 98%, and a coulombic efficiency of about 100%.

MOF-modified dendrite-free gel polymer electrolyte for zinc-ion batteries.

Zinc-ion batteries are promising candidates for large-scale energy storage, and gel polymer electrolytes (GPEs) play an important role in zinc-ion battery applications. Metal-organic frameworks (MOFs) are characterized by large specific surface areas and ordered pores. This highly ordered microporous structure provides a continuous transport channel for ions, thus realizing the high-speed transmission of ions. In this paper, an MOF-modified dendrite-free GPE was designed. The incorporation of MOF particles not only reduces the crystallinity of the polymer, increases the motility of the molecular chains, and facilitates the transfer of Zn2+, but also attracts anions to reduce polarization during electrochemical reactions. It was shown that this MOF-modified gel polymer electrolyte has a higher ionic conductivity compared to other PVDF-based polymer electrolytes (approximate range of 2 × 10-4 to 3 × 10-3 S cm-1), with a very high conductivity (1.63 mS cm-1) even at -20 °C. The Zn/Zn symmetric cell could maintain operation for more than 3600 h at a current density of 1 mA cm-2, and SEM showed that the MOF-modified gel electrolyte had uniform Zn2+ deposition.

Using polyacrylamide hydrogel to adsorb chloride ions in cement-based materials.

Concrete material is an important engineering material for modern marine engineering construction, but the presence of chloride ions in sea sand and seawater can cause corrosion of reinforcing steel, which greatly endangers the safety of reinforced concrete structures. Gel is an environmental friendly functional material which has the functions of exchange and adsorption of ions. Therefore, in this paper, polyacrylamide (PAM) gels were prepared for chloride ions adsorption in a reinforced concrete system. The chloride ions adsorption behavior of PAM gel in simulated seawater and cement were investigated and the maximum adsorption capacity of chloride ions in simulated seawater was 32.67 mg g-1. In addition, compared with the cement sample without gel, the chloride ion content in the cement sample containing 1.5 wt% gel was reduced 46.8% at a depth of 0-2.5 mm from the sample's surface. The results showed that PAM gel can effectively adsorb the chloride ion and improve the chloride ion penetration resistance in cement because the three-dimensional network structure of PAM gels allowed chloride ions to enter the inside of the gel. This gel has potential applications in the field of marine construction.