Investigation of the cap layer for improved GeSn multiple quantum well laser performance.

The study of all-group-IV SiGeSn lasers has opened a new avenue to Si-based light sources. SiGeSn heterostructure and quantum well lasers have been successfully demonstrated in the past few years. It has been reported that, for multiple quantum well lasers, the optical confinement factor plays an important role in the net modal gain. In previous studies, adding a cap layer was proposed to increase the optical mode overlap with the active region and thereby improve the optical confinement factor of Fabry-Perot cavity lasers. In this work, SiGeSn/GeSn multiple quantum well (4-well) devices with various cap layer thicknesses, i.e., 0 (no cap), 190, 250, and 290 nm, are grown using a chemical vapor deposition reactor and characterized via optical pumping. While no-cap and thinner-cap devices only show spontaneous emission, the two thicker-cap devices exhibit lasing up to 77 K, with an emission peak at 2440 nm and a threshold of 214 kW/cm2 (250 nm cap device). The clear trend in device performance disclosed in this work provides guidance in device design for electrically injected SiGeSn quantum well lasers.

Transfer-printing-enabled GeSn flexible resonant-cavity-enhanced photodetectors with strain-amplified mid-infrared optical responses.

Mid-infrared (MIR) flexible photodetectors (FPDs) constitute an essential element for wearable applications, including health-care monitoring and biomedical detection. Compared with organic materials, inorganic semiconductors are promising candidates for FPDs owing to their superior performance as well as optoelectronic properties. Herein, for the first time, we present the use of transfer-printing techniques to enable a cost-effective, nontoxic GeSn MIR resonant-cavity-enhanced FPDs (RCE-FPDs) with strain-amplified optical responses. A narrow bandgap nontoxic GeSn nanomembrane was employed as the active layer, which was grown on a silicon-on-insulator substrate and then transfer-printed onto a polyethylene terephthalate (PET) substrate, eliminating the unwanted defects and residual compressive strain, to yield the MIR RCE-FPDs. In addition, a vertical cavity was created for the GeSn active layer to enhance the optical responsivity. Under bending conditions, significant tensile strain up to 0.274% was introduced into the GeSn active layer to effectively modulate the band structure, extend the photodetection in the MIR region, and substantially enhance the optical responsivity to 0.292 A W-1 at λ = 1770 nm, corresponding to an enhancement of 323% compared with the device under flat conditions. Moreover, theoretical simulations were performed to confirm the strain effect on the device performance. The results demonstrated high-performance, nontoxic MIR RCE-FPDs for applications in flexible photodetection.