ABSTRACT
This study aimed to evaluate the bonding performance of self-adhesive flowable resin composites (SARs) to bovine teeth. Three SARs, one experimental, and two commercially available products, were used. The study parameters were shear bond strength (SBS), microleakage, and scanning electron microscopy (SEM) evaluation of bonding interfaces. The SBS of the materials was 14.1-15.1 MPa to enamel, 22.2-23.2 MPa to etched enamel, and 7.4-10.7 MPa to dentin. Specimens with pre-etching showed lower microleakage scores than those without pre-etching. SEM images of the interfaces of the materials showed excellent adaptation regardless of the substrate or etching mode. The study results indicate that enamel pre-etching can improve the bonding performance of SARs.
Subject(s)
Acid Etching, Dental , Composite Resins , Dental Bonding , Dental Enamel , Materials Testing , Microscopy, Electron, Scanning , Shear Strength , Surface Properties , Animals , Cattle , Composite Resins/chemistry , Dental Bonding/methods , Dentin , In Vitro Techniques , Dental Leakage , Dental Stress AnalysisABSTRACT
Computer-aided design-computer-aided manufacturing (CAD-CAM) systems have been widely used as a fabrication method for restorations because of their high efficiency and accuracy, which significantly reduces fabrication time. However, molars with insufficient clearance or short clinical crown lengths require retention holes or grooves on the preparation, making it difficult to replicate the shapes with the CAM milling system. In these cases, restorations using the lost-wax method are selected. This article focuses on one-piece endodontic crowns (endocrowns) fabricated with a CAD-CAM system (CAD-CAM endocrowns), in which their posts and crowns are integrated. Articles from July 2012 to August 2023 were searched in PubMed with the keyword "endocrown". This review discusses the application of CAD-CAM endocrowns to molars from the viewpoint of model experiment (fracture resistance, adaptation) and clinical research. This technique, which allows margins and internal gaps to be set within the clinically acceptable range, is reported to be an effective way of restoring molars with high survival rates in clinical research.
ABSTRACT
This study aimed to observe and compare the resin luting cement (RLC)/dentin interfaces of different types of RLC systems with scanning electron microscopy (SEM). This study evaluated six self-adhesive resin luting cement systems (SARLCs), four systems combining a SARLC with a tooth primer (SARLCPs), and six conventional resin luting cement systems (CVRLCs). Cured resin composite rods were bonded to bovine dentin using RLCs in different etching modes. The morphological features at the interfaces were observed using SEM. Although all RLCs in etch-&-rinse (ER) mode showed a clear hybrid layer, most SARLCs had a thinner and more porous hybrid layer than the SARLCPs and CVRLCs. All SARLCPs with primer and CVRLCs showed a thin high-density layer below the primer layer in both etching modes. CVRLCs and SARLCPs with primer treatment systems may be more versatile and reliable when compared to simplified RLC systems.
Subject(s)
Dental Bonding , Resin Cements , Animals , Cattle , Microscopy, Electron, Scanning , Resin Cements/chemistry , Dental Cements , Dentin-Bonding Agents/chemistry , Composite Resins/chemistry , Dentin , Materials Testing , Surface PropertiesABSTRACT
OBJECTIVES: This study aimed to investigate the immediate dentin bond performance and bond durability of self-adhesive resin luting cements (RLCs) in combination with universal adhesives in different curing modes. METHODS: Two self-adhesive RLCs were used with universal adhesives as primers. They were also used alone as self-adhesive RLCs. Two multiple-step RLC systems were used as comparison materials. To measure the shear bond strength (SBS) in different curing modes, 12 specimens were prepared for each group. Stainless-steel rods were bonded to bovine dentin, and the bonded specimens were assigned to the baseline group (stored for 24 h) and artificially aged group (thermal cycling [TC], 10,000 cycles). After each storage period, the SBS of the bonded specimens was measured. The Knoop hardness number (KHN) of the cured RLCs was measured with or without primer application in different curing modes at 24 h and after 10,000 TC. The representative RLC/dentin interfaces were observed using scanning electron microscopy (SEM). RESULTS: Dentin SBS was significantly influenced by the RLC system but not by the curing mode. Self-adhesive RLCs alone showed significantly lower SBS values than self-adhesive RLCs with primer regardless of the curing mode or storage period. The storage period, curing mode, and RLC system significantly influenced the KHN. SIGNIFICANCE: The use of universal adhesives as a primer may help enhance the immediate dentin bond performance and bond durability of self-adhesive RLCs.