ABSTRACT
AIM: The aim of this study was to investigate the adhesive performance of three different universal adhesives to repair aged amalgam by composite resins with or without Alloy Primer. MATERIALS AND METHODS: Sixty amalgam samples were prepared, aged, and randomly divided into 12 main groups according to adhesive procedures used. Composite buildups were placed on amalgam surfaces. After micro-shear bonding test, the fracture surfaces were examined under the scanning electron microscopy statistical analysis was performed using two-way analysis of variance and Tukey's post hoc tests. RESULTS: Without use of Alloy Primer, all of the universal adhesives provided similar bond strength values with conventional adhesives (P > 0.05); however, an Alloy Primer significantly increased the bond strength values of universal adhesives (P < 0.05). No significant difference in bond strength values was noted for conventional adhesives with or without Alloy Primer (P > 0.05) except for Clearfil SE Bond (P < 0.05). CONCLUSIONS: Within the limitations of this study, it can be concluded; using Alloy Primer before universal adhesives increased the bond strength significantly.
ABSTRACT
This study evaluated the bond strength of different adhesive agents to TheraCal LC and mineral trioxide aggregate (MTA) and examined the morphologic changes of these materials with different surface treatments. A total of 120 specimens, 60 of MTA Angelus (AMTA), and 60 of TheraCal LC, were prepared and divided into six subgroups according to the adhesive agent used; these agents included Scotchbond Multipurpose, Clearfil SE Bond, Clearfil Protect Bond, Clearfil S3 Bond, OptiBond All-in-One, and G-aenial Bond. After application of adhesive agents, Filtek Z250 composite resin was placed onto the specimens. Shear bond strengths were measured using a universal testing machine, followed by examination of the fractured surfaces. The surface changes of the specimens were observed using scanning electron microscopy. Data were compared by two-way analysis of variance. Although no significant differences were found among the bond strengths of different adhesives to AMTA (p = 0.69), a significant difference was found in terms of bond strengths of different adhesives to the TheraCal LC surface (p < 0.001). The total-etch adhesive system more strongly bonded to TheraCal LC compared to the bond with other adhesives. TheraCal LC bonded significantly more strongly than AMTA regardless of the adhesive agents tested. Resin-modified calcium silicate showed higher bond strength than AMTA in terms of the composite bond to these materials with different bonding systems. On the other hand, the highest shear bond-strength values were found for composite bonds with the combination of TheraCal LC and the total-etch adhesive system. SCANNING 38:403-411, 2016. © 2015 Wiley Periodicals, Inc.