ABSTRACT
Graphene is a popular material with outstanding properties due to its single layer. Graphene and its oxide have been put to the test as nano-sized building components for separation membranes with distinctive structures and adjustable physicochemical attributes. Graphene-based membranes have exhibited excellent water and gas purification abilities, which have garnered the spotlight over the past decade. This work aims to examine the most recent science and engineering cutting-edge advances of graphene-based membranes in regard to design, production and use. Additional effort will be directed towards the breakthroughs in synthesizing graphene and its composites to create various forms of membranes, such as nanoporous layers, laminates and graphene-based compounds. Their efficiency in separating and decontaminating water via different techniques such as cross-linking, layer by layer and coating will also be explored. This review intends to offer comprehensive, up-to-date information that will be useful to scientists of multiple disciplines interested in graphene-based membranes.
ABSTRACT
The first objective of this experimental study is the assessment of the alkali activation potential of two types of fayalitic slags, an as-received one (FS) and the one obtained after plasma treatment (FSP) of the initial FS, for the production of alkali activated materials (AAMs). Furthermore, the second objective is the elucidation of the co-valorization potential of FS and FSP slags when mixed with ferronickel (FeNi) slag (LS). The alkaline activating solution used was a mixture of sodium hydroxide (NaOH) and sodium silicate (Na2SiO3). The effect of various operating parameters, such as H2O/Na2O and SiO2/Na2O ratios present in the activating solution, curing temperature, curing period and ageing period on the compressive strength, density, water adsorption, porosity and toxicity of the produced AAMs was explored. The structural integrity of selected AAMs was investigated after firing specimens for 6 h at temperature up to 500 °C, immersion in distilled water and acidic solution or subjection to freeze-thaw cycles for a period of 7 or 30 days. The results of this study show that FS- and FSP-based AAMs acquire compressive strength of 44.8 MPa and 27.2 MPa, respectively. When FS and FSP were mixed with LS at 50:50%wt ratios the compressive strength of the produced specimens increased to 64.3 MPa and 45.8 MPa, respectively. Furthermore, selected AAMs produced after co-valorisation of slags retained sufficient compressive strength after firing at 500 °C, 45-68 MPa, and exhibited very low toxicity. These findings prove the alkali activation potential of fayalitic slags as well as their co-valorization with ferronickel slag for the production of AAMs, an approach which is in line with the principles of zero-waste and circular economy.