Temperature selectivity for single phase hydrothermal synthesis of PEG-400 coated magnetite nanoparticles.

Herein, we have presented a detailed investigation of the temperature effect on hydrothermal synthesis of Fe3O4 magnetic nanoparticles (MNPs). The appearance of single-phase cubic spinel Fe3O4 at and above critical temperature provides a clear indication that temperature plays a crucial role in the single-phase synthesis of the Fe3O4 MNPs. A detailed investigation of the structural, magnetic and spin dynamic properties of PEG-400 coated Fe3O4 MNPs synthesized by a facile hydrothermal method at different temperatures (120 °C, 140 °C, 160 °C and 180 °C for 16 hours) has been presented. The single-phase cubic magnetite structure with high crystallinity was found in the samples synthesized at 160 and 180 °C and confirmed from XRD results, whereas samples prepared at 120 and 140 °C are of mixed phase (α-Fe2O3 and Fe3O4). The magnetic hysteresis curves reveal that saturation magnetization and coercivity of MNPs enhanced systematically with the increase in the reaction temperature from 120 °C to 180 °C. Maximum saturation magnetization (88.98 emu g-1) and coercivity (134.16 Oe) were found for the sample synthesized at 180 °C. Furthermore, ferromagnetic resonance (FMR) spectra obtained for samples synthesised at higher temperatures indicate a lower value of the line width due to the high magnetic ordering in the samples. Also, the resonance field decreased, and the g-value increased due to enhancement in magnetization for the single-phase samples synthesized at higher reaction temperatures. The spin resonance properties obtained from fitting the FMR data clearly indicate that a large spin-orbit coupling was observed for the single phase Fe3O4 MNPs and excellent magnetic properties were obtained from the static magnetic measurements.

Microwave spin resonance investigation on the effect of the post-processing annealing of CoFe2O4 nanoparticles.

A novel investigation on the finite-size effects on the spin resonance properties of cobalt ferrite (CoFe2O4) nanoparticles has been performed using a room temperature ferromagnetic resonance (FMR) technique. A single broad spectrum was obtained for the CoFe2O4 nanoparticle samples, which indicated that all the samples were showing ferromagnetic characteristics. An asymmetric FMR line shape with a hefty trailing section was obtained due to the high magneto-crystalline anisotropy in CoFe2O4 nanoparticles, which changed with the size distribution. The resonance field for the samples shifted to a higher value due to the increase in the magneto-crystalline anisotropy in the CoFe2O4 nanoparticles with an increase in size. A systematic change in the resonance field and line width was observed with the change in the size distribution of the particles. Initially, it decreased with an increase in the size of the particles and increased after the critical size range. The critical size range is the imprint of the shift of the magnetic domain from a single domain to multi domain. The line width increased at higher annealing temperatures due to the enhancement in the dipole-dipole interaction, which led to a higher spin concentration as well as magneto-crystalline anisotropy. Furthermore, the saturation magnetization (M s) as well as 'M r/M s' increased from 37.7 to 71.4 emu g-1 and 0.06 to 0.31, respectively. The highest coercivity (750.9 Oe) and anisotropy constant (4.62 × 104 erg cm-3) were found for the sample annealed at 700 °C, which can be corroborated by the literature as the critical annealing temperature at which CoFe2O4 nanoparticles shift from single domain nanoparticles to multi-domain nanoparticles. Post-processing annealing is critical in advanced processing techniques and spin dynamics plays a vital role in various interdisciplinary areas of applications.

Structural, magnetic and magneto-optical studies of Mn/Al bilayer thin films on GaAs substrates.

Ferromagnetism and magnetic anisotropy in Mn-Al thin films can be of great interest due to their applications in spintronic components and as rare-earth free magnets. Temperature-dependent uniaxial anisotropy has been observed in ferromagnetic MnAl thin films, which is attributed to the modification of the tetragonal lattice distortion with the change in annealing temperature, confirmed by VSM, MOKE and XRD results; the annealing time did not affect the magnetic anisotropy. A simple evaporation technique was used to deposit the Mn/Al bilayer thin films (thickness ∼ 64 nm) on GaAs substrates. A comprehensive study of the effect of annealing temperature as well as annealing time on structural, microstructural, magnetic and magneto-optical properties are reported in this paper. The ferromagnetic phase was enriched in annealed samples, which was confirmed by XRD, MOKE and magnetic hysteresis loops. XRD results revealed that the ferromagnetic τ-phase was enhanced in annealed films with the increase in annealing temperature ≥ 400 °C. Surface roughness was estimated from the AFM micrographs and was found to be increased, whereas the mean grain size was decreased on annealing the as-deposited Mn/Al bilayer thin film. The gradual increase in magnetic coercivity was found on increasing the annealing temperature. It is interesting to note that the magnetic easy axis can be tuned by changing the annealing temperature of MnAl thin films, and the easy axis changes from perpendicular to parallel direction of the film plane when the annealing temperature varies from 400 °C to 500 °C. MOKE results were also found to be consistent with the magnetic results.