Ceria-Catalyzed Hydrolytic Cleavage of Sulfonamides.

Nanoceria is a promising nanomaterial for the catalytic hydrolysis of a wide variety of substances. In this study, it was experimentally demonstrated for the first time that CeO2 nanostructures show extraordinary reactivity toward sulfonamide drugs (sulfadimethoxine, sulfamerazine, and sulfapyridine) in aqueous solution without any illumination, activation, or pH adjustment. Hydrolytic cleavage of various bonds, including S-N, C-N, and C-S, was proposed as the main reaction mechanism and was indicated by the formation of various reaction products, namely, sulfanilic acid, sulfanilamide, and aniline, which were identified by HPLC-DAD, LC-MS/MS, and NMR spectroscopy. The kinetics and efficiency of the ceria-catalyzed hydrolytic cleavage were dependent on the structure of the sulfonamide molecule and physicochemical properties of Nanoceria prepared by three different precipitation methods. However, in general, all three ceria samples were able to cleave SA drugs tested, proving the robust and unique surface reactivity toward these compounds inherent to cerium dioxide. The demonstrated reactivity of CeO2 to molecules containing sulfonamide or even sulfonyl (and similar) functional groups may be significant for both heterogeneous catalysis and environmentally important degradation reactions.

Effect of Surface Treatment of Nanocrystalline CeO2 on Its Dephosphorylation Activity and Adsorption of Inorganic Phosphates.

The surface of nanocrystalline cerium oxide (CeO2) was treated with various chemical agents by a simple postmodification method at 25 °C and atmospheric pressure. Hydrogen peroxide, ammonium persulfate, deionized water, ascorbic acid, and ortho-phosphoric acid were used in order to study and evaluate their effect on surface materials, such as surface area, crystallite size, number of surface hydroxyl groups, particle morphology, and Ce3+/Ce4+ ratio. Paraoxon-methyl (PO) decomposition and inorganic phosphate adsorption were used to evaluate the effect of surface treatment on catalytic and adsorption properties. CeO2 surface was studied by Fourier transform infrared spectroscopy, Raman spectroscopy, X-ray photoelectron spectroscopy, and acid-base titration. While the treatment procedure affected the number of surface hydroxyl groups and the amount of bulk surface oxygen vacancies, only negligible changes were observed in the Ce3+/Ce4+ ratio. Interestingly, surface treatment affected the ability to decompose PO, but only a small effect on inorganic phosphate adsorption was observed, indicating the robustness of CeO2 for the latter. A mechanism for possible interaction of the used chemicals with the CeO2 surface was proposed.

Impact of Ce/Zr Ratio in the Nanostructured Ceria and Zirconia Composites on the Selective CO2 Adsorption.

High surface-area, mesoporous CeO2, ZrO2, and Ce-Zr composite nanoparticles were developed using the hydrothermal template-assisted synthesis method. Samples were characterized using XRD, N2 physisorption, TEM, XPS, and FT-IR spectroscopic methods. The CO2 adsorption ability of the obtained materials was tested under dynamic and equilibrium conditions. A high CO2 adsorption capacity in CO2/N2 flow or CO2/N2/H2O was determined for all studied adsorbents depending on their composition flow. A higher CO2 adsorption was registered for Ce-Zr composite nanomaterials due to the presence of strong O2- base sites and enriched surface oxygen species. The role of the Ce/Zr ratio is the process of the formation of highly active and selective adsorption sites is discussed. The calculated heat of adsorption revealed the processes of chemisorption and physisorption. Experimental data could be appropriately described by the Yoon-Nelson kinetic model. The composites reused in five adsorption/desorption cycles showed a high stability with a slight decrease in CO2 adsorption capacities in dry flow and in the presence of water vapor.

Electrospun PA6 Nanofibers Bearing the CeO2 Dephosphorylation Catalyst.

Two types of CeO2 nanoparticles (CeNPs) prepared by low-temperature (<100 °C) precipitation methods in water were successfully immobilized in a matrix of electrospun PA6 nanofibers. The colloidal solutions of CeNPs in AcOH were directly mixed with the polymer solution before the needle electrospinning process, thereby achieving their good dispersion in the nanofibers. CeNPs embedded in the structure and on the surface of nanofibers exposing their reactive surfaces showed robust dephosphorylation catalytic activity, as demonstrated by monitoring the hydrolytic cleavage of three phosphodiester molecules (p-NP-TMP, p-NPPC, BNPP) in water by the HPLC method. This procedure allowed us to study the kinetics and mechanism of the hydrolytic cleavage and the ability of immobilized CeNPs to cleave different types of P-O bonds. One of the main hydrolysis products, p-nitrophenol, was effectively adsorbed on PA6 nanofibers, which may allow the selective separation of the degradation products after hydrolysis.

Unveiling the nanotoxicological aspects of Se nanomaterials differing in size and morphology.

Although the general concept of nanotechnology relies on exploitation of size-dependent properties of nanoscaled materials, the relation between the size/morphology of nanoparticles with their biological activity remains not well understood. Therefore, we aimed at investigating the biological activity of Se nanoparticles, one of the most promising candidates of nanomaterials for biomedicine, possessing the same crystal structure, but differing in morphology (nanorods vs. spherical particles) and aspect ratios (AR, 11.5 vs. 22.3 vs. 1.0) in human cells and BALB/c mice. Herein, we report that in case of nanorod-shaped Se nanomaterials, AR is a critical factor describing their cytotoxicity and biocompatibility. However, spherical nanoparticles (AR 1.0) do not fit this statement and exhibit markedly higher cytotoxicity than lower-AR Se nanorods. Beside of cytotoxicity, we also show that morphology and size substantially affect the uptake and intracellular fate of Se nanomaterials. In line with in vitro data, in vivo i.v. administration of Se nanomaterials revealed the highest toxicity for higher-AR nanorods followed by spherical nanoparticles and lower-AR nanorods. Moreover, we revealed that Se nanomaterials are able to alter intracellular redox homeostasis, and affect the acidic intracellular vesicles and cytoskeletal architecture in a size- and morphology-dependent manner. Although the tested nanoparticles were produced from the similar sources, their behavior differs markedly, since each type is promising for several various application scenarios, and the presented testing protocol could serve as a concept standardizing the biological relevance of the size and morphology of the various types of nanomaterials and nanoparticles.

Cerium-Bismuth Oxides/Oxynitrates with Low Toxicity for the Removal and Degradation of Organophosphates and Bisphenols.

Nanoscale cerium-bismuth oxides/oxynitrates were prepared by a scalable low-temperature method at ambient pressure using water as the sole solvent. Solid solutions were formed up to a 1:1 Ce/Bi molar ratio, while at higher doping levels, bismuth oxynitrate photocatalysts with a pronounced layered structure were formed. Bismuth caused significant changes in the structure and surface properties of nanoceria, such as the formation of defects, oxygen-containing surface groups, and Lewis and Brønsted acid sites. The prepared bifunctional adsorbents/photocatalysts were efficient in the removal of toxic organophosphate (methyl paraoxon) from water by reactive adsorption followed by photocatalytic decomposition of the parent compound and its degradation product (p-nitrophenol). Bi-doped ceria also effectively adsorbed and photodegraded the endocrine disruptors bisphenols A and S and outperformed pure ceria and the P25 photocatalyst in terms of efficiency, durability, and long-term stability. The very low toxicity of Bi-nanoceria to mammalian cells, aquatic organisms, and bacteria has been demonstrated by comprehensive in vivo/in vitro testing, which, in addition to its simple "green" synthesis, high activity, and durability, makes Bi-doped ceria promising for safe use in abatement of toxic chemicals.

Comparison of the Influence of Two Types of Plasma Treatment of Short Carbon Fibers on Mechanical Properties of Epoxy Composites Filled with These Treated Fibers.

The interfacial interface between fibers and matrix plays a key role for epoxy matrix composites and short recycled randomly arranged fibers. This study used short recycled carbon fiber (RCF) as a filler. Plasma treatment was used for carbon fiber surface treatment. This treatment was performed using radio (RF) and microwave (MW) frequencies at the same pressure and atmosphere. Appropriate chemical modification of the fiber surfaces helps to improve the wettability of the carbon fibers and, at the same time, allows the necessary covalent bonds to form between fibers and the epoxy matrix. The effect of the plasma treatment was analyzed and confirmed by X-ray photoelectron spectroscopy, Raman microscopy, scanning electron microscopy, transmission electron microscopy and wettability measurements. Composite samples filled with recycled carbon fibers with low concentrations (1 wt%, 2.5 wt% and 5 wt%) and high concentrations (20 wt% and 30 wt%) were made from selected treated fibers. The mechanical properties (impact toughness, 3PB) were analyzed on these samples. It was found that the modulus of elasticity and bending stress increase with the increasing content of recycled carbon fibers. A more significant change in impact strength occurred in samples with low concentration.

Nickel-Decorated Mesoporous Iron-Cerium Mixed Oxides: Microstructure and Catalytic Activity in Methanol Decomposition.

Nickel-decorated mesoporous cerium-iron oxide composites were synthesized by a combination of incipient wetness impregnation and template-assisted hydrothermal techniques. The effects of the Fe/Ce ratio and the calcination temperature of cerium-iron oxides on the phase composition, texture, structure, and redox properties of the composites were studied by a combination of N2 physisorption, XRD, high-resolution transmission electron microscopy, SEM, Mössbauer, Raman, XPS, ultraviolet-visible and FTIR spectroscopies, H2-temperature-programmed reduction, and total oxidation of ethyl acetate as a catalytic test. The combined physicochemical characterization and in situ FTIR investigation of methanol decomposition was used for a proper understanding of the microstructure of the Ni/FeCe oxide composites and the mechanism of the reaction occurring on them. The complex role of the FeCe support in the stabilization of highly dispersed Ni particles, the generation of surface intermediates, and the impact of the support phase transformation under the reaction medium are discussed.

Amidoxime-functionalized bead cellulose for the decomposition of highly toxic organophosphates.

Regenerated bead cellulose is a promising material with excellent mechanical and rheological properties, ideally suited for advanced environmental applications. By introducing the amidoxime functional group into the glucose unit at the C-6 position, highly effective reactive sorbent was prepared and used to destroy priority hazardous substances such as organophosphate pesticides or nerve-paralytic chemical warfare agents (CWAs). Quantum mechanical (QM) calculations were performed to study the interactions of organophosphates with amidoxime functional groups at the molecular level. It was found that the energetic reaction barrier of the rate-limiting step is markedly reduced (from 31.40 to 11.37 kcal mol-1) in the case of the amidoxime-catalysed degradation of parathion methyl, which resulted in a dramatic increase in the degradation rate; this was fully confirmed by experiments, in which the pesticide degradation proceeded at the time scale of several hours (t 1/2 = 20-30 hours at pH 7.22).

Synthesis and characterization of TiO2/Mg(OH)2 composites for catalytic degradation of CWA surrogates.

Surface catalyzed reactions can be a convenient way to deactivate toxic chemical warfare agents (CWAs) and remove them from the contaminated environment. In this study, pure titanium oxide, magnesium hydroxide, and their composites TiO2/Mg(OH2) were prepared by thermal decomposition and precipitation of the titanium peroxo-complex and/or magnesium nitrate in an aqueous solution. The as-prepared composites were examined by XRD, XPS, HRTEM, and nitrogen physisorption. Their decontamination ability was tested on CWA surrogates and determined by high-performance liquid chromatography (HPLC) and gas chromatography coupled with mass spectrometry (GC-MS). Dimethyl methyl phosphonate (DMMP) was used as a G simulant for the nerve agents sarin (GB) and soman (GD) while 2-chloroethyl ethyl sulfide (2-CEES) and 2-chloroethyl phenyl sulfide (2-CEPS) were used as surrogates of sulfur mustard (HD). The activity of the as-prepared composites was correlated with acid-base properties determined by potentiometric titrations and pyridine adsorption studied by in situ DRIFTS. The mixing of Ti and Mg led to an increase of the surface area and the amount of surface -OH groups (with an increasing amount of Ti) that caused improved degradation of DMMP.

Stability of antibacterial modification of nanofibrous PA6/DTAB membrane during air filtration.

Stable antimicrobial nanofibrous membrane for air filtration based on polyamide 6 (hereafter PA6) modified by 1-dodecyltrimethylammonium bromide (DTAB) has been prepared by electrospinning using one-step technology, i.e. with modifying antimicrobial agent dissolved in spinning solution. Stability of antibacterial membrane function has been tested by air-blowing test to prove the permanency of chemical composition and antibacterial activity. X-ray diffraction, high-resolution scanning electron microscopy (HRSEM) revealed the effect of modifying agent on structure and morphology of PA6 nanofibres. X-ray photoelectron spectroscopy, electrokinetic analysis and antibacterial tests proved the stability of chemical composition and antibacterial activity after air-blowing tests. Special air-blowing device has been constructed for this purpose. The results prove the applicability so prepared membrane for a long-term air-conditioning.

Thin SnOx films for surface plasmon resonance enhanced ellipsometric gas sensing (SPREE).

Background: Gas sensors are very important in several fields like gas monitoring, safety and environmental applications. In this approach, a new gas sensing concept is investigated which combines the powerful adsorption probability of metal oxide conductive sensors (MOS) with an optical ellipsometric readout. This concept shows promising results to solve the problems of cross sensitivity of the MOS concept. Results: Undoped tin oxide (SnOx) and iron doped tin oxide (Fe:SnOx) thin add-on films were prepared by magnetron sputtering on the top of the actual surface plasmon resonance (SPR) sensing gold layer. The films were tested for their sensitivity to several gas species in the surface plasmon resonance enhanced (SPREE) gas measurement. It was found that the undoped tin oxide (SnOx) shows higher sensitivities to propane (C3H8) then to carbon monoxide (CO). By using Fe:SnOx, this relation is inverted. This behavior was explained by a change of the amount of binding sites for CO in the layer due to this iron doping. For hydrogen (H2) no such relation was found but the sensing ability was identical for both layer materials. This observation was related to a different sensing mechanism for H2 which is driven by the diffusion into the layer instead of adsorption on the surface. Conclusion: The gas sensing selectivity can be enhanced by tuning the properties of the thin film overcoating. A relation of the binding sites in the doped and undoped SnOx films and the gas sensing abilities for CO and C3H8 was found. This could open the path for optimized gas sensing devices with different coated SPREE sensors.

Shape-controlled synthesis of Sn-doped CuO nanoparticles for catalytic degradation of Rhodamine B.

The uniform Sn-doped CuO nanoparticles were synthesized by a simple solution method at a low temperature. The prepared samples were investigated by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), electron microscopy techniques (HRSEM, HRTEM, SAED, STEM and EDS elemental mapping), atomic force microscopy (AFM), UV/Vis spectroscopy, nitrogen physisorption (BET) and by evaluation of the catalytic activity on the degradation of Rhodamine B. The tin doping had a considerable influence on the morphology of CuO. The gradual narrowing of the particles morphology in the crystallographic [010] direction was observed with increasing the dopant concentration. The plate-like, rectangularsquare and rod-like CuO nanoparticles were obtained. The mechanism of a crystal growth of CuO associated with doping is proposed. The tin doping also affected the structural and optical properties of CuO. Increasing the amount of a dopant led to a red-shift of a band gap from 1.33 to 1.18eV. The incorporation of tin into the structure of copper oxide was confirmed by XRD and distribution of tin mapped by EDS analysis. The good catalytic properties of the as-prepared doped material were demonstrated by the enhanced catalytic removal of Rhodamine B in the presence of H2O2. The undoped CuO nanosheets reached only 24% efficiency in the removal of Rhodamine B within two hours. The best result exhibited CuO_050Sn sample containing 4at.% of tin and the degradation of Rhodamine B reached 99% within the same time. We have demonstrated a simple, scalable process for the preparation of catalytically very active Sn-doped CuO nanoparticles with varying properties.

Cerium oxide for the destruction of chemical warfare agents: A comparison of synthetic routes.

Four different synthetic routes were used to prepare active forms of cerium oxide that are capable of destroying toxic organophosphates: a sol-gel process (via a citrate precursor), homogeneous hydrolysis and a precipitation/calcination procedure (via carbonate and oxalate precursors). The samples prepared via homogeneous hydrolysis with urea and the samples prepared via precipitation with ammonium bicarbonate (with subsequent calcination at 500°C in both cases) exhibited the highest degradation efficiencies towards the extremely dangerous nerve agents soman (O-pinacolyl methylphosphonofluoridate) and VX (O-ethyl S-[2-(diisopropylamino)ethyl] methylphosphonothioate) and the organophosphate pesticide parathion methyl. These samples were able to destroy more than 90% of the toxic compounds in less than 10 min. The high degradation efficiency of cerium oxide is related to its complex surface chemistry (presence of surface OH groups and surface non-stoichiometry) and to its nanocrystalline nature, which promotes the formation of crystal defects on which the decomposition of organophosphates proceeds through a nucleophilic substitution mechanism that is not dissimilar to the mechanism of enzymatic hydrolysis of organic phosphates by phosphotriesterase.

A green method of graphene preparation in an alkaline environment.

We present a new, simple, quick and ecologically friendly method of exfoliating graphite to produce graphene. The method is based on the intercalation of a permanganate M2MnO4 (M=K, Na, Li), which is formed by the reaction of a manganate MMnO4 with an alkali metal hydroxide MOH. The quality of exfoliation and the morphology were determined using X-ray photoelectron spectroscopy, X-ray diffraction and microscopic techniques, including transmission electron microscopy and atomic force microscopy. We observed that a stable graphene suspension could be prepared under strongly alkaline conditions in the presence of permanganate and ultrasound assistance. The use of only an alkaline environment for the direct preparation of graphene from graphite structures has not been previously described or applied. It was found that such a method of preparation leads to surprisingly high yields and a stable product for hydrophilic graphene applications.

TiO2-graphene oxide nanocomposite as advanced photocatalytic materials.

BACKGROUND: Graphene oxide composites with photocatalysts may exhibit better properties than pure photocatalysts via improvement of their textural and electronic properties. RESULTS: TiO2-Graphene Oxide (TiO2 - GO) nanocomposite was prepared by thermal hydrolysis of suspension with graphene oxide (GO) nanosheets and titania peroxo-complex. The characterization of graphene oxide nanosheets was provided by using an atomic force microscope and Raman spectroscopy. The prepared nanocomposites samples were characterized by Brunauer-Emmett-Teller surface area and Barrett-Joiner-Halenda porosity, X-ray Diffraction, Infrared Spectroscopy, Raman Spectroscopy and Transmission Electron Microscopy. UV/VIS diffuse reflectance spectroscopy was employed to estimate band-gap energies. From the TiO2 - GO samples, a 300 µm thin layer on a piece of glass 10×15 cm was created. The photocatalytic activity of the prepared layers was assessed from the kinetics of the photocatalytic degradation of butane in the gas phase. CONCLUSIONS: The best photocatalytic activity under UV was observed for sample denoted TiGO_100 (k = 0.03012 h-1), while sample labeled TiGO_075 (k = 0.00774 h-1) demonstrated the best activity under visible light.

Hydrogen peroxide route to Sn-doped titania photocatalysts.

BACKGROUND: The work aims at improving photocatalytic activity of titania under Vis light irradiation using modification by Sn ions and an original, simple synthesis method. Tin-doped titania catalysts were prepared by thermal hydrolysis of aqueous solutions of titanium peroxo-complexes in the presence of SnCl4 or SnCl2 using an original, proprietary "one pot" synthesis not employing organic solvents, metallo-organic precursors, autoclave aging nor post-synthesis calcination. The products were characterized in details by powder diffraction, XPS, UV-vis, IR, and Raman spectroscopies, electron microscopy and surface area and porosity measurements RESULTS: The presence of tin in synthesis mixtures favors the formation of rutile and brookite at the expense of anatase, decreases the particle size of all formed titania polymorphs, and extends light absorption of titania to visible light region >400 nm by both red shift of the absorption edge and introduction of new chromophores. The photocatalytic activity of titania under UV irradiation and >400 nm light was tested by decomposition kinetics of Orange II dye in aqueous solution CONCLUSIONS: Doping by Sn improves titania photoactivity under UV light and affords considerable photoactivity under >400 nm light due to increased specific surface area and a phase heterogeneity of the Sn-doped titania powders.