Heat-Transfer Properties of Additively Manufactured Aluminum Lattice Structures in Combination with Phase Change Material.

Compared to sensible heat storage, latent heat storage provides higher energy density due to the enthalpy difference of the storage medium undergoing a phase change. However, the heat storage capability of phase change materials is opposed by low thermal conductivity. To enable sufficient heat transfer within a latent heat storage unit, phase change materials can be used in combination with a metallic matrix. One approach is the infiltration of phase change materials into additively manufactured metallic lattice structures. In this work, the fabrication of aluminum lattice structures through laser powder bed fusion is described. During fabrication, the cell size and the strut diameter were varied to obtain specimens of different geometries. To obtain the thermal conductivity of the fabricated lattices, measurements were conducted based on the transient plane source method. Additionally, finite element simulations were carried out to evaluate the effect of fabrication and measurement uncertainties. The thermal conductivity of the fabricated lattices was found to be between 3 W/(m·K) and 130 W/(m·K). The numerically and analytically performed calculations provide good estimations of the experimentally obtained data.

Characterization of Filigree Additively Manufactured NiTi Structures Using Micro Tomography and Micromechanical Testing for Metamaterial Material Models.

This study focuses on the influence of additive manufacturing process strategies on the specimen geometry, porosity, microstructure and mechanical properties as well as their impacts on the design of metamaterials. Filigree additively manufactured NiTi specimens with diameters between 180 and 350 µm and a nominal composition of Ni50.9Ti49.1 (at %) were processed by laser powder bed fusion in a first step. Secondly, they structures were characterized by optical and electron microscopy as well as micro tomography to investigate the interrelations between the process parameters, specimen diameters and microstructure. Each specimen was finally tested in a micro tensile machine to acquire the mechanical performance. The process strategy had, besides the resulting specimen diameter, an impact on the microstructure (grain size) without negatively influencing its quality (porosity). All specimens revealed a superelastic response while the critical martensitic phase transition stress decreased with the applied vector length. As a conclusion, and since the design of programmable metamaterials relies on the accuracy of FEM simulations, precise and resource-efficient testing of filigree and complex structures remains an important part of creating a new type of metamaterials with locally adjusted material behavior.