ABSTRACT
Green thermoplastic starch (TPS) nanocomposite films aided by cellulose nanofibers (CNFs) from Chrysopogon zizanioides roots were developed and characterized. When compared to other lignocellulosic fibers, Chrysopogon zizanioides roots revealed exceptionally high cellulose content (~48%). CNFs were separated using an environmentally friendly acid isolation technique that included three stages: (i) alkali treatment; (ii) bleaching; and (iii) mild acid hydrolysis using oxalic acid in an autoclave. Following that, green nanocomposite films were made from potato starch using the solution casting process, by which we used glycerol (30 wt%) to make thermoplastic starch. Then, cellulose nanofibers in different concentrations (0, 1, 2, 3, 4 wt%) were added to the thermoplastic starch matrix. The isolated CNFs had diameters in the range of 17-27 nm. Besides, these nanostructures presented a very high crystallinity index (~65%), thereby enhanced the thermal stability. TPS/CNF green nanocomposites containing 3 wt% CNFs had exceptional tensile strength (~161%), tensile modulus (~167%), thermal stability, and crystallinity. As a result, nanocomposite films made of starch and cellulose nanofibers (3 wt%) extracted from Chrysopogon zizanioides roots would be alternatives for sustainable packaging. It can be concluded that Chrysopogon zizanioides roots have high potential for polymer industry.
Subject(s)
Cellulose/analogs & derivatives , Chrysopogon/chemistry , Nanocomposites/chemistry , Nanofibers/chemistry , Starch/analogs & derivatives , Edible Films , Hydrolysis , Tensile StrengthABSTRACT
In the present work, we used the steam explosion method for the isolation of cellulose nanofiber (CNF) from Cuscuta reflexa, a parasitic plant commonly seen in Kerala and we evaluated its reinforcing efficiency in natural rubber (NR). Fourier Transform Infrared Spectroscopy (FTIR), X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM), and Thermogravimetric analysis (TGA) techniques indicated that type I cellulose nanofibers, with diameter: 10-30 nm and a 67% crystallinity index were obtained by the proposed method. The results showed that application of CNF in NR based nanocomposites resulted in significant improvement of their processing and performance properties. It was observed that the tensile strength and tear strength of NR/CNF nanocomposites are found to be a maximum at 2 phr CNF loading, which corresponds with the studies of equilibrium swelling behavior. Dynamic mechanical analysis, thermogravimetric analysis, and morphological studies of tensile fractured samples also confirm that CNF isolated from Cuscuta reflexa plant can be considered as a promising green reinforcement for rubbers.