ABSTRACT
Tribological tests in real conditions enable obtaining full data on the life of interacting machine parts. This article presents the results of operational tests on the elements of the support ring guidance system in a vertical ball-race mill. The guide and active armour operate under abrasive wear conditions with moderate-impact loads. The wear resistance of elements with overlay welding layers deposited with flux cored wire with a structure of high-alloy chrome cast iron and with a coating flame-sprayed with nickel-based powder was compared. The wear intensity of the overlay weld deposits was much lower than that of the sprayed coatings. The scope of this study also included the analysis of the chemical and phase composition, macro- and microscopic metallographic examinations, and the measurement of the hardness of the deposited layers and coatings.
ABSTRACT
The article presents the assessment of solutions and dried residues precipitated from solutions after the bioleaching process of Printed Circuit Boards (PCB) utilizing the Acidithiobacillus ferrooxidans. The obtained dried residues precipitated from bioleaching solution (leachate) and control solution were tested using morphology, phase, and chemical composition analysis, with particular emphasis on the assessment of crystalline and amorphous components. The analysis of the dried residues from leachate after bioleaching as well as those from the sterile control solution demonstrated a difference in the component oxidation-the leachate consisted of mainly amorphous spherical particles in diameter up to 200 nm, forming lacy aggregates. In the specimenform control solution larger particles (up to 500 nm) were observed with a hollow in the middle and crystalline outer part (probably Fe2O3, CuFeS2, and Cu2O). The X-ray diffraction phase analysis revealed that specimen obtained from leachate after bioleaching consisted mainly of an amorphous component and some content of Fe2O3 crystalline phase, while the dried residue from control solution showed more crystalline components. The share of the crystalline and amorphous components can be related to efficiency in dissolving metals during bioleaching. Obtained results of the investigation confirm the activity and participation of the A. ferrooxidans bacteria in the solubilization process of electro-waste components, with their visible degradation-acceleration of the reaction owing to a continuous regeneration of the leaching medium. The performed investigations allowed to characterize the specimen from leachate and showed that the application of complementary cross-check of the micro (SEM and S/TEM) and macro (ICP-OES and XRD) methods are of immense use for complete guidance assessment and obtained valuable data for the next stages of PCBs recycling.
ABSTRACT
The thermal conditions in the molten pool during the laser surface melting of ductile cast iron EN-GJS-700-2 were estimated by using infrared thermography and thermocouple measurements. The thermal data were then correlated with the microstructure of the melted zone. Additionally, the thermodynamic calculations of a Fe-C-Si alloy system were performed to predict the solidification path of the melted zone. It was found that increasing the cooling rate during solidification of the refined ledeburite eutectic but also suppressed the martensitic transformation. A continuous network of plate-like secondary cementite precipitates and nanometric spherical precipitates of tertiary cementite were observed in regions of primary and eutectic austenite. The solidification of the melted zone terminated with the Liquid â γ-Fe + Fe3C + Fe8Si2C reaction. The hardness of the melted zone was affected by both the fraction of the retained austenite and the morphology of the ledeburite eutectic.