ABSTRACT
We examined the effect of the particle size of gold on steam reforming of methanol over Au/CeO2-ZrO2 catalysts. Gold was loaded onto CeO2-ZrO2 through deposition-precipitation. The average particle size (2-12 nm) of the gold was controlled by thermal reduction under H2 at various temperatures and by chemical reduction with various reducing agents. The catalytic activity decreased significantly with increasing particle size of the gold. The turnover frequency at the interface between gold and a support appeared to be independent of particle size in the range 2-5 nm, which implies that the perimeter of the particle may be the active site for this reaction. Methanol adsorption and conversion over these catalysts were also investigated with in-situ diffuse reflectance infrared Fourier transform spectroscopy. Analytical results for various adsorbed intermediate species during methanol conversion suggests that transformation of methoxy species is facilitated by use of smaller gold particles.
Subject(s)
Hydrogen/chemistry , Metal Nanoparticles/chemistry , Metal Nanoparticles/ultrastructure , Methanol/chemistry , Steam , Carbon Dioxide/chemical synthesis , Catalysis , Cerium/chemistry , Materials Testing , Particle Size , Zirconium/chemistryABSTRACT
The thermal stability of a nanosized Ce(x)Zr(1-x)O2 solid solution on a silica surface and the dispersion behavior of V2O5 over Ce(x)Zr(1-x)O2/SiO2 have been investigated using XRD, Raman spectroscopy, XPS, HREM, and BET surface area techniques. Oxidative dehydrogenation of ethylbenzene to styrene was performed as a test reaction to assess the usefulness of the VOx/Ce(x)Zr(1-x)O2/SiO2 catalyst. Ce(x)Zr(1-x)O2/SiO2 (1:1:2 mol ratio based on oxides) was synthesized through a soft-chemical route from ultrahigh dilute solutions by adopting a deposition coprecipitation technique. A theoretical monolayer equivalent to 10 wt % V2O5 was impregnated over the calcined Ce(x)Zr(1-x)O2/SiO2 sample (773 K) by an aqueous wet impregnation technique. The prepared V2O5/Ce(x)Zr(1-x)O2/SiO2 sample was subjected to thermal treatments from 773 to 1073 K. The XRD measurements indicate the presence of cubic Ce0.75Zr0.25O2 in the case of Ce(x)Zr(1-x)O2/SiO2, while cubic Ce0.5Zr0.5O2 and tetragonal Ce0.16Zr0.84O2 in the case of V2O5/Ce(x)Zr(1-x)O2/SiO2 when calcined at various temperatures. Dispersed vanadium oxide induces more incorporation of zirconium into the ceria lattice, thereby decreasing its lattice size and also accelerating the crystallization of Ce-Zr-O solid solutions at higher calcination temperatures. Further, it interacts selectively with the ceria portion of the composite oxide to form CeVO4. The RS measurements provide good evidence about the dispersed form of vanadium oxide and the CeVO4 compound. The HREM studies show the presence of small Ce-Zr-oxide particles of approximately 5 nm size over the surface of amorphous silica and corroborate with the results obtained from other techniques. The catalytic activity studies reveal the ability of vanadium oxide supported on Ce(x)Zr(1-x)O2/SiO2 to efficiently catalyze the ODH of ethylbenzene at normal atmospheric pressure. The remarkable ability of Ce(x)Zr(1-x)O2 to prevent the deactivation of supported vanadium oxide leading to stable activity in the time-on-stream experiments and high selectivity to styrene are other important observations.
ABSTRACT
Ce(x)Zr(1)(-)(x)O(2) solid solutions deposited over silica surface were investigated by X-ray diffraction (XRD), Raman spectroscopy (RS), and high-resolution transmission electron microscopy (HREM) techniques in order to understand the role of silica support and the temperature stability of these composite oxides. For the purpose of comparison, an unsupported Ce(x)Zr(1)(-)(x)O(2) was also synthesized and subjected to characterization by various techniques. The Ce(x)Zr(1)(-)(x)O(2)/SiO(2) (CZ/S) (1:1:2 mole ratio based on oxides) was synthesized by depositing Ce(x)Zr(1)(-)(x)O(2) solid solution over a colloidal SiO(2) support by a deposition precipitation method and unsupported Ce(x)Zr(1)(-)(x)O(2) (CZ) (1:1 mole ratio based on oxides) was prepared by a coprecipitation procedure, and the obtained catalysts were subjected to thermal treatments from 773 to 1073 K. The XRD measurements disclose the presence of cubic phases with the composition Ce(0.75)Zr(0.25)O(2) and Ce(0.6)Zr(0.4)O(2) in CZ samples, while CZ/S samples possess Ce(0.75)Zr(0.25)O(2), Ce(0.6)Zr(0.4)O(2), and Ce(0.5)Zr(0.5)O(2) in different proportions. The crystallinity of these phases increased with increasing calcination temperature. The cell a parameter estimations indicate contraction of ceria lattice due to the incorporation of zirconium cations into the CeO(2) unit cell. Raman measurements indicate the presence of oxygen vacancies, lattice defects, and displacement of oxygen ions from their normal lattice positions in both the series of samples. The HREM results reveal, in the case of CZ/S samples, a well-dispersed nanosized Ce-Zr-oxides over the surface of amorphous SiO(2). The structural features of these crystals as determined by digital diffraction analysis of experimental images reveal that the Ce-Zr-oxides are mainly in the cubic geometry and exhibit high thermal stability. Oxygen storage capacity measurements by a thermogravimetric method reveal a substantial enhancement in the oxygen vacancy concentration of CZ/S sample over the unsupported CZ sample.
ABSTRACT
Structural characteristics of CeO(2)-ZrO(2)/TiO(2) (CZ/T) and V(2)O(5)/CeO(2)-ZrO(2)/TiO(2) (V/CZ/T) mixed oxide catalysts have been investigated using X-ray diffraction (XRD), BET surface area, Raman spectroscopy (RS), and high-resolution transmission electron microscopy (HREM) techniques. The CeO(2)-ZrO(2) (1:1 mole ratio) solid solution was deposited over a finely powdered TiO(2) support by a deposition precipitation method. A nominal 5 wt % V(2)O(5) was impregnated over the calcined (773 K) CZ/T mixed oxide carrier by a wet impregnation technique. The obtained CZ/T and V/CZ/T samples were further subjected to thermal treatments from 773 to 1073 K to understand the dispersion and temperature stability of these materials. In the case of CZ/T samples, the XRD results suggest the formation of different cubic and tetragonal Ce-Zr-oxide phases, Ce(0.75)Zr(0.25)O(2), Ce(0.6)Zr(0.4)O(2), Ce(0.5)Zr(0.5)O(2), and Ce(0.16)Zr(0.84)O(2) in varying proportions depending on the treatment temperature. With increasing calcination temperature from 773 to 1073 K, the intensity of the lines pertaining to cubic Ce(0.6)Zr(0.4)O(2) and Ce(0.5)Zr(0.5)O(2) phases increased at the expense of cubic Ce(0.75)Zr(0.25)O(2), indicating more incorporation of zirconia into the ceria lattice. The TiO(2) was mainly in the anatase form whose crystallite size also increased with increasing treatment temperature. A better crystallization and more incorporation of zirconia into the ceria lattice was noted when CZ/T was impregnated with V(2)O(5). However, no crystalline V(2)O(5) could be seen from both XRD and RS measurements. In particular, a preferential formation of CeVO(4) compound and an intense tetragonal Ce(0.16)Zr(0.84)O(2) phase were noted beyond 873 K. The HREM results indicate, in the case of CZ/T samples, a well-dispersed Ce-Zr-oxide of the size approximately 5 nm over the bigger crystals ( approximately 40 nm) of TiO(2) when treated at 873 K. The exact structural features of these crystals as determined by digital diffraction analysis of experimental images reveal that the Ce-Zr-oxides are mainly in the cubic fluorite geometry and the TiO(2) is in anatase form. A better crystallization of Ce-Zr-oxides ( approximately 8 nm) over the surface of bigger crystals of TiO(2) was noted at 1073 K. A further enhancement in the crystallite size and zirconia-rich tetragonal phase was noted in the case of V/CZ/T samples. Further, the structure of CeVO(4) formed was also clearly identified in conformity with XRD and RS results.
ABSTRACT
Structural characteristics of nanosized ceria-silica, ceria-titania, and ceria-zirconia mixed oxide catalysts have been investigated using X-ray diffraction (XRD), Raman spectroscopy, BET surface area, thermogravimetry, and high-resolution transmission electron microscopy (HREM). The effect of support oxides on the crystal modification of ceria cubic lattice was mainly focused. The investigated oxides were obtained by soft chemical routes with ultrahighly dilute solutions and were subjected to thermal treatments from 773 to 1073 K. The XRD results suggest that the CeO(2)-SiO(2) sample primarily consists of nanocrystalline CeO(2) on the amorphous SiO(2) surface. Both crystalline CeO(2) and TiO(2) anatase phases were noted in the case of CeO(2)-TiO(2) sample. Formation of cubic Ce(0.75)Zr(0.25)O(2) and Ce(0.6)Zr(0.4)O(2) (at 1073 K) were observed in the case of the CeO(2)-ZrO(2) sample. Raman measurements disclose the fluorite structure of ceria and the presence of oxygen vacancies/Ce(3+). The HREM results reveal well-dispersed CeO(2) nanocrystals over the amorphous SiO(2) matrix in the cases of CeO(2)-SiO(2), isolated CeO(2), and TiO(2) (anatase) nanocrystals, some overlapping regions in the case of CeO(2)-TiO(2), and nanosized CeO(2) and Ce-Zr oxides in the case of CeO(2)-ZrO(2) sample. The exact structural features of these crystals as determined by digital diffraction analysis of HREM experimental images reveal that the CeO(2) is mainly in cubic fluorite geometry. The oxygen storage capacity (OSC) as determined by thermogravimetry reveals that the OSC of the mixed oxide systems is more than that of pure CeO(2) and is system dependent.