ABSTRACT
Strain is known to enhance the activity of the oxygen reduction reaction in catalytic platinum alloy nanoparticles, whose inactivity is the primary impediment to efficient fuel cells and metal-air batteries. Bragg coherent diffraction imaging (BCDI) was employed to reveal the strain evolution during the voltammetric cycling in Pt-Ni alloy nanoparticles composed of Pt2Ni3, Pt1Ni1, and Pt3Ni2. Analysis of the 3D strain images using a core-shell model shows that the strain as large as 5% is induced on Pt-rich shells due to Ni dissolution. The composition dependency of the strain on the shells is in excellent agreement with that of the catalytic activity. The present study demonstrates that BCDI enables quantitative determination of the strain on alloy nanoparticles during electrochemical reactions, which provides a means to exploit surface strain to design a wide range of electrocatalysts.
Subject(s)
Alloys , Nanoparticles , Catalysis , Oxidation-Reduction , PlatinumABSTRACT
Here, we demonstrate the impact of ferromagnetic layer coating on controlling the magneto-optical response. We found that the transverse magneto-optical Kerr effect (TMOKE) signal and TMOKE hysteresis loops of Ni80Fe20 thin layers coated with a Cr layer show a strong dependence on the thickness of the Cr layer and the incidence angle of the light. The transmission and reflection spectra were measured over a range of incidence angles and with different wavelengths so as to determine the layers' optical parameters and to explain the TMOKE behavior. The generalized magneto-optical and ellipsometry (GMOE) model based on modified Abeles characteristic matrices was used to examine the agreement between the experimental and theoretical results. A comprehensive theoretical and experimental analysis reveals the possibility to create a TMOKE suppression/enhancement coating at specific controllable incidence angles. This has potential for applications in optical microscopy and sensors.