Bacterial cellulose nanocrystals obtained through enzymatic and acidic routes: A comparative study of their main properties and in vitro biological responses.

Cellulose nanocrystals (CNCs) are crystalline domains isolated from cellulosic fibers. They have been utilized in a wide range of applications, such as reinforcing fillers, antibacterial agents and manufacturing of biosensors. Whitin this context, the aim of this work was to obtain and analyze CNCs extracted from bacterial nanocellulose (BNC) using two distinct methods combined with milling pre-treatment: an acidic hydrolysis using 64 % sulfuric acid and an enzymatic hydrolysis using a commercial cellulase enzyme mixture. The CNCs obtained from the enzymatic route (e-CNCs) were observed to be spherical nanoparticles with diameter of 56 ± 11 nm. In contrast, the CNCs from the acid hydrolysis (a-CNCs) appeared as needle-shaped nanoparticles with a high aspect ratio with lengths/widths of 158 ± 64 nm/11 ± 2 nm. The surface zeta potential (ZP) of the a-CNCs was -30,8 mV, whereas the e-CNCs has a potential of +2.70 ± 3.32 mV, indicating that a-CNCs consisted of negatively charged particles with higher stability in solution. Although the acidic route resulted in nanocrystals with a slightly higher crystallinity index compared to the enzymatic route, e-CNCs was found to be more thermally stable than BNC and a-CNCs. Here, we also confirmed the safety of a-CNCs and e-CNCs using L929 cell line. Lastly, this article describes two different CNCs synthesis approaches that leads to the formation of nanoparticles with different dimensions, morphology and unique physicochemical properties. To the best of our knowledge, this is the first study to yield spherical nanoparticles as a result of BNC enzymatic treatment.

Antimicrobial Formulation of a Bacterial Nanocellulose/Propolis-Containing Photosensitizer for Biomedical Applications.

With the aim of contributing to the development of more efficient materials for wound care, new topical formulations based on bacterial nanocellulose (BNC) hydrogels containing propolis were produced. Characterizations confirmed the incorporation of propolis into the BNC matrix, maintaining its structure and properties. Rheological analysis confirmed that the hydrogels showed thixotropic behavior appropriate for topical application. Chromatographic profiles showed sustained release of propolis biomarkers for at least 20 h. The formulations did not present mutagenicity. For application in photodynamic inactivation (PDI), BNC/propolis hydrogels were prepared with the photosensitizers methylene blue (MB). Spectroscopy and confocal fluorescence microscopy confirmed the interaction of MB and propolis in BNC hydrogels, as well as the formation of a new composite material. In the antibacterial assays, formulations containing MB and propolis significantly reduced Staphylococcus aureus growth. In the presence of light, BNC/MB hydrogels completely inhibited the microorganism. Therefore, the results suggest potential materials for the prevention or treatment of Staphylococcus aureus infections in wounds.