ABSTRACT
Silver nanoparticles (AgNPs) have been regarded as a highly promising substrate for surface-enhanced Raman scattering (SERS) sensors. In this study, we focused on the electrochemical synthesis method by developing three kinds of AgNPs using three different electrolytes: citrate (e-Ag-C), oleic acid (e-Ag-O) and fish mint (Houttuynia cordata Thunb.) extract (e-Ag-bio). The as-prepared AgNPs were characterized and then employed as SERS substrates to detect the pesticide thiram. The obtained results show that e-Ag-O exhibits the best SERS performance. The effect of the coating agent was explained by chemical and electromagnetic enhancements (CM and EM). Although thiram could absorb onto e-Ag-C at the highest level, allowing its Raman signal to be best enhanced via the CM, the smallest interparticle distance of e-Ag-O could have resulted in the largest improvement in the EM. Using e-Ag-O to develop SERS-based sensors for thiram, we obtain the impressive detection limit of 1.04 × 10-10 M in standard samples and 10-9 M in tea leaves. The linear ranges are from 10-4 M to 10-7 M and from 10-7 M to 10-9 M, covering the maximum residue levels for plant commodities established by the United States Environment Protection Agency and European Food Safety Authority (2-13 ppm â¼7.7 × 10-6 M to 5 × 10-5 M).
ABSTRACT
Recently, there have been publications on preparing hybrid materials between noble metal and semiconductor for applications in surface-enhanced Raman scattering (SERS) substrates to detect some toxic organic dyes. However, the use of cuprous oxide/silver (Cu2O/Ag) to measure the trace amounts of methyl orange (MO) has not been reported. Therefore, in this study, the trace level of MO in water solvent was determined using a SERS substrate based on Cu2O microcubes combined with silver nanoparticles (Ag NPs). Herein, a series of Cu2O/Agx (x= 1-5) hybrids with various Ag amounts was synthesized via a solvothermal method followed by a reduction process, and their SERS performance was studied in detail. X-ray diffraction (XRD) and scanning electron microscopy results confirmed that 10 nm Ag NPs were well dispersed on 200-500 nm Cu2O microcubes to form Cu2O/Ag heterojunctions. Using the as-prepared Cu2O and Cu2O/Agx as MO probe, the Cu2O/Ag5 nanocomposite showed the highest SERS activity of all samples with the limit of detection as low to 1 nM and the enhancement factor as high as 4 × 108. The logarithm of the SERS peak intensity at 1389 cm-1 increased linearly with the logarithm of the concentration of MO in the range from 1 nM to 0.1 mM.