ABSTRACT
Rechargeable sodium-ion batteries are becoming a viable alternative to lithium-based technology in energy storage strategies, due to the wide abundance of sodium raw material. In the past decade, this has generated a boom of research interest in such systems. Notwithstanding the large number of research papers concerning sodium-ion battery electrodes, the development of a low-cost, well-performing anode material remains the largest obstacle to overcome. Although the well-known anatase, one of the allotropic forms of natural TiO2, was recently proposed for such applications, the material generally suffers from reduced cyclability and limited power, due to kinetic drawbacks and to its poor charge transport properties. A systematic approach in the morphological tuning of the anatase nanocrystals is needed, to optimize its structural features toward the electrochemical properties and to promote the material interaction with the conductive network and the electrolyte. Aiming to face with these issues, we were able to obtain a fine tuning of the nanoparticle morphology and to expose the most favorable nanocrystal facets to the electrolyte and to the conductive wrapping agent (graphene), thus overcoming the intrinsic limits of anatase transport properties. The result is a TiO2-based composite electrode able to deliver an outstandingly stability over cycles (150 mA h g-1 for more than 600 cycles in the 1.5-0.1 V potential range) never achieved with such a low content of carbonaceous substrate (5%). Moreover, it has been demonstrated for the first time than these outstanding performances are not simply related to the overall surface area of the different morphologies but have to be directly related to the peculiar surface characteristics of the crystals.
ABSTRACT
The present study reports on the synthesis and the electrochemical behavior of Na(0.71)CoO(2), a promising candidate as cathode for Na-based batteries. The material was obtained in two different morphologies by a double-step route, which is cheap and easy to scale up: the hydrothermal synthesis to produce Co(3)O(4) with tailored and nanometric morphology, followed by the solid-state reaction with NaOH, or alternatively with Na(2)CO(3), to promote Na intercalation. Both products are highly crystalline and have the P2-Na(0.71)CoO(2) crystal phase, but differ in the respective morphologies. The material obtained from Na(2)CO(3) have a narrow particle length (edge to edge) distribution and 2D platelet morphology, while those from NaOH exhibit large microcrystals, irregular in shape, with broad particle length distribution and undefined exposed surfaces. Electrochemical analysis shows the good performances of these materials as a positive electrode for Na-ion half cells. In particular, Na(0.71)CoO(2) thin microplatelets exhibit the best behavior with stable discharge specific capacities of 120 and 80 mAh g(-1) at 5 and 40 mA g(-1), respectively, in the range 2.0-3.9 V vs. Na(+)/Na. These outstanding properties make this material a promising candidate to construct viable and high-performance Na-based batteries.
ABSTRACT
Macroporous WO(3) films with inverted opal structure were synthesized by one-step procedure, which involves the self-assembly of the spherical templating agents and the simultaneous sol-gel condensation of the semiconductor alkoxide precursor. Transition metal doping, aimed to enhance the WO(3) electrical response, was carried out by including Cr(III) and Pt(IV) centers in the oxide matrix. It turned out that Cr remains as homogeneously dispersed Cr(III) centers inside the WO(3) host, while Pt undergoes reduction and aggregation to form nanoclusters located at the oxide surface. Upon interaction with NH(3), the electrical conductivity of transition metal doped-WO(3) increases, especially in the presence of Pt dopant, resulting in outstanding sensing properties (S = 110 ± 15 at T = 225 °C and [NH(3)] = 74 ppm). A mechanism was suggested to explain the excellent electrical response of Pt-doped films with respect to the Cr-doped ones. This associates the easy chemisorption of ammonia on the WO(3) nanocrystals, promoted by the inverted opal structure, with the catalytic action exerted by the surface Pt nanoclusters on the N-H bond dissociation. The overall results indicate that in Pt-doped WO(3) films the effects of the macroporosity positively combine with the electrical sensitization promoted by the metal nanoclusters, thus providing very lightweight materials which display high functionality even at relatively low temperatures. We expect that this synergistic effect can be exploited to realize other functional hierarchical metal oxide structures to be used as gas sensors or catalysts.
ABSTRACT
The mechanism of NO interaction with nanosized Ru(Pd,Pt)-doped SnO(2) was studied by electron paramagnetic resonance, Mössbauer, and electric resistance measurements. Three steps were proposed for the reaction between the semiconductor oxide and the gaseous component: (i) the formation of bielectronic oxygen vacancies (V(o)) in SnO(2); (ii) their single-ionization (V(o)(*)) with injection of electrons into the SnO(2) conduction band; (iii) the subsequent transfer of electrons from V(o)(*) to [Ru(Pd,Pt)](4+). The last process induces the formation of further oxygen vacancies which reduce the transition metal centers to lower oxidation states; the redox processes is enhanced and the electrical resistance in transition metal-doped SnO(2) is stronger modified with respect to the undoped material.