Degree of conversion of resin cements polymerized under different ceramic systems.

The aim of this study was to evaluate the degree of conversion of resin cements polymerized under different ceramic systems. Forty specimens of RelyX ARC (3M ESPE) and Maxcem Elite (Kerr) resin cements were polymerized under 5 types of dental ceramics: feldspathic, aluminum oxide-reinforced, aluminum oxide-based strengthened with zirconium oxide, leucite-reinforced, and lithium disilicate-reinforced. Measurements of the degree of conversion of the resin cements were performed 10 minutes, 1 hour, and 24 hours after curing using a Fourier transform infrared spectrophotometer. The values were subjected to a 3-way repeated-measures analysis of variance, and the means were compared with the Fisher protected least significant difference test (α = 0.05). The study findings showed that RelyX ARC resin cement displayed a higher degree of conversion than Maxcem Elite (P < 0.05). The degree of conversion was significantly lower for RelyX ARC polymerized under aluminum oxide ceramic and aluminum oxide ceramic strengthened with zirconium oxide (P < 0.05). For Maxcem Elite, there was no significant difference in the degree of conversion attained under the various ceramics (P > 0.05). For both cements, the degree of conversion increased gradually up to 24 hours after curing (P < 0.05). The ceramic system used directly influenced the degree of conversion of RelyX ARC. Both resin cements displayed an increase in the degree of conversion over time.

Degree of conversion of resin cements polymerized under different thicknesses of feldspathic porcelain

Aim The aim of this study is to evaluate the degree of conversion (DC) of resin cements polymerized under different thicknesses of feldspathic dental ceramic. Methods: Forty samples of RelyX ARC and RelyX Veneer resin cements were polymerized under Starlight feldspathic ceramic discs (DeguDent Gmbh) with 0.5 mm, 1.2 mm, 1.8 mm, and 2.4 mm in thickness. The control group was cured without the interposition of ceramic. The DC measurements were performed 10 minutes, 1 hour, and 24 hours after the light-activation in a Nexus 670 FTIR spectrophotometer. Data were analyzed by two-way repeated measure ANOVA and Fisher PLSD test. Results: The RelyX ARC showed higher DC for all ceramic thicknesses. There was significant decrease in DC related to an increase in ceramic thickness. For RelyX ARC, the values of DC obtained after 1 hour and 24 hours did not differ statistically between them, but they were higher than those analyzed after 10 minutes. For RelyX Veneer cement, there was gradual increase in the DC up to 24 hours. Conclusion: The higher the thicknesses of ceramic, the lower DC of the resin cement

Influência da interposição de diferentes cerâmicas no grau de conversão de agentes cimentantes resinosos / Influence of different ceramics on the degree of conversion of resin cements

O objetivo deste estudo foi avaliar o grau de conversão de agentes cimentantes resinosos polimerizados sob diferentes espessuras de cerâmica feldspática e diferentes sistemas cerâmicos de mesma espessura. No primeiro estudo, oitenta amostras dos cimentos resinosos RelyX ARC (3M Espe) e RelyX Veneer (3M Espe) foram confeccionadas sob discos de cerâmica convencional Starlight (DeguDent) com espessuras de 0,5mm, 1,2mm, 1,8mm e 2,4mm. No segundo estudo, oitenta amostras dos cimentos resinosos RelyX ARC (3M Espe) e Maxcem Elite (Kerr) foram confeccionadas sob discos de diferentes sistemas cerâmicos: Starlight (DeguDent), Empress (Ivoclair Vivadent), E-max (Ivoclair Vivadent), In Ceram Alumina (Vita) e In Ceram Zircônia (Vita) com espessuras de 2,0mm. A leitura do grau de conversão dos cimentos resinosos foi realizada 10 minutos, 1 hora e 24 horas após a fotoativação dos cimentos, em espectrofotômetro FTIR Nexus 670 (Nicolet). Os resultados do primeiro estudo mostraram que o cimento resinoso dual RelyX ARC apresentou maior grau de conversão que o cimento fotoativado RelyX Veneer em todas as espessuras de cerâmica, inclusive sem interposição (p<0.0001). Os valores de grau de conversão obtidos após 1 hora e 24 horas não diferiram estatisticamente entre si (p=0.7433), mas foram superiores aos analisados após 10 minutos (p<0.0001). Para o cimento fotoativado, houve aumento gradativo no grau de conversão de 10 minutos até 24 horas (p<0.0001). No segundo estudo, os maiores valores de grau de conversão foram obtidos para as amostras polimerizadas sob as cerâmicas reforçadas por leucita e dissilicato de lítio, sem diferença estatisticamente significante entre si (p=0.1181), enquanto os menores valores do grau de conversão obtidos foram das amostras polimerizadas sob cerâmicas reforçadas por alumina e zircônia, sem diferença entre si (p=0.2374). Com base nos resultados destes estudos, concluímos que a espessura de cerâmica feldspática bem como o tipo de sistema cerâmico...

The aim of this study was to evaluate the degree of conversion of resin cements polymerized under different thicknesses of feldspatic ceramic and different ceramic systems with the same thickness. In the first study, eighty samples of RelyX ARC (3M Espe) and RelyX Veneer (3M Espe) were polymerized under conventional ceramic discs (Starlight, DeguDent) with thickness of 0.5 mm 1.2 mm, 1.8 mm and 2.4 mm. In the second study, eighty samples of RelyX ARC (3M Espe) and Maxcem Elite (Kerr) resin cements were polymerized over ceramics systems: Starlight (DeguDent), Empress (Ivoclar Vivadent), E-max (Ivoclar Vivadent), In Ceram Alumina (Vita) and In Ceram Zircon (Vita) with 2.0 mm of thickness. The degree of conversion of the resin cements was calculated 10 minutes, 1 hour and 24 hours after the curing of cements using a Nexus 670 FTIR spectrophotometer (Nicolet). The RelyX ARC showed higher values of degree of conversion than RelyX Veneer considering all the ceramics thickness in the first study. The measurements obtained after 1 hour and 24 hours did not differ significantly (p=0.7433), but were higher than those analyzed after 10 minutes (p<0.0001). Comparing the ceramic systems in the second study, the highest degree of conversion were obtained for samples polymerized under Empress and e.max ceramics, without statistically difference between them (p= 0.1181) and the lower values of conversion were obtained for the samples polymerized under In Ceram Alumina and In Ceram Zircon ceramics (p= 0.2374). Based on the results of these studies, we can conclude that the thickness of feldspatic porcelain as well as the ceramic system itself could influence the degree of conversion of light- and dual-cured resin cements. All the resin cements showed an increase on the degree of conversion after 24 hours, which could create an especial guideline for the clinical procedures using resin cements

Avaliação da alteração dimensional linear de silicones para inclusão laboratorial / Evaluation of linear dimensional alteration of laboratorial inclusion silicone

Foi propósito deste estudo avaliar a alteração dimensional linear de 6 silicones porcondensação indicados para inclusão de próteses em laboratório: Labor Mass, Perfil Lab, Silon IP,Vipi Sil, Zetalabor e Zetalabor Titanium. A partir de uma matriz metálica e seguindo a especificaçãonº 19 da ADA, Revisão ISO 4823, e as instruções dos fabricantes, foram obtidas 120 réplicas dos6 materiais (n = 20). Para a verificação da alteração dimensional linear, as réplicas foram avaliadaspor meio de um microscópio comparador, sendo a primeira leitura realizada imediatamenteapós a obtenção e a segunda depois de 60 minutos. Os dados obtidos foram transformados emporcentagem por meio de uma fórmula matemática e submetidos à análise de variância, sendoas médias comparadas pelo teste de Tukey. Houve diferença significativa entre as mensuraçõesrealizadas imediatamente e após 60 minutos, independente do material utilizado, e quando osmateriais foram analisados conjuntamente (p < 0,05), as maiores médias foram obtidas após60 minutos. Com relação à interação entre os fatores material e tempo, pôde-se observar que, nosdois períodos analisados não houve diferença estatisticamente significante entre os materiais e ogrupo controle (matriz metálica) quando analisados isoladamente (p > 0,05). Todos os materiaistestados apresentaram comportamento semelhante no que diz respeito à alteração dimensionallinear, independente do período analisado, as leituras tardias (após 60 minutos) apresentarammaiores alterações dimensionais.

The objective of this study was to evaluate the linear dimensional alteration of6 codensing silicone materials indicated for laboratorial denture inclusion, being: Labor Mass,Perfl Lab, Silon IP, Vipi Sil, Zetalabor and Zetalabor Titanium. The materials were measuredand handled according to manufacturer instructions, and, the 19th ADA especifications and the4823 ISO Review for elastomeric materials were used as guides of the realized exams. The readingswere made trough a comparison microscopic, the first, imediately after the samples been obtained,and the second after 60 minutes. 20 samples of each material were made, totalizing 120 replicas.The data was analysed by two way ANOVA and mean were compared by Tukey test. There was adifference between the measures taken imediately and after 60 minutes, independing the materialused and when they were analysed together (p < 0.05). Therefore the highest mean were obtainedafter 60 minutes. In relation to interaction between the factor material and time, it was observedthat in both analysed periods there was no significantly estatistic difference among the materialsand the control group (metallic matrix), when analysed alone/apart (p > 0.05). All tested materialspresented a similar behavior in respect of linear dimensional alteration, in both times studied, wherethe later readings (after 60 minutes) presented higher dimensional alterations.

Análise da movimentação dos dentes artificiais em próteses totais superiores. / Artificial teeth movement analysis in upper complete denture. Influence of polishing

O propósito desse estudo foi o de verificar a influência do polimento sobre a posição relativa dos dentes artificiais de próteses totais superiores, quando essas são confeccionadas com diferentes tipos de materiais ou associações, analisando para tanto à diferença entre as distâncias dos dentes pelo método de computação gráfica. Foram confeccionadas quarenta próteses totais superiores idênticas, sendo divididas em oito grupos de cinco espécimes cada de acordo com o tipo de resina (Vipi-wave e Onda-cryl), tipo de silicone para inclusão (Vipi-sil e Zetalabor) e tipo de polimento. As próteses foram polimerizadas em microondas, demarcadas e submetidas ao polimento químico e ao polimento mecânico. Em cada fase as próteses foram digitalizadas em scanner de mesa e suas imagens exportadas para o software AutoCad 2000 que possibilitou a mensuração dos segmentos entre os pontos previamente demarcados nos dentes. Os dados foram sub-metidos ao tratamento estatístico, e os resultados possibilitaram concluir que o polimento físico resultou em alterações significantemente superiores ao polimento químico quando os dados foram analisados independentemente do grupo estudado (p<0,05). O polimento das próteses resultou na grande maioria das amostras em uma recuperação gradual da contração de polimerização. Os grupos em que a resina de eleição foi a Vipi-wave (T1, T1’, T2 e T2’) apresentaram-se menos susceptível ao polimento químico que os grupos em que a resina foi a Onda-cryl (T3, T3’, T4 e T4’).