ABSTRACT
The coronavirus disease 2019 (COVID-19) pandemic had caused a severe depletion of the worldwide supply of N95 respirators. The development of methods to effectively decontaminate N95 respirators while maintaining their integrity is crucial for respirator regeneration and reuse. In this study, we systematically evaluated five respirator decontamination methods using vaporized hydrogen peroxide (VHP) or ultraviolet (254 nm wavelength, UVC) radiation. Through testing the bioburden, filtration, fluid resistance, and fit (shape) of the decontaminated respirators, we found that the decontamination methods using BioQuell VHP, custom VHP container, Steris VHP, and Sterrad VHP effectively inactivated Cardiovirus (3-log10 reduction) and bacteria (6-log10 reduction) without compromising the respirator integrity after 2-15 cycles. Hope UVC system was capable of inactivating Cardiovirus (3-log10 reduction) but exhibited relatively poorer bactericidal activity. These methods are capable of decontaminating 10-1000 respirators per batch with varied decontamination times (10-200 min). Our findings show that N95 respirators treated by the previously mentioned decontamination methods are safe and effective for reuse by industry, laboratories, and hospitals.
ABSTRACT
Ultrafiltration grade polysulfone-based mixed matrix membranes (MMMs) incorporated with two-dimensional boron nitride nanosheet (BNNS) was prepared via phase inversion method. The amount of BN incorporated was varied and the influence on membrane morphology, contact angle, surface charge, as well as water permeability and humic acid rejection were investigated. Results revealed that the addition of BN to the membrane matrix resulted in profound increase in water permeability (almost tripled to that of neat PSf) and humic acid rejection due to the increase in pore size and surface negative charge. Beyond the morphological changes imparted by the inclusion of BNNS, we postulated that the presence of BNNS within the membrane matrix also contribute to the enhancement in flux and rejection based on surface-slip and selective interlayer transport. Despite the favourable augmentation of water transport and filtration performance, the MMMs suffered with fouling problem due to the entrapment of foulant within the enlarged pores and the membrane valleys. Its inherent adsorptive character could be a disadvantage when utilized as membrane filler.