Effects of experimental bleaching gels containing co-doped titanium dioxide and niobium pentoxide combined with violet light.

OBJECTIVES: The objective of the study is to evaluate the bleaching potential of 6% hydrogen peroxide (6% HP) gels containing NF_TiO2 or Nb2O5 irradiated with a violet LED light and the effects on enamel mineral content and surface morphology. METHODS: Particles were synthesized, and experimental gels were chemically analyzed by preliminary and accelerated stability tests, pH, and HP decomposition rate. Bovine enamel blocks were treated with 6% HP gels containing (n = 10): 5% NF_TiO2, 5% Nb2O5, 2.5% NF_TiO2 + 2.5% Nb2O5 or without particles (6% HP), irradiated or not with LED, and the control was treated with 35% HP. Color (∆E00) and whitening index (∆WID) variations, surface microhardness (SH), average roughness (∆Ra), Ca-P concentration (EDS), and enamel morphology (SEM) were assessed. Bleaching was performed in 3 sessions of 30 min and 7-day intervals. Data were submitted to two- (pH, decomposition rate, ∆E00, and ∆WID) or three-way ANOVA and Bonferroni (SH), Kruskal-Wallis (∆Ra), and Dunnet tests (α = 0.05). RESULTS: No changes in the gel's color, odor, or translucency were observed. The pH (6 to 6.5) remained stable over time, and light irradiation boosted the HP decomposition rate. NF_TiO2 and Nb2O5-containing gels displayed higher ∆E00 and ΔWID when light-irradiated (p < 0.05). Nb2O5 and Nb2O5 + NF_TiO2 decreased enamel SH (p < 0.05), but no SH changes were found among groups (p > 0.05). No differences among groups were noted in ∆Ra, Ca-P content, and enamel morphology after treatments (p > 0.05). CONCLUSION: Experimental light-irradiated 6% HP gels containing NF_TiO2 or Nb2O5 were chemically stable and exhibited bleaching potential comparable with 35% HP. CLINICAL RELEVANCE: Low-concentrated HP gels containing NF_TiO2 or Nb2O5 and light-irradiated stand as a possible alternative to in-office bleaching.

Mechanical and antibacterial properties of an experimental flowable composite containing Nb2O5 and NF_TiO2 nanoparticles.

This study developed an experimental flowable composite incorporated with niobium pentoxide (Nb2O5) combined or not with titanium dioxide co-doped with fluorine and nitrogen (NF_TiO2) and evaluated the mechanical and antibacterial properties. The experimental flowable composite (TEGDMA + BisGMA 1:1 + 60%wt - inorganic filler - borosilicate 0.7 µm) was formulated according to the type and concentration of Nb2O5 and NF_TiO2 (0.5, 1, 1.5 and 2 wt%) or NF_TiO2 + Nb2O5 (0.25, 0.5, 0.75 and 1 wt% - 1:1). The control groups were formed by the experimental composite without the incorporation of Nb2O5 and/or NF_TiO2 (GC-E) and by a commercial flowable composite (GC). The characterization of the surface of the composite and its particles was carried out using scanning electron microscopy (SEM) and energy dispersive x-rays (EDX). Specimens were manufactured and subjected to mechanical tests of flexural strength (FS) (n = 12), flexural modulus (FM) (n = 12), roughness (Ra) (n = 10), microhardness (n = 10), and contact angle (n = 10); and, to evaluate the antibacterial activity, they were submitted to tests of biofilm formation against S. mutans (CFU/mL) (n = 5), biofilm biomass by dry weight (n = 5) and confocal laser microscopy (%LIVE/DEAD) (n = 5). Data were submitted to one-way ANOVA and Tukey's post-hoc and, those that were not homoscedastic, but with normality, were submitted to Welch's ANOVA and Games-Howell's post-hoc. Dunnet's test was used to compare the controls with the other experimental groups (α = 5). The Nb2O5 particles had an average size of 32.4 µm and the nanoparticles (NPs) of NF_TiO2, 10 nm. EDX analysis identified isolated peaks of N, F, Ti, and Nb confirming the presence of these particles in the resin matrix. The 1.5% NF_TiO2 group had a higher FS and FM than the controls (p < 0.05). GC showed higher microhardness between groups (p < 0.05). There was no difference between the experimental groups regarding contact angle and roughness (p > 0.05), except for GC, which had the highest Ra values and the lowest contact angle between groups (p < 0.05). Composites containing 0.5%, 1%, 1.5%, and 2% Nb2O5, 1%, 1.5%, and 2% NF_TiO2 and 2% Nb2O5 + NF_TiO2 showed lower biofilm formation (p < 0.05), lower total biofilm biomass (p < 0.05), and a higher percentage of dead cells (44%, 52%, 52%, 79%, 42% 43%, 62%, 65%, respectively) than GC and GC-E (5% and 1%, respectively). It is concluded that the incorporation of 1.5% NF_TiO2 promoted a greater FS and FM among the experimental composites and that the addition of Nb2O5 particles (0.5%, 1%, 1.5%, and 2%), NF_TiO2 (1%, 1.5% and 2%) and the combination Nb2O5 + NF_TiO2 (2%) showed significant antibacterial effects.