ABSTRACT
In order to clarify the role of R2O3 in the metal-oxide catalysts derived from complex oxide precursors, a series of R1.5Ca0.5NiO4 (R = Nd, Sm, Eu) complex oxides was obtained. A significant systematic increase in the orthorhombic distortion of the R1.5Ca0.5NiO4 structure (K2NiF4 type, Cmce) from Nd to Eu correlates with a corresponding decrease in their ionic radii. A reduction of R1.5Ca0.5NiO4 in the Ar/H2 gas mixture at 800 °C causes a formation of dense agglomerates of CaO and R2O3 coated with spherical 25-30 nm particles of Ni metal. The size of metal particles and oxide agglomerates is similar in all Ni/(R2O3,CaO) composites in the study. Their morphology is rather similar to the products of redox exsolution obtained by the partial reduction of complex oxides. All obtained composites demonstrated a significant catalytic activity in the dry reforming (DRM) and partial oxidation (POM) of methane at 700-800 °C. A systematic decrease in the DRM catalytic activity of composites from Nd to Eu could be attributed to the basicity reduction of R2O3 components of the composite catalysts. The maximum CH4 conversion in POM reaction was observed for Ni/(Sm2O3,CaO), while the maximum selectivity was demonstrated by Nd2O3-based composite. The possible reasons for the observed difference are discussed.
ABSTRACT
Highly textured thin films of undoped, Ce-doped, and Sr-doped Pr2CuO4 were synthesized on single crystal YSZ substrates using pulsed laser deposition to investigate their area-specific resistance (ASR) as cathodes in solid-oxide fuel cells (SOFCs). The effects of T' and T* crystal structures, donor and acceptor doping, and a-axis and c-axis orientation on ASR were systematically studied using electrochemical impedance spectroscopy on half cells. The addition of both Ce and Sr dopants resulted in improvements in ASR in c-axis oriented films, as did the T* crystal structure with the a-axis orientation. Pr1.6Sr0.4CuO4 is identified as a potential cathode material with nearly an order of magnitude faster oxygen reduction reaction kinetics at 600 °C compared to thin films of the commonly studied cathode material La0.6Sr0.4Co0.8Fe0.2O3-δ. Orientation control of the cuprate films on YSZ was achieved using seed layers, and the anisotropy in the ASR was found to be less than an order of magnitude. The rare-earth doped cuprate was found to be a versatile system for study of relationships between bulk properties and the oxygen reduction reaction, critical for improving SOFC performance.