ABSTRACT
The effect of the addition of an ionic dopant to calcium phosphates for biomedical applications requires specific research due to the essential roles played in such processes. In the present study, the mechanical and biological properties of Ni-doped hydroxyapatite (HA) and Ni-doped HA mixed with graphene nanoplatelets (GNPs) were evaluated. Ni (3wt.% and 6wt.%)-doped HA was synthesized using a continuous precipitation method and calcined at 900°C for 1h. The GNP (0.5-2wt.%)-reinforced 6% Ni-doped HA (Ni6) composite was prepared using rotary ball milling for 15h. The sintering process was performed using hot isostatic pressing at processing conditions of 1150°C and 160MPa with a 1-h holding time. The results indicated that the phase compositions and structural features of the products were noticeably affected by the Ni and GNPs. The mechanical properties of Ni6 and 1.5Ni6 were increased by 55% and 75% in hardness, 59% and 163% in fracture toughness and 120% and 85% in elastic modulus compared with monolithic HA, respectively. The in-vitro biological behavior was investigated using h-FOB osteoblast cells in 1, 3 and 5days of culture. Based on the osteoblast results, the cytotoxicity of the products was indeed affected by the Ni doping. In addition, the effect of GNPs on the growth and proliferation of osteoblast cells was investigated in Ni6 composites containing different ratios of GNPs, where 1.5wt.% was the optimum value.
Subject(s)
Biocompatible Materials/chemistry , Calcium Phosphates/chemistry , Graphite/chemistry , Nanocomposites/chemistry , Nickel/chemistry , Biocompatible Materials/pharmacology , Calcium Phosphates/pharmacology , Cells, Cultured , Durapatite/chemistry , Durapatite/pharmacology , Elastic Modulus/drug effects , Graphite/pharmacology , Hardness , Humans , Hydroxyapatites/chemistry , Materials Testing/methods , Nickel/pharmacology , Osteoblasts/drug effects , Pressure , Surface PropertiesABSTRACT
Calcium silicate (CS, CaSiO3 ) is a bioactive, degradable, and biocompatible ceramic and has been considered for its potential in the field of orthopedic surgery. The objective of this study is the fabrication and characterization of the ß-CS/poly(1.8-octanediol citrate) (POC) biocomposite, with the goals of controlling its weight loss and improving its biological and mechanical properties. POC is one of the most biocompatible polymers, and it is widely used in biomedical engineering applications. The degradation and bioactivity of the composites were determined by soaking the composites in phosphate-buffered saline and simulated body fluid, respectively. Human osteoblast cells were cultured on the composites to determine their cell proliferation and adhesion. The results illustrated that the flexural and compressive strengths were significantly enhanced by a modification of 40% POC. It was also concluded that the degradation bioactivity and amelioration of cell proliferation increased significantly with an increasing ß-CS content.
Subject(s)
Calcium Compounds , Cell Proliferation/drug effects , Citrates , Composite Resins , Materials Testing , Osteoblasts/metabolism , Polymers , Silicates , Calcium Compounds/chemistry , Calcium Compounds/pharmacology , Cell Line , Composite Resins/chemistry , Composite Resins/pharmacology , Humans , Osteoblasts/cytology , Silicates/chemistry , Silicates/pharmacologyABSTRACT
The focus of this study is to investigate the effect of Al2O3 on α-calcium silicate (α-CaSiO3) ceramic. α-CaSiO3 was synthesized from CaO and SiO2 using mechanochemical method followed by calcinations at 1000°C. α-CaSiO3 and alumina were grinded using ball mill to create mixtures, containing 0-50w% of Al2O3 loadings. The powders were uniaxially pressed and followed by cold isostatic pressing (CIP) in order to achieve greater uniformity of compaction and to increase the shape capability. Afterward, the compaction was sintered in a resistive element furnace at both 1150°C and 1250°C with a 5h holding time. It was found that alumina reacted with α-CaSiO3 and formed alumina-rich calcium aluminates after sintering. An addition of 15wt% of Al2O3 powder at 1250°C were found to improve the hardness and fracture toughness of the calcium silicate. It was also observed that the average grain sizes of α-CaSiO3 /Al2O3 composite were maintained 500-700nm after sintering process.
Subject(s)
Aluminum Oxide/chemistry , Biocompatible Materials/chemistry , Biomedical Engineering , Calcium Compounds/chemistry , Mechanical Phenomena , Physical Phenomena , Silicates/chemistry , Elastic Modulus , TemperatureABSTRACT
This study describes the synthesis of Al(2)O(3)/SiC/ZrO(2) functionally graded material (FGM) in bio-implants (artificial joints) by electrophoretic deposition (EPD). A suitable suspension that was based on 2-butanone was applied for the EPD of Al(2)O(3)/SiC/ZrO(2), and a pressureless sintering process was applied as a presintering. Hot isostatic pressing (HIP) was used to densify the deposit, with beneficial mechanical properties after 2 h at 1800 °C in Ar atmosphere. The maximum hardness in the outer layer (90 vol.% Al(2)O(3)+10 vol.% SiC) and maximum fracture toughness in the core layer (75 vol.% Al(2)O(3)+10 vol.% SiC + 15 vol.% ZrO(2)) composite were 20.8±0.3 GPa and 8±0.1 MPa m(1/2), respectively. The results, when compared with results from Al(2)O(3)/ZrO(2) FGM, showed that SiC increased the compressive stresses in the outer layers, while the inner layers were under a residual tensile stress.
Subject(s)
Aluminum Oxide/chemistry , Biocompatible Materials/chemistry , Carbon Compounds, Inorganic/chemistry , Electrophoresis/methods , Joint Prosthesis , Silicon Compounds/chemistry , Zirconium/chemistry , Butanones/chemistry , Compressive Strength , Hardness , Hot Temperature , Materials Testing , Powders , Prosthesis Design , Stress, Mechanical , Surface Properties , Temperature , Tensile Strength , X-Ray DiffractionSubject(s)
Dental Implantation, Endosseous , Dental Implants , Tooth Avulsion/surgery , Tooth Fractures/surgery , Adolescent , Child , Crowns , Humans , Male , Tooth ExtractionABSTRACT
Heretofore, the absence of adequate alveolar bone (4 mm or less) beneath the maxillary sinus has prevented placement of endosteal root-form implants at the same time as antroplasty. A technique has been devised which permits implantation to occur upon the occasion of sinus floor elevation. This has been made possible by the use of titanium fracture miniplates, which serve as transitional fixation devices until mineralization of the graft material creates implant osseointegration.