ABSTRACT
The mass production of synthetic plastics began in the last century and today they have become one of the most abundant man-made materials. The disposal or the beneficiation of end-of-life plastics represent a great challenge for society especially in the case of polyvinyl chloride (PVC). This study is focused on the use of PVC waste as a useful agent for the direct reduction of hematite (Fe2O3) after a thermal treatment at 300 °C for removing the chlorine contained in PVC. Thermal reduction tests were conducted from 600 °C to 1100 °C with (Fe2O3 + PVC + clay) pellet mixtures in which clay was used as plasticizing and binder agent of the pellets. The starting samples and treatment residues were analyzed by scanning electron microscopy through energy dispersive spectroscopy (SEM-EDS) and X-ray diffraction (XRD) to monitor the chemical behavior and reactivity of the pellet constituents during their thermal treatment. The stepwise reduction of hematite up to metallic iron was achieved at temperatures approaching 1000 °C, confirming the capability of using PVC waste for the direct reduction of iron oxides.
ABSTRACT
The grown demand of current and future development of new technologies for high added value and strategic metals, such as molybdenum, vanadium, and chromium, and facing to the depletion of basic primary resources of these metals, the metal extraction and recovery from industrial by-products and wastes is a promising choice. Slag from the steelmaking sector contains a significant amount of metals; therefore, it must be considered to be an abundant secondary resource for several strategic materials, especially chromium. In this work, the generated slag from electric arc furnace (EAF) provided by the French steel industry was characterized by using multitude analytical techniques in order to determine the physico-chemical characteristics of the targeted slag. The revealed main crystallized phases are larnite (Ca2SiO4), magnetite (Fe3O4), srebrodolskite (Ca2Fe2O5), wüstite (FeO), maghemite (Fe2.6O3), hematite (Fe2O3), chromite [(Fe,Mg)Cr2O4], and quartz (SiO2). The collected slag sample contains about 34.1% iron (48.5% Fe2O3) and 3.5% chromium, whilst the vanadium contents is around 1500 ppm. The Mössbauer spectroscopy suggested that the non-magnetic fraction represents 42 wt% of the slag, while the remainder (58 wt%) is composed of magnetic components. The thermal treatment of steel slag up to 900 °C indicated that this solid is almost stable and few contained phases change their structures.