ABSTRACT
Solution combustion synthesis (SCS) is considered as an efficient and energy-saving method for preparing LiFePO4/C composite material with the nanostructure (Nano-LiFePO4/C). In this study, Nano-LiFePO4/C cathode material was prepared using SCS using a cost-effective combination of urea and sorbitol as mixed fuels. The effect of mixed fuels on combustion behavior and microstructure as well as on electrochemical performance was studied using XRD, BET, SEM, TEM, and electrochemical characterization methods. Multiple characterization results indicated that the maximum temperature (Tm) and particle size were influenced by the usage of urea and sorbitol. The sample derived under optimum conditions exhibits a mesoporous nanostructure with a large surface specific area and attractive electrochemical performance with a discharge capacity of 153.5 mAh/g at 0.1 C, which shows strong potential for commercial applications in the future.
ABSTRACT
In this work, CuFe2O4 nanospheres with hierarchically porous structure have been synthesized via a facile solvothermal procedure. The superstructures consist of the textured aggregations of nanocrystals with high specific surface area, pore volume, and uniform pore size distribution.To figure out the formation mechanism, we discussed in detail the effects of a series of experimental parameters, including the concentrations of the precipitation agent, stabilizer agent, and reaction temperature and time on the size and morphology of the resulting products. Furthermore, the electrochemical properties of CuFe2O4 nanospheres were evaluated by cyclic voltammetry and galvanostatic charge-dischrge studies. The results demonstrate that the as-prepared CuFe2O4 nanospheres are excellent electrode material in supercapacitor with high specific capacitance and good retention. The hierarchically CuFe2O4 nanospheres show the highest capacitance of 334F/g, and 88% of which can still be maintained after 600 charge-discharge cycles.