Prolonged corrosion protection via application of 4-ferrocenylbutyl saturated carboxylate ester derivatives with superior inhibition performance for mild steel.

A series of 4-ferrcenylbutyl carboxylate esters with different alkyl chain length (C2-C4) of carboxylic acids were synthesized using Fe3O4@SiO2@(CH2)3-Im-bisEthylFc[I] nanoparticles as catalyst and have been characterized with FT-IR, 1H NMR, and 13C NMR. Ferrocenyl-based esters were used as corrosion inhibitors of mild steel in the 1M HCl solution as corrosive media. The corrosion inhibition efficiency of the synthesized ferrocenyl-based esters has been assessed by electrochemical impedance spectroscopy (EIS), potentiodynamic polarization (PDP), atomic force microscopy (AFM), and scanning electron microscopy (SEM). The 4-ferrocenylbutyl propionate showed a more effective corrosion inhibition behavior among the studied esters with 96% efficiency after immersion in the corrosive media for 2 weeks. The corrosion inhibition mechanism is dominated by formation of passive layer of inhibitor on the surface of the mild steel by adsorption. Moreover, the adsorption characteristics of 4-butylferrcenyl carboxylate esters on mild steel were thoroughly explored using density functional theory calculations. It was found that the Fe atoms located around the C impurity in the mild steel are the most efficient and active sites to adsorb 4-butylferrcenyl carboxylate esters.

Promotion of hydrogen evolution from seawater via poly(aniline-co-4-nitroaniline) combined with 3D nickel nanoparticles.

This work reports the synthesis of poly (aniline-co-4-nitroaniline) deposited on a three-dimensional nanostructured nickel (3D-Ni) film, where both layers were fabricated via potentiostatic electrodeposition. The obtained electrocatalyst exhibited excellent electrochemical activity for the Hydrogen Evolution Reaction (HER) with small overpotentials of - 195 and - 325 mV at - 10 and - 100 mAcm-2, respectively, and a low Tafel slope of 53.3 mV dec-1 in seawater. Additionally, the electrocatalyst exhibited good stability after 72 h operation under a constant potential of - 1.9 V vs. RHE. The efficient HER performance of the as-prepared catalyst was found to originate from the synergy between the conducting polymer and three-dimensional nickel nanoparticles with a large electrochemical active surface area. Moreover, the results obtained from electrochemical impedance spectroscopy (EIS) measurements revealed that the presence of 3D-Ni layer improved the kinetics of HER by reducing the charge transfer resistance for the electrocatalyst.