ABSTRACT
The use of the polypropylene (PP) recyclates in certain processing methods and applications is still limited by their quality. The high melt flow rate (MFR) and the inconsistent properties of recyclates are common obstacles to their use. Therefore, this work aims to identify possible reasons for the low and inconsistent quality of PP recyclates depending on the source material in PP waste bales. The levels of polymeric and non-polymeric contaminants were assessed. As mixing of different PP grades is an issue for the MFR, the proportions of the different processing grades were also investigated and the potential of sorting by processing method to produce lower MFR recyclates was assessed. The analysis showed that the waste bales, although pre-sorted, still contained high amounts of contaminants. Injection moulding was found to be the predominant processing method in the bales, explaining the high MFR of PP recyclates. However, a sufficiently high amount of low MFR products was found in the bales, which seems promising for the production of low MFR recyclates. Seasonal variations in the composition of the waste bales were identified as one of the reasons for the inconsistent qualities of recyclates. These results highlight the importance of proper sorting and treatment of PP waste bales prior to reprocessing in order to obtain high-quality recycled products.
Subject(s)
Polypropylenes , Recycling , Recycling/methods , Waste Management/methods , Refuse Disposal/methodsABSTRACT
This work covers a lifecycle assessment of monolayer and multilayer films to quantify the environmental impacts of changing the management of plastic film waste. This lifecycle assessment offers the possibility of quantifying the environmental impacts of processes along the lifecycle of monolayer and multilayer films and mapping deviating impacts due to changed process parameters. Based on the status quo, the changes in global warming potential and abiotic fossil resource depletion were calculated in different scenarios. The changes included collecting, sorting, and recycling mono- and multilayer films. The "Functional Unit" under consideration comprised 1000 kg of plastic film waste, generated as post-consumer waste in Austria and captured in the lightweight packaging collection system. The results showed the reduction of environmental impacts over product lifecycles by improving waste management and creating a circular economy. Recycling all plastic film reduced global warming potential by 90% and abiotic fossil resource consumption by 93%. The necessary optimisation steps to meet the politically required recycling rates by 2025 and 2030 could be estimated, and the caused environmental impacts are presented. This work shows the need for increased collection, recycling, and significant improvement in the sorting of films to minimise global warming potential and resource consumption.
ABSTRACT
Delamination is one of the most critical failure modes of a PV module during service lifetime. Delamination within a backsheet primarily imposes a safety risk, but may also accelerate various other PV module degradation modes. The main aim of this paper is to present a peel test set-up, which is more practical in sample preparation and execution than the width-tapered cantilever beam test and overcomes some issues of standard peel tests like the influence of sample geometry and energy dissipation through deformation on the peel test results. The best results with respect to accuracy and effort were achieved by using a 180° peel geometry where an additional adhesive tape is applied to the peel arm in order to avoid plastic deformation or breakage. The additional support of the adhesive tape leads to comparable peel strength values without any influence of the plastic deformation behavior of the peel arms with different thickness.
ABSTRACT
The power degradation and failure of photovoltaic (PV) modules can be caused by changes in the mechanical properties of the polymeric components during the module lifetime. This paper introduces instrumented nanoindentation as a method to investigate the mechanical properties of module materials such as polymeric encapsulants. To this end, nanoindentation tests were carried out on ethylene vinyl acetate (EVA) surfaces, which have been separated from the glass panel. Two types of time-dependent indentation cycle modes, the time domain (creep mode) and frequency domain (dynamic mode) were performed to determine the viscoelastic behavior. For each mode, a corresponding model was applied to calculate the main mechanical properties. The general capability of nanoindentation as cross-linking determination method is investigated with the methodological advantages over bulk mechanical characterization methods. A large number of Glass/EVA/Backsheet laminates were built using different lamination conditions resulting in different degrees of curing. Both indentation modes indicate good modulus sensitivity for following the EVA crosslinking in its early stages but could not reliably differentiate between samples with higher EVA branching. Additional dynamic mechanical analysis (DMA) characterization was used as an established method to validate the indentation measurements. Both nanoindentation and DMA tensile mode produce similar quantitative viscoelastic responses, in the form of the damping factor parameter, demonstrated for three different frequencies at room temperature. A statistical study of the data reveals the advantages for the investigation of multilayer PV laminates by using nanoindenation as a surface method while also being applicable to field aged modules.
ABSTRACT
The main focus of this work is to investigate the degradation behavior of two newly developed encapsulants for photovoltaic applications (thermoplastic polyolefin (TPO) and polyolefin elastomer (POE)), compared to the most widely used Ethylene Vinyl Acetate (EVA) upon exposure to two different artificial ageing tests (with and without ultraviolet (UV) irradiation). Additive composition, optical and thermal properties and chemical structure (investigated by means of Thermal Desorption Gas Chromatography coupled to Mass Spectrometry, UV-Visible-Near Infrared spectroscopy, Differential Scanning Calorimetry, Thermogravimetric Analysis and Fourier Transform-Infrared spectroscopy, respectively) of the analyzed polymers were monitored throughout the exposure to artificial ageing tests. Relevant signs of photo-oxidation were detectable for TPO after the UV test, as well as a depletion of material's stabilizers. Signs of degradation for EVA and POE were detected when the UV dose applied was equal to 200 kW h m-2. A novel approach is presented to derive information of oxidation induction time/dose from thermogravimetric measurements that correlate well with results obtained by using oxidation indices.
ABSTRACT
In the project 'NEW-MINE' the use of sensor-based sorting machinery in the field of 'landfill mining' is investigated. Defilements pose a particular challenge in the treatment and sorting of plastics contained in landfills. For this reason, the effects of various pollutants caused by the interactions in the landfill body or the mechanical treatment steps in landfill mining are examined. In the following elaboration, the focus is on the influences of surface moisture and surface roughness of plastics on sensor-based sorting by means of near-infrared technology. Near-infrared radiation (NIR) in a wavelength range of 990 nm to 1500 nm has been used for the detection and classification of plastic particles. The experiments demonstrate that increased surface roughness reduces signal noise and thereby improves the classification of both spectrally similar and transparent plastics, but reduces the yield of low-softening plastics because their sliding speed on a sensor-based chute sorter varies as a result of the heating of the chute. Surface moisture causes the absorption of radiation from 1115 nm (high density polyethylene [HDPE], linear low density polyethylene [LLDPE], polyethylen terephthalate [PET] and polyvinylchloride [PVC]) or from 1230 nm (low density polyethylene [LDPE], polypropylene [PP] and thermoplastic polyurethane [TPU]) up to at least 1680 nm, which causes amplification or attenuation of various extremes in the derivative. However, the influence of surface moisture on the yield of plastics is usually very low and depends on the spectral differences between the different plastics.
Subject(s)
Environmental Pollutants , Plastics , Polyethylene , Polyvinyl ChlorideABSTRACT
An 80-membered library of gels composed of monofunctional 2-ethyl-2-oxazoline and 2-nonyl-2-oxazoline and one of four selected difunctional 2-oxazolines (containing either ether or ester bonds) were synthesized by microwave-assisted ring-opening polymerizations. The difunctional 2-oxazolines were prepared from the thiol-ene reaction of glycol dimercaptoacetate or 2,2'-(ethylenedioxy)diethanethiol and 2-but-3'-enyl-2-oxazoline or 2-dec-9'-enyl-2-oxazoline. 53 of the gels exhibited glass-transition temperatures, which ranged from -5.9 to 45.3 °C. 13 Derivatives exhibited glass-transition temperatures in the range from 20 to 30 °C, which renders them stiff at room temperature and flexible at body temperature. The gels that did not contain any 2-ethyl-2-oxazoline acted as lipogels, whereas the gels that did not contain any 2-nonyl-2-oxazoline acted as hydrogels; all other gels may be classified as amphigels. The swelling degrees were measured by gravimetry and maximum swelling degrees of 6 (in water) were observed for the gels with the lowest degrees of crosslinking. In a second approach, the synthesis of crosslinked networks had been achieved by performing the polymeranalogous thiol-ene reaction of copoly(2-oxazoline)s containing olefinic side-chains and glycol dimercaptoacetate. This soft strategy enabled the straightforward loading of such gels with active pharmaceutical ingredients without altering them. This method delivered gels with selected composition exhibiting a targeted disc-shape and loaded with active pharmaceutical ingredients from one-step syntheses. The maximum swelling degrees of these specimens were found to be in accordance with the ones from the first route investigated. Preliminary degradation studies were performed at 25 °C; these types of gels were found to be degraded in alkaline media as well as by esterases.