ABSTRACT
Electronic waste recycling is a strategy that contributes to implement a circular economy model which include reuse, component and raw material recovery and minimum final deposition. Given the importance of reincorporating the components of electronic devices into the productive chain and a correct recovery for some hazardous metals such as lead contained in such residues. This study is focused on the effect of maximum available content (MAC) of metal, sulfuric acid initial concentration, agitation velocity, and oxidising agent on the recovery of copper, lead and iron from electronic waste through acid leaching. A solid-state characterization before and after treatment and electrochemical analysis was carried out to analyse MCA effects and surface chemistry. It was found that sub-millimetric particles show a better available extraction percentage in case of copper and iron, being opposite for lead. Presence of hydrogen peroxide enhance the extraction efficiency, however, this cause iron and lead precipitation, therefore it is inefficient for metals recovery as well as for reagent consumption. The presence of calcium salts reacts producing gypsum, which reduces the extraction yield of copper at particle size below 250 µm.
ABSTRACT
In this work, a pH-responsive drug-carrier based on chitosan-silica nanospheres was developed as a carrier for Albendazole (ABZ), a poorly water-soluble anthelmintic drug. Spherical silica nanoparticles were obtained by Stöber method and further etched to obtain mesoporous particles with sizes ranging from 350 to 400 nm. The specific BET area of nanoparticles increased from 15 m2/g to 150 m2/g for etched silica, which also exhibited a uniform pore size distribution. X-ray powder diffraction showed the presence of amorphous phase of silica and a low-intensity peak attributed to ABZ for the drug-loaded nanoparticles. A uniform layer of chitosan was obtained ranging from 10 to 15 nm in thickness due to the small concentration of chitosan used (0.45 mg of chitosan/mg of SiO2). The in vitro evaluation of hybrid nanoparticles was performed using four cervical cancer cell lines CaSki, HeLa, SiHa and C33A, showing a significant reduction in cell proliferation (>85%) after 72 h. Therefore, we confirmed the encapsulation and bioavailability of the drug, which was released in a controlled way, and the presence of chitosan delayed the release, which could be of interest for the development of prolonged release drug delivery systems.