ABSTRACT
Three isocoumarins, ascoisocoumarin A (1), embeurekol (2), and sclerotinin A (3), and five biosynthetically related derivatives, ascospinols A-C (4, 6, and 7), and talaflavuols C and B (5 and 8), together with twelve polyketides or terpenes (9-20) were isolated from the fungus Aspergillus sp. LY-1-2 inhabited in a sample of Cordyceps sp. Most of them belong to the family of oxygen-containing aromatic compounds and compounds 1, 4, 6, and 7 are previously undescribed compounds. Their planar structures were established by a combined spectroscopic analysis of HRESIMS and NMR, and their stereochemistry was determined by 13C NMR calculations with sorted training set (STS) protocol analysis, and ECD calculations. New compounds 1 and 6 displayed potential anti-inflammatory effects in lipopolysaccharide (LPS)-induced BV2 microglia cells.
ABSTRACT
Seed predation by insect herbivores reduces crop production worldwide. Foraging on seeds at pre-dispersal generally means that females need to find the suitable host plant within a relatively short timeframe in order to synchronize larval development with seed production. The mechanistic understanding of host finding by seed pests can be harnessed for more sustainable pest management strategies. We here studied the chemical communication between the bean bug Riptortus pedestris, a major pest of legumes, and several crop species and cultivars in the Fabaceae. Via a comparative chemical analysis, we found that 1-octen-3-ol is the principal constituent of the floral scents of most species tested in the subfamily Faboideae, including soybean and faba bean. With field trapping and laboratory bioassays, including electroantennography, we further revealed that this compound can be perceived, and stimulate attraction responses, by R. pedestris nymphs and adults. The addition of 1-octen-3-ol to pheromone traps might therefore improve trapping efficacy for controlling populations of this important granivore pest on legumes.
Subject(s)
Fabaceae , Odorants , Vegetables , Seeds , PheromonesABSTRACT
To investigate the relationship between surface microstructure and wear mechanism in D2/U71Mn wheel-rail material under different contact stress conditions, rolling wear tests using a GPM-40 wear machine to simulate the wheel-rail operation was performed. After wear tests, an optical microscope (OM), scanning electron microscope (SEM) and micro-hardness testers were used to characterize the microstructure and fatigue wear cracks. The results show that the thickness of the plastic deformation layer and surface hardness is increased with the increase of contact stress. Under high contact stress condition (1200 MPa), the severe plastic deformation layer led to the formation of fatigue wear of wheel-rail samples. Under a contact stress of 700 MPa, the wear mechanism of samples is adhesive wear and wear rate is low. With the increase of contact stress, the fatigue cracks are gradually severe. Under a contact stress of 1200 MPa, the wear mechanism of samples becomes fatigue wear and the fatigue wear cracks cause the increase of wear rate. The fatigue wear can accelerate the wear failure of wheel-rail samples. The fatigue wear cracks of wheel samples are severer than that of rail samples due to both the rate of plastic strain and the content of proeutectoid ferrite.