In situ fabrication of Ag decorated porous ZnO photocatalyst via inorganic-organic hybrid transformation for degradation of organic pollutant and bacterial inactivation.

In this study, in situ silver (Ag) - porous ZnO photocatalysts were synthesized via solvothermal and post-annealing treatment. The formation of the porous ZnO structure due to the removal of organic moieties from the inorganic-organic hybrids Ag-ZnS(en)0.5 during the annealing process. The optimal Ag-ZnO photocatalyst showed excellent photocatalytic degradation activity, with 95.5% orange II dye and 97.2% bisphenol A (BPA) degradation under visible light conditions. Additionally, the photocatalytic inactivation of Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) led to a 97% inactivation rate after 2 h under dark conditions. Trapping experiments suggest that the superoxide anion (O2-) radicals are the main active species to degrade the organic dye. The improved photocatalytic dye degradation activity and inactivation of bacteria were attributed to the synergistic effect of Ag and porous ZnO structure, increased surface area, and efficiently separated the photoexcited charge carriers. This work could provide an effective strategy for the synthesis of porous structures toward organic pollutant degradation and bacterial inactivation in wastewater.

Porous Zn1-xCdxSe/ZnO Nanorod Photoanode Fabricated from ZnO Building Blocks Grown on Zn Foil for Photoelectrochemical Solar Hydrogen Production.

Solar energy is the most promising, efficient, environmentally friendly energy source with the potential to meet global demand due to its non-polluting nature. Herein, a porous Zn1-xCdxSe/ZnO nanorod (NR) heterojunction was synthesized by hydrothermal and low-temperature solvothermal methods. First, the ZnO NR was grown on a Zinc foil, and an inorganic-organic hybrid ZnSe(en)0.5 material was developed by the low-temperature solvothermal method. In this work, the ZnO NR acted as a base material and a building block for the growth of ZnSe(en)0.5. Moreover, after the solvothermal process, the reduced Se2- reacts with the ZnO NR and forms inorganic-organic hybrid ZnSe(en)0.5. After the selenization process, the obtained material shows a red brick color due to the absorbance of excessive Se metal particles during the solvothermal process. Furthermore, in order to enhance the photoelectrochemical properties, the Cd2+ ion exchange method was applied at various temperatures (140, 160, and 180 °C for 3 h) to produce a precursor material to a porous Zn1-xCdxSe/ZnO NR nanostructure. The optimum Zn1-xCdxSe/ZnO NR-160 photoanode showed a high photocurrent density of 7.8 mA·cm-2 at -0.5 V vs. Ag/AgCl with a hydrogen evolution rate of 199 µmol·cm-2/3 h. The improved photocurrent performance was attributed to effective light absorption and prolonged recombination lifetime.

Understanding systematic growth mechanism of porous Zn1-xCdxSe/TiO2 nanorod heterojunction from ZnSe(en)0.5/TiO2 photoanodes for bias-free solar hydrogen evolution.

Herein, a porous Zn1-xCdxSe structure was developed on TiO2 nanorod (NR) array for photoelectrochemical (PEC) application. Firstly, TiO2 NR and ZnO/TiO2 NR photoanode were synthesized via a series of hydrothermal methods on FTO. Next, the solvothermal synthesis method was adopted to develop inorganic-organic hybrid ZnSe(en)0.5 on ZnO /TiO2 NR-based electrode using different concentrations of the selenium (Se). We found that the ZnO NR acts as a mother material for the formation of inorganic-organic hybrid ZnSe(en)0.5, whereas TiO2 NR acts as a building block. In order to further improve the PEC charge transfer performance, inorganic-organic hybrid ZnSe(en)0.5/TiO2 NR electrode was transferred into a porous Zn1-xCdxSe/TiO2 NR photoanode using the Cd2+ ion-exchange method. The optimized porous Zn1-xCdxSe/TiO2 NR -(2) photoanode converted from ZnSe(en)0.5 -(2) electrode (optimized Se concentration) showed a higher photocurrent density of 6.6 mA·cm-2 at applied potential 0 V vs. Ag/AgCl. The enhanced photocurrent density was owing to the effective light absorption, enhanced charge separation, delay the charge recombination, and porous structure of Zn1-xCdxSe. This work highlights the promising strategy for the synthesis of porous Zn1-xCdxSe/TiO2 NR from inorganic-organic ZnSe(en)0.5/TiO2 NR for effective charge separation and prolonging the lifetime during the photoelectrochemical reaction.

Topotactic and Self-Templated Fabrication of Zn1-xCdxSe Porous Nanobelt-ZnO Nanorod for Photoelectrochemical Hydrogen Production.

Herein, we propose the topotactic and self-templated fabrication of Zn1-xCdxSe porous nanobelt-ZnO nanorod (termed as ZnCdSe/ZnO) photoelectrode via the cadmium (Cd2+) ion-exchange process on zinc (Zn) foil. Inorganic-organic hybrid ZnSe(en)0.5 nanobelt (NB) was synthesized on Zn foil by a facial solvothermal method at different temperatures of 140, 160, and 180 °C for 12 h. The interfacial properties and photoelectrochemical (PEC) performance of inorganic-organic ZnSe(en)0.5 NB fabricated through the Cd2+ ion-exchange method at different time durations of 6, 12, 18, and 24 h at 140 °C were investigated. The TEM analysis results indicate that the inorganic-organic ZnSe(en)0.5 NB transformed into ZnCdSe and a self-assembled ZnO formed on the Zn foil. In particular Cd2+ ion temperature (140 °C/18 h), the optimized ZnCdSe/ZnO-(F) photoelectrode shows an excellent photocurrent density of 14 mA·cm-2 at 0 V vs Ag/AgCl with 219 µmol·cm-2 hydrogen gas evolution for 3 h under 1 sun illumination. The higher photocurrent value resulted from the optimum growth of ZnO, the formation of porous ZnCdSe, and the effective electrolyte penetration for electron-hole pair separation. The photoluminescence spectroscopy shows that the photoexcited charged carriers promoted a longer lifetime. Furthermore, we provide a full account of the possible charge-transfer mechanism during PEC hydrogen production.