ABSTRACT
For inorganic thermoelectric materials, Seebeck coefficient and electrical conductivity are interdependent, and hence optimization of thermoelectric performance is challenging. In this work we show that thermoelectric performance of PEDOT:PSS can be enhanced by greatly improving its electrical conductivity in contrast to inorganic thermoelectric materials. Free-standing flexible and smooth PEDOT:PSS bulky papers were prepared using vacuum-assisted filtration. The electrical conductivity was enhanced to 640, 800, 1300, and 1900 S cm(-1) by treating PEDOT:PSS with ethylene glycol, polyethylene glycol, methanol, and formic acid, respectively. The Seebeck coefficient did not show significant variation with the tremendous conductivity enhancement being 21.4 and 20.6 µV K(-1) for ethylene glycol- and formic acid-treated papers, respectively. This is because secondary dopants, which increase electrical conductivity, do not change oxidation level of PEDOT. A maximum power factor of 80.6 µW m(-1) K(-2) was shown for formic acid-treated samples, while it was only 29.3 µW m(-1) K(-2) for ethylene glycol treatment. Coupled with intrinsically low thermal conductivity of PEDOT:PSS, ZT ≈ 0.32 was measured at room temperature using Harman method. We investigated the reasons behind the greatly enhanced thermoelectric performance.