ABSTRACT
This in vitro study evaluated the influence of radiant exposure and material shade on the degree of conversion (DC) and microhardness of a resin-based composite (RBC). Sixty-four RBC specimens in shades A1E (enamel) and A4D (dentin) were light cured at a calibrated exitance of 1000 mW/cm2 for 5, 10, 15, or 20 seconds, resulting in radiant exposure levels of 5, 10, 15, or 20 J/cm2. The DC was determined using Fourier-transform infrared spectroscopy (n = 3 per shade per exposure level). The Knoop hardness number (KHN) was measured on the top and bottom surfaces of each specimen (n = 5 per shade per exposure level). Data were analyzed using 2- and 3-way analyses of variance and post hoc Tukey tests (α = 0.05). The RBC shade did not affect the DC (P = 0.860), and the lowest DC values were achieved with an exposure level of 5 J/cm2 (P < 0.001). The shade did not affect the KHN on the top surface, but the radiant exposure level did, with the application of 5 J/cm2 resulting in significantly lower values (P < 0.05). For the bottom surface, shade A1E showed significantly higher KHN values than A4D (P < 0.001). An increase in the radiant exposure led to increased DC and KHN for both shades of RBC until reaching a saturation point of 10 J/cm2 for A1E and the top surface of A4D. The darker and more opaque shade was not adequately polymerized at a 2-mm depth, even when the highest radiant exposure level was applied.
Subject(s)
Composite Resins , Hardness , Materials Testing , Composite Resins/chemistry , Composite Resins/therapeutic use , Spectroscopy, Fourier Transform Infrared , Color , Humans , Polymerization , Surface Properties , Curing Lights, Dental , In Vitro Techniques , Dental Materials/chemistry , Light-Curing of Dental Adhesives/methodsABSTRACT
OBJECTIVE: To investigate the effect of hydrophilic/permeable polymer matrices on water sorption/solubility (WS/SL), Ca2+ release, mechanical properties and hydrolytic degradation of composites containing dicalcium phosphate dihydrate (DCPD) particles. METHODS: Six composites were tested, all with 10 vol% of glass particles and either 30 vol% or 40 vol% DCPD. Composites containing 1BisGMA:1TEGDMA in mols (at both inorganic levels) were considered controls. Four materials were formulated where 0.25 or 0.5 of the BisGMA/TEGDMA was replaced by pyromellitic dianhydride glycerol dimethacrylate (PMGDM)/ polyethylene glycol dimethacrylate (PEGDMA). Composites were tested for degree of conversion (FTIR spectroscopy), WS/SL (ISO 4049) and Ca2+ release (inductively coupled plasma optical emission spectroscopy). Fracture toughness (FT) and biaxial flexural strength/modulus (BFS/FM) were determined after 24 h and 60 days in water. The contributions of diffusional and relaxational mechanisms to Ca2+ release kinetics were analyzed using the semi-empirical Salim-Peppas model. Data were analysed by ANOVA/Tukey test (alpha: 0.05). RESULTS: WS/SL was higher for composites containing PMGDM/PEGDMA compared to the controls (p < 0.001). Only at 40% DCPD the 0.5 PMGDM/PEGDMA composite showed statistically higher Ca2+ release than the control. Relaxation diffusion was the main release mechanism. Initial FT was not negatively affected by matrix composition. BFS (both DCPD fractions) and FM (30% DCPD) were lower for composites with hydrophilic/permeable networks (p < 0.01). After 60 days in water, composites with PMGDM/PEGDMA presented significant reductions in FT, while all composites had reductions in BFS/FM. SIGNIFICANCE: Increasing matrix hydrophilicity/permeability significantly increased Ca2+ release only at a high DCPD fraction.
Subject(s)
Calcium Phosphates , Composite Resins , Flexural Strength , Hydrophobic and Hydrophilic Interactions , Materials Testing , Methacrylates , Polyethylene Glycols , Polymethacrylic Acids , Composite Resins/chemistry , Polyethylene Glycols/chemistry , Methacrylates/chemistry , Calcium Phosphates/chemistry , Polymethacrylic Acids/chemistry , Calcium/chemistry , Solubility , Spectroscopy, Fourier Transform Infrared , Bisphenol A-Glycidyl Methacrylate/chemistry , Water/chemistry , Elastic Modulus , BenzoatesABSTRACT
OBJECTIVES: to assess the impact of universal adhesives, cured with single-peak and polywave LEDs, on the metabolic activity and cytokine release of human dental pulp stem cells (hDPSCs). In addition, analyze the degree of conversion (DC) of the adhesives cured with the different LEDs. METHODS: Discs (5 mm diameter, 1 mm thick) were prepared using three universal adhesives: Single Bond Universal (SBU, 3 M ESPE), Optibond Universal (OBU, Kerr), and Zipbond Universal (ZBU, SDI). These discs were cured for 40 s using a single-peak (DeepCure, 3 M ESPE) or a polywave light-emmiting diode (LED) curing unit (Valo Grand, Ultradent). After 24 h, the specimens were placed in 24-well culture plates, each containing 1 mL of culture medium for 24 h. hDPSCs (1.8 ×104) were seeded in 96-well plates and allowed to grow for 24 h. Subsequently, the cells were exposed to the extracts (culture medium containing eluates from the adhesive discs) for an additional 24 h. Cells not exposed to the extracts were used as a control group. The mitochondrial metabolism was assessed using the MTT assay and the cytokine release evaluated through MAGPIX. The degree of conversion of the adhesives was analyzed using FTIR (n = 5). The results were analyzed by ANOVA two-way and Tukey's test. RESULTS: OBU and ZBU eluates caused a statistically significant reduction in mitochondrial metabolism, regardless of the LED used, indicating their cytotoxicity. In contrast, SBU did not significantly affect the MTT results, resembling the control group. A higher release of cytokines IL-1, IL-6, IL-10, and TNF-α were found in association to ZBU. SBU, on the other hand, increased the release of IL-8. OBU did not influenced the cytokine release. SBU presented the higher DC, while OBU and ZBU had similar DC, lower than SBU. SIGNIFICANCE: In conclusion, universal adhesives exhibit toxicity towards hDPSCs, but the extent of toxicity varies depending on the adhesive material. ZBU was associated with increased cytokine release, particularly pro-inflammatory mediators, from hDPSCs. The different LEDs did not influenced the cytotoxicity of the evaluated adhesives.
Subject(s)
Curing Lights, Dental , Cytokines , Dental Cements , Dental Pulp , Materials Testing , Stem Cells , Humans , Dental Pulp/cytology , Cytokines/metabolism , Dental Cements/chemistry , Dental Cements/pharmacology , Light-Curing of Dental Adhesives , Resin Cements/chemistry , Resin Cements/toxicity , Cells, Cultured , Bisphenol A-Glycidyl Methacrylate/toxicity , Bisphenol A-Glycidyl Methacrylate/chemistryABSTRACT
Background: Evaluate the effects of incorporating silica-coated silver nanoparticles (Ag@SiO2 NPs) into odontological clinic resin materials. Material and Methods: Silver nanoparticles coated with silicon dioxide were added to the experimental resin matrix at 1, 3, and 5wt%. Degree of conversion (DC), optical properties (total transmittance and color change), and microstructural analysis were evaluated. Materials were tested for silver ion release, cytotoxicity in dental pulp fibroblasts, Streptococcus mutans biofilm growth by Colony-Forming Unit (CFU) and confocal laser scanning microscopy (CLSM). Results: Groups had a similar DC, despite significant differences observed in transmittance and color change analysis for all groups with NPs. Silver ion release values were below the detection limit after 72h for all groups, and NPs incorporation did not show a statistical difference from the control on pulp fibroblasts assay. After 72h, the CFU count was significantly reduced by 74% from 3wt% of Ag@SiO2NPs. CLSM evaluation on S. mutans colonies showed a dose-dependent decrease in the emitted fluorescence. Conclusions: The application of Ag@SiO2 NPs in a resinous matrix, demonstrates a significant reduction of S. mutans CFU in oral biofilm, at concentrations from 3wt%, without an increase in cytotoxicity. The reduced transmittance values did not affect the DC, although a significant color change was perceived in all concentrations. Key words:Nanoparticles, Silver Compounds, Composite Dental Resin, Anti-Bacterial Agent, Optical Imaging.
ABSTRACT
In recent years, alternative pulpal therapies targeting dentinogenesis signaling pathways using different peptides have been investigated. The aim of this study was to verify the effectiveness of poly(aspartic acid), pAsp, in dentin regeneration using an animal model. METHODS: Mechanical pulp exposure was performed in the upper molars of 56 Wistar rats, randomly divided as follows (n = 14): control (no treatment); MTA group-pulp capping with mineral trioxide aggregate (MTA Angelus); pAsp group-application of 20 µL of pAsp solution (25 mg·mL-1); MTA+pAsp group-application of MTA mixed with pAsp (5:1 by mass). Animals were euthanized after 7 or 21 days. Histological sections were submitted to hematoxylin-eosin and Brown and Brenn staining and immunohistochemical analysis for osteopontin (OPN) and dentin matrix protein 1 (DMP 1). RESULTS: At 7 days, an acute inflammatory infiltrate and the presence of disorganized mineralized tissue were observed in all groups. At 21 days, the quality and thickness of the reparative dentin in treated groups were superior to the control, and bacterial contamination was observed in two MTA-pAsp specimens. While all treated groups showed intense immunostaining for OPN at 21 days, only the pAsp group expressed DMP 1, indicating the presence of fully differentiated odontoblast-like cells. CONCLUSION: Poly(aspartic) acid promoted dentin regeneration in rat molars in the absence of an additional calcium source and may be an alternative to MTA as a pulp-capping agent.
ABSTRACT
Objectives: This study verified the possibility of cementing fiberglass-reinforced posts using a flowable bulk-fill composite (BF), comparing its push-out bond strength and microhardness with these properties of 3 luting materials. Materials and Methods: Sixty endodontically treated bovine roots were used. Posts were cemented using conventional dual-cured cement (CC); self-adhesive cement (SA); dual-cured composite (RC); and BF. Push-out bond strength (n = 10) and microhardness (n = 5) tests were performed after 1 week and 4 months of storage. Two-way repeated measures analysis of variance (ANOVA), 1-way ANOVA, t-test, and Tukey post-hoc tests were applied for the push-out bond strength and microhardness results; and Pearson correlation test was applied to verify the correlation between push-out bond strength and microhardness results (α = 0.05). Results: BF presented higher push-out bond strength than CC and SA in the cervical third before aging (p < 0.01). No differences were found between push-out bond strength before and after aging for all the luting materials (p = 0.84). Regarding hardness, only SA presented higher values measured before than after aging (p < 0.01). RC and BF did not present 80% of the maximum hardness at the apical regions. A strong positive correlation was found between the luting materials' push-out bond strength and microhardness (p < 0.01, R2 = 0.7912). Conclusions: The BF presented comparable or higher push-out bond strength and microhardness than the luting materials, which indicates that it could be used for cementing resin posts in situations where adequate light curing is possible.
ABSTRACT
OBJECTIVE: Evaluate light transmittance (%T), color change (ΔE), degree of conversion (DC), bottom-to-top Knoop microhardness (KHN), flexural strength (BFS) and modulus (FM), water sorption/solubility (WS/SL) and calcium release of resin composites containing different dicalcium phosphate dihydrate (DCPD)-to-barium glass ratios (DCPD:BG) and DCPD particle sizes. METHODS: Ten resin-based composites (50 vol% inorganic fraction) were prepared using BG (0.4 µm) and DCPD particles (12 µm, 3 µm or mixture) with DCPD:BG of 1:3, 1:1 or 3:1. A composite without DCPD was used as a control. DC, KHN, %T and ΔE were determined in 2-mm thick specimens. BFS and FM were determined after 24 h. WS/SL was determined after 7 d. Calcium release was determined by coupled plasma optical emission spectroscopy. Data were analyzed by ANOVA/Tukey test (alpha: 0.05). RESULTS: %T was significantly reduced in composites with milled, compared to pristine DCPD (p < 0.001). ΔE > 3.3 were observed with DCPD:BG of 1:1 and 3:1 formulated with milled DCPD (p < 0.001). DC increased at 1:1 and 3:1 DCPD:BG (p < 0.001). All composites presented bottom-to-top KHN of at least 0.8. BFS was not affected by DCPD size but was strongly dependent on DCPD:BG (p < 0.001). Reductions in FM were observed with milled DCPD (p < 0.001). WS/SL increased with DCPD:BG (p < 0.001). At 3DCPD: 1BG, using small DCPD particles led to a 35 % increase in calcium release (p < 0.001). SIGNIFICANCE: A trade-off between strength and Ca2+ release was observed. In spite of its low strength, the formulation containing 3 DCPD: 1 glass and milled DCPD particles is preferred due to its superior Ca2+ release.
Subject(s)
Calcium , Phosphates , Particle Size , Materials Testing , Composite Resins/chemistryABSTRACT
OBJECTIVES: To investigate the interrelationships among handling, degree of conversion (DC), mechanical behavior and Ca2+ release of composites containing dicalcium phosphate dihydrate (DCPD, CaHPO4.2H2O), as a function of total inorganic content and DCPD: glass ratio. METHODS: Twenty-one formulations (1 BisGMA: 1 TEGDMA, in mols) with inorganic fractions ranging from zero to 50 vol% and different DCPD: glass ratios were evaluated for viscosity (parallel plate rheometer, n = 3), DC (near-FTIR spectroscopy, n = 3), fracture toughness/K1C (single-edge notched beam, n = 7-11) and 14-day Ca2+ release (inductively coupled plasma optical emission spectroscopy, n = 3). Data were analyzed by ANOVA/Tukey test (except viscosity, where Kruskal-Wallis/Dunn tests were used, α: 0.05). RESULTS: Viscosity and DC increased with DCPD: glass ratio among composites with the same inorganic content (p < 0.001). At inorganic fractions of 40 vol% and 50 vol%, keeping DCPD content at a maximum of 30 vol% did not compromise K1C. Ca2+ release showed an exponential relationship with DCPD mass fraction in the formulation (R2 = 0.986). After 14 days, a maximum of 3.8% of the Ca2+ mass in the specimen was released. CONCLUSION: Formulations containing 30 vol% DCPD and 10-20 vol% glass represent the best compromise between viscosity, K1C and Ca2+ release. Materials with 40 vol% DCPD should not be disregarded, bearing in mind that Ca2+ release will be maximized at the expense of K1C.
Subject(s)
Calcium , Phosphates , Calcium Phosphates/chemistry , Viscosity , Materials Testing , Composite Resins/chemistryABSTRACT
The study verified the influence of calcium orthophosphate (CaP):glass ratio on the degree of conversion and mechanical properties of resin-based composites containing either TEGDMA-functionalized dicalcium phosphate anhydrous (DCPA) or non-functionalized DCPA particles. The null hypotheses were that the evaluated variables are not affected by (1) CaP:glass ratio or (2) DCPA functionalization. DCPA particles were synthesized and half of them were functionalized with TEGDMA. Particle characterization included x-ray diffraction, elemental analysis, laser scattering, helium picnometry and scanning electron microscopy. Two series of composites were prepared containing either DCPA-NF (non-functionalized) or DCPA-F (functionalized), with total inorganic content of 50 vol % and DCPA:silanized barium glass (BG) ratios from 10:40 to 50:0. A composite containing 50 vol % BG was tested as control. DC was determined using FTIR spectroscopy. Biaxial flexural strength and modulus were tested after 24 h in water. Data were analyzed using Kruskal-Wallis/Dunn (flexural properties) or analysis of variance/Tukey tests (DC). Materials with similar actual DCPA contents were compared using Student's t test (alpha: 0.05). DC was higher for materials with DCPA-F, except for the 10:40 ratio. DCPA-F resulted in higher strength than DCPA-NF only at 40:10 ratio. Modulus was not affected by functionalization. Materials with similar actual DCPA contents showed differences in DC (F > NF), while no difference in flexural properties was observed between materials with 28%-30% DCPA. Both null hypotheses were rejected.
Subject(s)
Calcium , Phosphates , Humans , Composite Resins/chemistry , Materials Testing , Dental Materials , Surface PropertiesABSTRACT
This study evaluated the efficacy of experimental TEGDMA-functionalized dicalcium phosphate dihydrate (T-DCPD) filler-based resin-based composites (RBC) in preventing caries lesions around the restoration margins (secondary caries, SC). Standardized Class-II cavities were made in sound molars with the cervical margin in dentin. Cavities were filled with a commercial resin-modified glass-ionomer cement (RMGIC) or experimental RBCs containing a bisGMA-TEGDMA resin blend and one of the following inorganic fractions: 60 wt.% Ba glass (RBC-0); 40 wt.% Ba glass and 20 wt.% T-DCPD (RBC-20); or 20 wt.% Ba glass and 40 wt.% T-DCPD (RBC-40). An open-system bioreactor produced Streptococcus mutans biofilm-driven SC. Specimens were scanned using micro-CT to evaluate demineralization depths. Scanning electron microscopy and energy-dispersive X-ray spectroscopy characterized the specimen surfaces, and antimicrobial activity, buffering effect, and ion uptake by the biofilms were also evaluated. ANOVA and Tukey's tests were applied at p < 0.05. RBC-0 and RBC-20 showed SC development in dentin, while RBC-40 and RMGIC significantly reduced the lesion depth at the restoration margin (p < 0.0001). Initial enamel demineralization could be observed only around the RBC-0 and RBC-20 restorations. Direct antibiofilm activity can explain SC reduction by RMGIC, whereas a buffering effect on the acidogenicity of biofilm can explain the behavior of RBC-40. Experimental RBC with CaP-releasing functionalized T-DCPD filler could prevent SC with the same efficacy as F-releasing materials.
ABSTRACT
The latest advancements in dentin bonding have focused on strategies to impair degradation mechanisms in order to extend the longevity of bonded interfaces. Protease inhibitors can reduce collagen degradation within the hybrid layer (HL). Collagen cross-linkers allow better adhesive infiltration and also inhibit proteases activity. Particles added to adhesive can promote mineral precipitation within the HL, reducing nanoleakage and micropermeability, besides possible antimicrobial and enzymatic inhibition effects. Most of these approaches are still experimental, and aspects of the adhesive under the clinician's control are still determinant for the long-term stability of adhesive restorations.
Subject(s)
Dental Bonding , Dentin-Bonding Agents , Collagen/chemistry , Dentin/metabolism , Dentin-Bonding Agents/pharmacology , Humans , Peptide Hydrolases/metabolism , Protease Inhibitors/pharmacology , Resin CementsABSTRACT
PURPOSE: To evaluate the kinetics of polymerization and shrinkage stress of resin cements, as well as their bond strength to dentin after 24-h or one-year water storage. MATERIALS AND METHODS: Three conventional resin cements were evaluated: RelyX Ultimate (RUL), Panavia V5 (PNV), and Multilink N (MLN); and three self-adhesive resin cements: RelyX Unicem 2 (RUN), Panavia SA Cement Plus (PSA), and G-CEM LinkAce (GCL). Degree of conversion (DC), maximum polymerization rate (RPmax) and gel time values were obtained using Fourier-transform infrared spectroscopy (FTIR/ATR). Shrinkage stress values were determined with a tensiometer, using a universal testing machine (n=5). Indirect resin composite restorations (Solidex) were fabricated and cemented to the dentin surface using self-adhesive resin cements, or conventional resin cements with self-etching adhesive (n=5). Bonding performance was evaluated with the microtensile bond strength (µTBS) test after 24 h or one year of water storage. RESULTS: MLN exhibited a higher DC (76.7%), whereas the percentage of other materials differed slightly (ranging from 54% to 58.5%). The RPmax and shrinkage stress values differed significantly between the cements. PSA showed the longest gel time. Significantly higher µTBS were observed for conventional resin cements after 24-h and one-year storage; a decrease in µTBS was observed for MLN only. CONCLUSION: Self-adhesive resin cements may not perform as well as conventional resin cements. Although both categories of cements presented similar polymerization kinetics and shrinkage values, the self-adhesive resin cements showed lower µTBS compared to those of conventional resin cements. Nevertheless, storage time only affected the bonding performance of MLN.
Subject(s)
Dental Bonding , Resin Cements , Dental Bonding/methods , Dental Cements/chemistry , Dental Stress Analysis , Dentin , Dentin-Bonding Agents/chemistry , Materials Testing , Polymerization , Resin Cements/chemistry , Tensile Strength , Water/chemistryABSTRACT
The development of restorative materials containing antibacterial agents is an alternative to reduce the progression of caries lesions. OBJECTIVE: to compare the influence of the degree of crosslinking of chitosan particles loaded with dibasic calcium phosphate (DCPA) on the mechanical properties, degree of conversion (DC), and antimicrobial properties of experimental composites. METHODS: Chitosan/DCPA particles were synthesized by the electrospraying, crosslinked by 0, 8, or 16 h in glutaraldehyde, and characterized by zeta potential and minimum inhibitory concentration (MIC) against S. mutans. Experimental resin composites of Bis-GMA and TEGDMA and 59.5% of barium glass were synthesized, chitosan/DCPA particles were added at 0 or 0.5 wt% with the different crosslinking time. The materials were subject to DC analysis, three-point bending test at 24 h and 7 days, and antimicrobial assays. Data were submitted to one-way ANOVA and Tukey test (α = 0.05). RESULTS: The particles with longer crosslinking time presented higher zeta potential and MIC, and the composite containing these particles showed significantly higher biofilm inhibition than the control group. The other two groups were similar to each other and the control. The composite containing particles with 88 h crosslinking time showed the lowest flexural strength at 7 days in water, and materials with non-crosslinked particles and longer crosslinking time presented flexural strength similar to control. The flexural modulus and DC showed no statistical difference among groups. SIGNIFICANCE: composite resin containing 0.5% chitosan/DCPA particles crosslinked by 16 h showed a reduction of biofilm formation without affecting the mechanical properties in relation to the control.
Subject(s)
Anti-Infective Agents , Chitosan , Anti-Bacterial Agents/pharmacology , Bisphenol A-Glycidyl Methacrylate , Calcium Phosphates/pharmacology , Composite Resins/pharmacology , Materials Testing , Methacrylates , Phthalic AcidsABSTRACT
OBJECTIVES: to evaluate the effect of different concentrations of an iodonium salt on the degree of conversion, polymerisation rate, flexural strength and modulus of an amine-free photopolymerizable resin system. METHODS: Two series of UDMA/TEGDMA resin mixtures (1:1 mass ratio) containing 0, 0.5, 1.0 or 2.0 mol% of bis(4-methyl phenyl)iodonium hexafluorophosphate(BPI): and 1 mol% camphorquinone (CQ) were evaluated. One of the series contained 2 mol% of the amine (2-(dimethylamino)ethyl methacrylate-DMAEMA), while the other series had only CQ and BPI as photoinitiators. Polymerisation kinetics and degree of conversion (DC) were evaluated by Fourier transform near-infrared spectroscopy (n = 3). Flexural strength (FS) and modulus (E) were evaluated by a three-point bending method (n = 12). Data were analysed by two-way ANOVA and Tukey's test. RESULTS: The system containing CQ + DMAEMA + BPI provided the highest DC and FS. Amine-free resins had similar E regardless of the presence of BPI. The resins containing CQ+DMAEMA with 1 and 2 mol% of BPI presented higher E compared with others. SIGNIFICANCE: Amine-containing resins reached statistically higher DC, rate of polymerisation and FS than amine-free systems. The use of higher BPI concentrations did not improve the properties of amine-free resins.
Subject(s)
Amines , Composite Resins , Bisphenol A-Glycidyl Methacrylate , Composite Resins/chemistry , Flexural Strength , Materials Testing , Methacrylates/chemistry , Polyethylene Glycols , Polymerization , Polymethacrylic AcidsABSTRACT
OBJECTIVE: To assess the mechanical properties of two different dimethacrylate resin blends containing the photosensitizer camphorquinone (CQ) alone or in combination with one or more synergists including an amine and/or an iodonium. METHODS: Two co-monomer resin blends were formulated using Bis-GMA/TEGDMA and UDMA/TEGDMA, both at 1:1 mass ratio. Each resin blend was divided into four groups, comprising the following four photoinitiation systems: (1) CQ + 2-(dimethylamino)ethyl methacrylate (DMAEMA); (2) CQ + DMAEMA + bis(4-methyl phenyl)iodonium hexafluorophosphate (BPI); (3) CQ; and (4) CQ + BPI. Materials were evaluated for polymerisation kinetics, water sorption, solubility, flexural strength and modulus. RESULTS: BisGMA/TEGDMA with CQ showed minimal and insignificant degree of conversion and was not tested for water sorption/solubility and mechanical properties. The ternary system (i.e., CQ + DMAEMA + BPI), promoted the highest degree of conversion for each monomer blend. The resins containing amine had higher mechanical properties than the amine free. However, the UDMA amine free resins exhibited greater flexural strength and modulus than the corresponding amine free BisGMA resins. BisGMA/TEGDMA containing CQ + DMAEMA or CQ + BPI had significantly higher water sorption and solubility than the other groups. SIGNIFICANCE: Resins containing amine presented better properties than the amine-free systems. The addition of iodonium salt (BPI) improved the degree of conversion of the resins, even without an amine co-initiator. The amine-free initiator system (CQ + BPI) was more effective when used with UDMA versus BisGMA based-resins respectively.
Subject(s)
Amines , Composite Resins , Bisphenol A-Glycidyl Methacrylate , Materials Testing , PolymerizationABSTRACT
The purpose of this study was to synthesize dicalcium phosphate dihydrate (DCPD) particles functionalized with triethylene glycol dimethacrylate (TEGDMA) through different routes by varying the receptor solution: ammonium phosphate (AP groups) or calcium nitrate (CN groups) and the moment in which TEGDMA was incorporated: ab initio (ab) or at the end of dripping the solution (ap). Two syntheses were performed without adding TEGDMA (nf). The particles were characterized by X-ray diffractometry, true density (using a helium pycnometer), surface area, and scanning electron microscopy. A 20 vol% of DCPD particles from the D, E, and F groups was added to the resin matrix to determine the degree of conversion (DC), biaxial flexural strength (BFS), the flexural modulus (FM), and surface roughness after an abrasive challenge (RA). A group with silanized barium glass particles was tested as a control. The data were submitted to ANOVA/Tukey's test (DC, BFS, and RA), and the Kruskal-Wallis test (FM) (alpha = 0.05). BFS values varied between 83 and 142 MPa, and the CN_ab group presented a similar value (123 MPa) to the control group. FM values varied between 3.6 and 8.7 GPa (CN_ab and CN_nf groups, respectively), with a significant difference found only between these groups. RA did not result in significant differences. The use of calcium nitrate solution as a receptor, together with ab initio functionalization formed particles with larger surface areas. Higher BFS values were observed for the material containing DCPD particles with a higher surface area. In general, the DC, FM, and RA values were not affected by the variables studied.
Subject(s)
Polymers/chemistry , Composite Resins , Flexural StrengthABSTRACT
Protecting resin-dentin interfaces from hydrolytic and enzymatic degradation is critical for the longevity of adhesive restorations. In recent years, several strategies have been tested in vitro to induce apatite precipitation within interfibrillar and intrafibrillar collagen spaces, as well as in resin-sparse regions where the adhesive infiltration was incomplete. Also, the presence of calcium ions and other metallic ions has shown an inhibitory effect on enzymatic activity. Ion-releasing particles and biomimetic analogs have been studied for hybrid layer remineralization. Overall, remineralization strategy is dependent on the remaining mineral content. In partially demineralized dentin, residual apatite crystallites serve as nucleation sites for calcium and phosphate ions precipitation and crystal growth ("top-down" remineralization). In completely demineralized dentin where crystallites are absent (e.g., acid etched dentin) the use of mineral nano-precursors assisted by non-collagenous proteins analogs are necessary ("bottom-up" remineralization). This article reviews the approaches for hybrid layer remineralization and resin-dentin interface preservation.
Subject(s)
Biomimetics , Dentin-Bonding Agents , Dental Cements , Dentin , Microscopy, Electron, Transmission , Tooth RemineralizationABSTRACT
Abstract The purpose of this study was to synthesize dicalcium phosphate dihydrate (DCPD) particles functionalized with triethylene glycol dimethacrylate (TEGDMA) through different routes by varying the receptor solution: ammonium phosphate (AP groups) or calcium nitrate (CN groups) and the moment in which TEGDMA was incorporated: ab initio (ab) or at the end of dripping the solution (ap). Two syntheses were performed without adding TEGDMA (nf). The particles were characterized by X-ray diffractometry, true density (using a helium pycnometer), surface area, and scanning electron microscopy. A 20 vol% of DCPD particles from the D, E, and F groups was added to the resin matrix to determine the degree of conversion (DC), biaxial flexural strength (BFS), the flexural modulus (FM), and surface roughness after an abrasive challenge (RA). A group with silanized barium glass particles was tested as a control. The data were submitted to ANOVA/Tukey's test (DC, BFS, and RA), and the Kruskal-Wallis test (FM) (alpha = 0.05). BFS values varied between 83 and 142 MPa, and the CN_ab group presented a similar value (123 MPa) to the control group. FM values varied between 3.6 and 8.7 GPa (CN_ab and CN_nf groups, respectively), with a significant difference found only between these groups. RA did not result in significant differences. The use of calcium nitrate solution as a receptor, together with ab initio functionalization formed particles with larger surface areas. Higher BFS values were observed for the material containing DCPD particles with a higher surface area. In general, the DC, FM, and RA values were not affected by the variables studied.
Subject(s)
Polymers/chemistry , Composite Resins , Flexural StrengthABSTRACT
OBJETICVE: The aim of this study was to develop a composite material with antibacterial activity using MMT loaded with clorhexidine (CHX). For that it was used a BisGMA/TEGDMA matrix and added low concentration of MMT/CHX. The aim was to evaluate the drug release capacity of MMT, and not to provide reinforcement. METHODS: Six experimental composites were made with organic matrix of BisGMA/TEGDMA in equal proportions by weight. The composites received organophlizated montmorillonite with or without CHX. The concentrations were 2,5; 5 or 10% by weight. Degree of conversion (DC) was evaluated using FTIR (peak 6165 cm-1; n=5). Specimens for flexural properties (10×2×1mm) were immediate tested (24h). Elastic modulus(E) and flexural strength (FS) was measured using the three point bending test (n=10). Inibition halo was used to test the antibacterial activity against Staphylococcus aureus, Streptococcus mutans, and Porphyromonas gingivalis (n=5 for each bacteria). The inhibition of biofilm formation (BF) was evaluated by inserting polymerized disc of composite in to a culture media colonized with Streptococcus mutans (n=10). The release of CHX was measured using ultraviolet (255nm) for 10 days (n=5). The data of degree of conversion was analysed using Kruskal-Wallis/ Mann-Whitney, and the other variables using two-way ANOVA/Tukey, always considering a global level of significance of 5%. RESULTS: DC ranged from 71% to 74%. E ranged from 5.7 to 8.1GPa. FS ranged from 61.4 to 74.7MPa. There were no statistical differences among the groups for all the variables. For the three bacteria tested the composites with CHX loaded presented inhibition of growth for all concentration, except for 2,5% that did not inihibited the growth of P. gingivalis. BF was lower for the groups with 10% MMT/CHX, all groups presented BF, even those without CHX loaded. All concentrations presented release off CHX during all the 28 days analyzed. CONCLUSIONS: Within the limitation of this study it can be concluded that: all concentrations tested presented release of CHX and reduced BF. All concentration presented antibacterial activity for the three bacteria tested, except for 2,5% that did not inhibit the growth of P. gingivalis. The presence of MMT with CHX loaded did not interfere in the properties evaluated.
Subject(s)
Chlorhexidine , Composite Resins , Anti-Bacterial Agents , Dental Materials , Materials Testing , Streptococcus mutansABSTRACT
Non-invasive treatments for caries lesions are increasingly required for oral health; resin infiltration is one possible conservative option. In this study, we evaluated the effects of diphenyliodonium hexafluorophosphate salt (DPI) on experimental resin infiltrants with either (hydroxyethyl)methacrylate (HEMA) or ethanol as the diluent. A monomeric base with diglycidyl methacrylate ethoxylated (BisEMA, 25 wt%) and triethylene glycol dimethacrylate (TEGDMA, 75 wt%), 0.5 mol% of camphorquinone, and 1 mol% of ethyl-4-(dimethylamino)benzoate (EDAB) was prepared. The mixtures were divided into 12 groups according to DPI concentration (0; 0.25; 0.5; 1 mol%) and diluents (10 wt% HEMA, 10 wt% ethanol, or none). Degree of conversion (DC), water sorption (Ws), solubility (Sol), contact angle (CA), and cohesive strength (CS) tests were performed and compared to a commercial infiltrant control group (Icon). Only ethanol negatively affected DC and Sol, but both diluents negatively affected Ws and CS. Nevertheless, the presence of DPI, mainly at the 0.5 mol% concentration, compensated for the negative effects of the diluents. The commercial control group was less effective only for CS. In conclusion, 0.5% DPI seems to be the most suitable concentration to compensate for the negative effects of diluents.