ABSTRACT
Lithium metal batteries using solid electrolytes are considered to be the next-generation lithium batteries due to their enhanced energy density and safety. However, interfacial instabilities between Li-metal and solid electrolytes limit their implementation in practical batteries. Herein, Li-metal batteries using tailored garnet-type Li7-xLa3-aZr2-bO12 (LLZO) solid electrolytes is reported, which shows remarkable stability and energy density, meeting the lifespan requirements of commercial applications. We demonstrate that the compatibility between LLZO and lithium metal is crucial for long-term stability, which is accomplished by bulk dopant regulating and dopant-specific interfacial treatment using protonation/etching. An all-solid-state with 5 mAh cm-2 cathode delivers a cumulative capacity of over 4000 mAh cm-2 at 3 mA cm-2, which to the best of our knowledge, is the highest cycling parameter reported for Li-metal batteries with LLZOs. These findings are expected to promote the development of solid-state Li-metal batteries by highlighting the efficacy of the coupled bulk and interface doping of solid electrolytes.
ABSTRACT
A stable electrolyte is required for use in the open-packing environment of a Li-O2 battery system. Herein, a gelled quasi-solid-state electrolyte containing SiO2 nanoparticles was designed, in order to obtain a solidified electrolyte with a high discharge capacity and long cyclability. We successfully fabricated an organic-inorganic hybrid matrix with a gelled structure, which exhibited high ionic conductivity, thereby enhancing the discharge capacity of the Li-O2 battery. In particular, the improved electrochemical stability of the gelled cathode led to long-term cyclability. The organic-inorganic hybrid matrix with the gelled structure played a beneficial role in improving the ionic conductivity and long-term cyclability and diminished electrolyte evaporation. The experimental and theoretical findings both suggest that the preferential binding between amorphous SiO2 and polyethylene glycol dimethyl ether (PEGDME) solvent led to the formation of the solidified gelled electrolyte and improved electrochemical stability during cycling, while enhancing the stability of the quasi-solid state Li-O2 battery.