Effect of surface treatments on anodic oxide film growth and electrochemical properties of tantalum used for biomedical applications.

Self-expandable nitinol (nickel-titanium) alloys and 316L stainless steel are the most commonly used materials in the production of coronary stents. However, tantalum (Ta) has already been used to make stents for endovascular surgery and may constitute an alternative to other materials because of its better electrochemical performance, namely its higher corrosion resistance, as well as its radio-opacity. The characterization of wet polished, chemically polished, wet polished anodized, and chemically polished anodized Ta electrodes has been performed in a 0.15 M NaCl solution (simulated body fluid) using Ucorr = f(t) measurements, anodic polarizations, capacity measurements, anodic oxidations, and atomic force microscopy (AFM) imaging. Anodic polarization curves have shown that the abnormal current density peak with a maximum value around 1.65 V (critical applied potential, Uc) disappeared for the anodized electrodes indicating a probable relationship between the surface states and the film growth. These results are confirmed by capacity measurements. The behavior of wet polished and chemically polished electrodes during anodic oxidations seemingly indicated that for these particular treatments the film growth is different. The AFM images and roughness measurements have shown that chemical polishing produced smoother electrodes, a fact probably related to the differences in film growth.

In vitro and in vivo models for the evaluation of new inhibitors of human steroid sulfatase, devoid of residual estrogenic activity.

The goal of our research project is to develop a new class of orally active drugs, estrone sulfatase inhibitors, for the treatment of estrogen-dependent (receptor positive) breast cancer. Several compounds were synthesized and their pharmacological potencies explored. Based on encouraging preliminary results, three of them, TX 1299, TX 1492 and TX 1506 were further studied in vitro as well as in vivo. They proved to be strong inhibitors of estrone sulfatase when measured on the whole human JEG-3 choriocarcinoma and MCF-7 breast cancer cells and their IC(50)s found to be in the range of known standard inhibitors. Their residual estrogenic activity was checked as negative in the test of induction of alkaline phosphatase (APase) activity in whole human endometrial adenocarcinoma Ishikawa cells. In addition, their effect on aromatase activity in JEG-3 cells was also examined, since the goal of inhibiting both sulfatase and aromatase activities appears very attractive. However, it has been unsuccessful so far. Then, in vivo potencies of TX 1299, the lead compound in our chemical series, were evaluated in comparison with 6,6,7-COUMATE, a non-steroidal standard, in two different rat models and by oral route. First, the absence of any residual estrogenic activity for these compounds was checked in the uterotrophic model in prepubescent female rats. Second, antiuterotrophic activity in adult ovariectomized rat supplemented with estrone sulfate (E(1)S), showed that both compounds were potent inhibitors, the power of TX 1299 relative to 6,6,7-COUMATE being around 80%. This assay was combined with uterine sulfatase level determination and confirmed the complete inhibition of this enzyme within the target organ. Preliminary studies indicated that other non-steroid compounds in the Théramex series were potent in vitro and in vivo inhibitors of estrone sulfatase in rats and further studies are in progress.

Electrochemical and microstructural studies of tantalum and its oxide films for biomedical applications in endovascular surgery.

The most popular coronary stents are made of 316L stainless steel and self-expandable Nitinol. Nevertheless, Ta has already been used to make stents for endovascular surgery and may constitute a good alternative to the other materials because of its higher corrosion resistance and radio-opacity property, which may facilitate the follow-up of stent catheterization. The characterization of Ta and its natural passive oxide films has been performed in a 0.15 M NaCl solution (simulated body fluid - SBF) using anodic polarizations, electrochemical impedance spectroscopy and photoelectrochemical techniques. Changes in microstructure have been observed by atomic force microscopy (AFM). Polarization curves show the existence of a current density increase between 1.40 and 1.80 V. Bode complex plots show that some perturbation of the film occurred in this potential interval which may be associated with a decrease in polarization resistance, Rp, indicating that the film may be less resistant to corrosive attack. Mott-Schottky capacity measurements show that the density of donors, Nd, varies with polarization. The optical band gap, E(g), which is equal to 4.1 eV did not show variations in our experiments. The localized formation on the electrode surface, in the above potential interval of a Ta compound (possibly an oxide-hydroxide) was observed by AFM, and this may explain the appearance of the current density peak and capacity behavior at those potentials.

Dispersions of lamellar phases of non-ionic lipids in cosmetic products.

Synopsis Although aqueous dispersions of lipids in the form of particles having a lamellar structure (liposomes) are already known as excellent vehicles for pharmaceutical substances, their usefulness in cosmetic formulations has not been demonstrated. The present work shows the advantages obtained by application of such systems to the skin, and in particular the use of non-ionic lipids in aqueous dispersions. Thus, in comparison with classical formulations such as emulsions, these systems exhibit lower toxicity and permit closer control of the availability of active substances at the stratum corneum. As examples, compositions suitable for skin moisturising and for tanning products are presented.