Multiscale investigation on the chemical and anatomical changes of lignocellulosic biomass for different severities of hydrothermal treatment.

The chemical changes sustained by lignocellulosic biomass during hydrothermal treatment are reflected at multiple scales. This study proposes to benefit from this multiscale nature in order to provide a global understanding of biomass alterations during hydrothermal treatment. For this purpose, complementary imaging techniques-confocal Raman microscopy and X-ray nano-tomography-analysed by image processing and coupled to chemical measurements were used. This unique combination of analyses provided valuable information on topochemical and morphological changes of poplar samples, without the artefacts of sample preparation. At the cell wall level, holocellulose hydrolysis and lignin modifications were observed, which corresponded to anatomical modifications observed at higher scales. Overall, after treatment, samples shrank and had thinner cell walls. When subjected to more severe pre-treatments, cells were disrupted and detached from adjacent cells. Anatomical changes were then used to obtain quantitative indicators of the treatment severity. The effects of treatment at different scales can thus be quantitatively connected in both directions, from micro to macro and from macro to micro.

Shear bond strength and interfacial analysis of high-viscosity glass ionomer cement bonded to dentin with protocols including silver diammine fluoride.

PURPOSE: High-viscosity glass ionomer cements (HV-GICs) are reinforced with ultrafine, highly reactive glass particles, as well as a higher-molecular-weight polyalkenoic acid component. Silver diammine fluoride (SDF) is an agent with promising activity against active caries. The present study aimed to evaluate the shear bond strength (SBS) and interfacial morphology of a new HV-GIC bonded to dentin after treatment with various adhesive protocols including SDF. METHODS: HV-GIC cylinders were bonded to dentin after various surface treatments (6 groups, n = 22): water; polyalkenoic acid; SDF; SDF + potassium iodide (KI); SDF + KI + polyalkenoic acid; SDF + KI + two weeks of storage in water + polyalkenoic acid. For each group, 20 samples were tested for SBS after 48 h, and 2 samples were cut and subjected to environmental scanning electron microscopy (E-SEM) and energy-dispersive X-ray (EDX) analysis. RESULTS: No significant differences in SBS were found between any of the protocols tested. However, E-SEM and EDX images showed different interfaces when SDF was applied. CONCLUSION: SDF has no influence on the adhesion of HV-GIC to sound dentin and could potentially improve the cario-resistance of the dentin/HV-GIC interface.

Shear bond strength and interface analysis between a resin composite and a recent high-viscous glass ionomer cement bonded with various adhesive systems.

OBJECTIVE: This study investigated the shear bond strength (SBS) and interface between a resin composite and a new high-viscous glass ionomer cement (HV-GIC), a HV-GIC, a resin-modified glass ionomer cement (RM-GIC), a bulk-fill flowable composite, and a regular flowable composite bonded with various adhesive systems. METHODS AND MATERIALS: A resin composite (Filtek Z350) was bonded to a new HV-GIC (EQUIA Forte Fil) using various adhesive systems, including a universal adhesive in self-etch and etch-and-rinse mode (Scotchbond Universal), a two-step etch-and-rinse adhesive (Scotchbond 1-XT), a one-step self-etch adhesive (Optibond All-in-one) tested also after silane application (Monobond Plus), and a coating material (EQUIA Forte Coat). The resin composite was also bonded to a HV-GIC (Fuji IX GP), a RM-GIC (Fuji II LC), a bulk-fill flowable composite (SDR), and a regular flowable composite (Tetric Evo Flow) with the universal adhesive in self-etch mode (Scotchbond Universal). Two-way ANOVA followed by Dunnett's post hoc test was used to investigate the difference in SBS. Failures were analyzed by chi-square test. Bonding interfaces were examined by environmental scanning electron microscopy (E-SEM). RESULTS: SBS to EQUIA Forte Fil was significantly lower with Scotchbond 1-XT than with all other adhesive systems. By using Scotchbond Universal with the self-etch technique, the SBS to EQUIA Forte Fil was significantly higher than the SBS to Fuji IX GP and significantly lower than the SBS to Fuji II LC, SDR, and Tetric Evo Flow. E-SEM images showed an intimate contact at all interfaces examined. CONCLUSION: EQUIA Forte Fil showed satisfactory SBS and interfaces with all adhesives tested. CLINICAL RELEVANCE: Bonding between the resin composite and HV-GIC can be achieved using a universal adhesive in self-etch mode, an easy-to-use adhesive system.