ABSTRACT
OBJECTIVES: This study evaluated the effect of brushing orthodontic clear ligatures with a whitening dentifrice containing a blue pigment (Close Up White Now, Unilever, London, UK) on their color stability, when exposed to a staining agent. MATERIALS AND METHODS: Ligatures from 3M Unitek (Monrovia, CA, USA) and Morelli (Sorocaba, SP, Brazil) were tested. Baseline color measurements were performed and nonstained groups (control) were stored in distilled water whereas test groups were exposed for 1 hour daily to red wine. Specimens were brushed daily using regular or whitening dentifrice. Color measurements were repeated after 7, 14, 21, and 28 days using a spectrophotometer based on the CIE L*a*b* system. RESULTS: Decreased luminosity (CIE L*), increased red discoloration (CIE a* axis), and increased yellow discoloration (CIE b* axis) were generally observed for ligatures exposed to the staining agent. Color variation was generally lower in specimens brushed with regular dentifrice, but ligatures brushed with whitening dentifrice were generally less red and less yellow than regular dentifrice. The whitening dentifrice led to blue discoloration trend, with visually detectable differences particularly apparent according to storage condition and ligature brand. CONCLUSIONS: The whitening dentifrice containing blue pigment did not improve the ligature color stability, but it decreased yellow discoloration and increased a blue coloration. CLINICAL SIGNIFICANCE: The use of a whitening dentifrice containing blue pigment during orthodontic treatment might decrease the yellow discoloration of elastic ligatures.
Subject(s)
Color , Orthodontics , Tooth Bleaching , Toothpastes , HumansABSTRACT
OBJECTIVE: To establish the relationship between photoinitiator system and nanofiller size on the optical properties and cure efficiency of model composites. METHODS: Model composites based on BisGMA/TEGDMA (60:40mol%) were loaded with 40wt% of 7nm or 16nm-sized filler particles. One of the following photoinitiator systems was added: camphorquinone (CQ) associated with an amine (EDMAB), monoacylphosphine oxide (TPO), or bysacylphosphine oxide (BAPO). The optical properties of disk-shaped specimens were measured 24h after curing and repeated after storage in water for 90 days and coffee for 15 days. A large spectrum LED unit (Bluephase G2, Ivoclar Vivadent) was used for photoactivation. CIE L*a*b* parameters, color difference (ΔE), and translucency parameter (TP) were calculated. Knoop hardness readings were taken at top and bottom composite surfaces. Cure efficiency was determined by bottom/top hardness ratio. Data were statistically analyzed at α=0.05 significance level. RESULTS: Composites formulated with 16nm particles had higher CIE L* than those with 7nm particles in all storage conditions. BAPO-based composites generally had lower CIE a* than the other composites. The group TPO+16nm before storage and all groups with 16nm-sized particles after storage had lower CIE b* (i.e. lower degree of yellowing) than the other groups. TPO-based materials had higher color stability. The cure efficiency was not significantly affected by photoinitiator system or particle size. CQ+7nm had the lowest and BAPO+16nm the highest hardness values. SIGNIFICANCE: Combination of photoinitiator system and filler particle size might affect the optical properties of composites, with low influence on cure efficiency.