In vitro evaluation of MgSr and MgCaSr alloys via direct culture with bone marrow derived mesenchymal stem cells.

Magnesium (Mg) and its alloys have been widely investigated as the most promising biodegradable metals to replace conventional non-degradable metals for temporary medical implant applications. New Mg alloys have been developed for medical applications in recent years; and the concept of alloying Mg with less-toxic elements have aroused tremendous interests due to the promise to address the problems associated with rapid degradation of Mg without compromising its cytocompatibility and biocompatibility. Of particular interests for orthopedic/spinal implant applications are the additions of calcium (Ca) and strontium (Sr) into Mg matrix because of their beneficial properties for bone regeneration. In this study, degradation and cytocompatibility of four binary MgSr alloys (Mg-xSr, x = 0.2, 0.5, 1 and 2 wt%) and four ternary MgCaSr alloys (Mg-1Ca-xSr, x = 0.2, 0.5, 1 and 2 wt%) were investigated and compared via direct culture with bone marrow-derived mesenchymal stem cells (BMSCs). The influence of the alloy composition on the degradation rates were studied and compared. Moreover, the cellular responses to the binary MgSr alloys and the ternary MgCaSr alloys were comparatively evaluated; and the critical factors influencing BMSC behaviors were discussed. This study screened the degradability and in vitro cytocompatibility of the binary MgSr alloys and the ternary MgCaSr alloys. Mg-1Sr, Mg-1Ca-0.5Sr and Mg-1Ca-1Sr alloys are recommended for further in vivo studies toward clinical translation due to their best overall performances in terms of degradation and cytocompatibility among all the alloys studied in the present work. STATEMENT OF SIGNIFICANCE: Traditional Mg alloys with slower degradation often contain aluminum or rare earth elements as alloying components, which raised safety and regulatory concerns. To circumvent unsafe elements, nutrient elements such as calcium (Ca) and strontium (Sr) were selected to create Mg-Sr binary alloys and Mg-Ca-Sr ternary alloys to improve the safety and biocompatibility of bioresorbable Mg alloys for medical implant applications. In this study, in vitro degradation and cellular responses to four binary Mg-xSr alloys and four ternary Mg-1Ca-xSr alloys with increasing Sr content (up to 2 wt%) were evaluated in direct culture with bone marrow derived mesenchymal stem cells (BMSCs). The roles of Sr and Ca in tuning the alloy microstructure, degradation behaviors, and BMSC responses were collectively compared in the BMSC direct culture system for the first time. The most promising alloys were identified and recommended for further in vivo studies toward clinical translation.

Degradation of Bioresorbable Mg-4Zn-1Sr Intramedullary Pins and Associated Biological Responses in Vitro and in Vivo.

This article reports the degradation and biological properties of as-drawn Mg-4Zn-1Sr (designated as ZSr41) and pure Mg (P-Mg) wires as bioresorbable intramedullary pins for bone repair. Specifically, their cytocompatibility with bone marrow derived mesenchymal stem cells (BMSCs) and degradation in vitro, and their biological effects on peri-implant tissues and in vivo degradation in rat tibiae were studied. The as-drawn ZSr41 pins showed a significantly faster degradation than P-Mg in vitro and in vivo. The in vivo average daily degradation rates of both ZSr41 and P-Mg intramedullary pins were significantly greater than their respective in vitro degradation rates, likely because the intramedullary site of implantation is highly vascularized for removal of degradation products. Importantly, the concentrations of Mg2+, Zn2+, and Sr2+ ions in the BMSC culture in vitro and their concentrations in rat blood in vivo were all lower than their respective therapeutic dosages, i.e., in a safe range. Despite of rapid degradation with a complete resorption time of 8 weeks in vivo, the ZSr41 intramedullary pins showed a significant net bone growth because of stimulatory effects of the metallic ions released. However, proportionally released OH- ions and hydrogen gas caused adverse effects on bone marrow cells and resulted in cavities in surrounding bone. Thus, properly engineering the degradation properties of Mg-based implants is critical for harvesting the bioactivities of beneficial metallic ions, while controlling adverse reactions associated with the release of OH- ions and hydrogen gas. It is necessary to further optimize the alloy processing conditions and/or modify the surfaces, for example, applying coatings onto the surface, to reduce the degradation rate of ZSr41 wires for skeletal implant applications.

A Comparison Study on the Degradation and Cytocompatibility of Mg-4Zn-xSr Alloys in Direct Culture.

This article reports the behaviors of bone-marrow-derived mesenchymal stem cells (BMSCs) in the direct culture with four Mg-4Zn-xSr alloys (x = 0.15, 0.5, 1.0, 1.5 wt %), designated as ZSr41A, B, C, and D, respectively; and a systematic comparison on the degradation of the ZSr41 alloys and their biological impact in the direct culture with different cell types in their respective media. The direct culture method, in which cells are seeded directly onto the surface of the sample, was used to investigate cellular responses at the cell-biomaterial interface in vitro. The results showed that BMSCs adhered and remained viable on the surfaces of all ZSr41 alloys, but the faster degrading ZSr41A and ZSr41B alloys showed a significantly lower amount of viable BMSCs adhered to their surfaces. Moreover, BMSCs adhered to the culture plate surrounding the samples were unaffected by the solubilized degradation products from the ZSr41 alloys. The results from the comparison study showed that the in vitro degradation rates of Mg-based biomaterials in different culture systems might be mostly affected by media buffer capacity (i.e., HCO3- concentration), and to a lesser extent, d-glucose concentration. The comparison study also indicated that BMSCs were more robust than H9 human embryonic stem cells and human umbilical vein endothelial cells for screening the cytocompatibility of Mg-based biomaterials. In general, the adhesion and viability of BMSCs at the cell-material interface were inversely proportional to the alloy degradation rates. This study presented a clinically relevant in vitro culture system for screening bioresorbable alloys in direct culture, and provided valuable guidelines for determining the degradation rates of Mg-based biomaterials.

Cytocompatibility and early inflammatory response of human endothelial cells in direct culture with Mg-Zn-Sr alloys.

Crystalline Mg-Zinc (Zn)-Strontium (Sr) ternary alloys consist of elements naturally present in the human body and provide attractive mechanical and biodegradable properties for a variety of biomedical applications. The first objective of this study was to investigate the degradation and cytocompatibility of four Mg-4Zn-xSr alloys (x=0.15, 0.5, 1.0, 1.5wt%; designated as ZSr41A, B, C, and D respectively) in the direct culture with human umbilical vein endothelial cells (HUVEC) in vitro. The second objective was to investigate, for the first time, the early-stage inflammatory response in cultured HUVECs as indicated by the induction of vascular cellular adhesion molecule-1 (VCAM-1). The results showed that the 24-h in vitro degradation of the ZSr41 alloys containing a ß-phase with a Zn/Sr at% ratio ∼1.5 was significantly faster than the ZSr41 alloys with Zn/Sr at% ∼1. Additionally, the adhesion density of HUVECs in the direct culture but not in direct contact with the ZSr41 alloys for up to 24h was not adversely affected by the degradation of the alloys. Importantly, neither culture media supplemented with up to 27.6mM Mg2+ ions nor media intentionally adjusted up to alkaline pH 9 induced any detectable adverse effects on HUVEC responses. In contrast, the significantly higher, yet non-cytotoxic, Zn2+ ion concentration from the degradation of ZSr41D alloy was likely the cause for the initially higher VCAM-1 expression on cultured HUVECs. Lastly, analysis of the HUVEC-ZSr41 interface showed near-complete absence of cell adhesion directly on the sample surface, most likely caused by either a high local alkalinity, change in surface topography, and/or surface composition. The direct culture method used in this study was proposed as a valuable tool for studying the design aspects of Zn-containing Mg-based biomaterials in vitro, in order to engineer solutions to address current shortcomings of Mg alloys for vascular device applications. STATEMENT OF SIGNIFICANCE: Magnesium (Mg) alloys specifically designed for biodegradable implant applications have been the focus of biomedical research since the early 2000s. Physicochemical properties of Mg alloys make these metallic biomaterials excellent candidates for temporary biodegradable implants in orthopedic and cardiovascular applications. As Mg alloys continue to be investigated for biomedical applications, it is necessary to understand whether Mg-based materials or the alloying elements have the intrinsic ability to direct an immune response to improve implant integration while avoiding cell-biomaterial interactions leading to chronic inflammation and/or foreign body reactions. The present study utilized the direct culture method to investigate for the first time the in vitro transient inflammatory activation of endothelial cells induced by the degradation products of Zn-containing Mg alloys.

Magnetic Nanocomposite Hydrogel for Potential Cartilage Tissue Engineering: Synthesis, Characterization, and Cytocompatibility with Bone Marrow Derived Mesenchymal Stem Cells.

Hydrogels possess high water content and closely mimic the microenvironment of extracellular matrix. In this study, we created a hybrid hydrogel containing type II collagen, hyaluronic acid (HA), and polyethylene glycol (PEG) and incorporated magnetic nanoparticles into the hybrid hydrogels of type II collagen-HA-PEG to produce a magnetic nanocomposite hydrogel (MagGel) for cartilage tissue engineering. The results showed that both the MagGel and hybrid gel (Gel) were successfully cross-linked and the MagGel responded to an external magnet while maintaining structural integrity. That is, the MagGel could travel to the tissue defect sites in physiological fluids under remote magnetic guidance. The adhesion density of bone marrow derived mesenchymal stem cells (BMSCs) on the MagGel group in vitro was similar to the control group and greater than the Gel group. The morphology of BMSCs was normal and consistent in all groups. We also found that BMSCs engulfed magnetic nanoparticles in culture and the presence of magnetic nanoparticles did not affect BMSC adhesion and morphology. We hypothesized that the ingested nanoparticles may be eventually broken down by lysosome and excreted through exocytosis; further studies are necessary to confirm this. This study reports a promising magnetic responsive nanocomposite hydrogel for potential cartilage tissue engineering applications, which should be further studied for its effects on cell functions when combined with electromagnetic stimulation.

Investigation of magnesium-zinc-calcium alloys and bone marrow derived mesenchymal stem cell response in direct culture.

Crystalline Mg-Zn-Ca ternary alloys have recently attracted significant interest for biomedical implant applications due to their promising biocompatibility, bioactivity, biodegradability and mechanical properties. The objective of this study was to characterize as-cast Mg-xZn-0.5Ca (x=0.5, 1.0, 2.0, 4.0wt.%) alloys, and determine the adhesion and morphology of bone marrow derived mesenchymal stem cells (BMSCs) at the interface with the Mg-xZn-0.5Ca alloys. The direct culture method (i.e. seeding cells directly onto the surface of the sample) was established in this study to probe the highly dynamic cell-substrate interface and thus to elucidate the mechanisms of BMSC responses to dynamic alloy degradation. The results showed that the BMSC adhesion density on these alloys was similar to the cell-only positive control and the BMSC morphology appeared more anisotropic on the rapidly degrading alloy surfaces in comparison with the cell-only positive control. Importantly, neither culture media supplemented with up to 27.6mM Mg(2+) ions nor media intentionally adjusted up to alkaline pH 9 induced any detectable adverse effects on BMSC responses. We speculated that degradation-induced dynamic surface topography played an important role in modulating cell morphology at the interface. This study presents a clinically relevant in vitro model for screening bioresorbable alloys, and provides useful design guidelines for determining the degradation rate of implants made of Mg-Zn-Ca alloys.