ABSTRACT
Ti2Nb2O9 with a tunnel-type structure is considered as a perspective negative electrode material for Li-ion batteries (LIBs) with theoretical capacity of 252 mAh g-1 corresponding to one-electron reduction/oxidation of Ti and Nb, but only ≈160 mAh g-1 has been observed practically. In this work, highly reversible capacity of 200 mAh g-1 with the average (de)lithiation potential of 1.5 V vs Li/Li+ is achieved for Ti2Nb2O9 with pseudo-2D layered morphology obtained via thermal decomposition of the NH4TiNbO5 intermediate prepared by K+â H+â NH4+ cation exchange from KTiNbO5. Using operando synchrotron powder X-ray diffraction (SXPD), single-phase (de)lithiation mechanism with 4.8% unit cell volume change is observed. Operando X-ray absorption near-edge structure (XANES) experiment revealed simultaneous Ti4+/Ti3+ and Nb5+/Nb4+ reduction/oxidation within the whole voltage range. Li+ migration barriers for Ti2Nb2O9 along [010] direction derived from density functional theory (DFT) calculations are within the 0.15-0.4 eV range depending on the Li content that is reflected in excellent C-rate capacity retention. Ti2Nb2O9 synthesized via the ion-exchange route appears as a strong contender to widely commercialized Ti-based negative electrode material Li4Ti5O12 in the next generation of high-performance LIBs.
ABSTRACT
The electrical conductivity of La0.5-xSr0.5FeO3-δ, investigated as a function of the nominal cation deficiency in the A-sublattice, x, varying from 0 to 0.02, has demonstrated a nonlinear dependence. An increase in the x value from 0 to 0.01 resulted in a considerable increase in electrical conductivity, which was shown to be attributed mainly to an increase in the mobility of the charge carriers. A combined analysis of the defect equilibrium and the charge transport in La0.5-xSr0.5FeO3-δ revealed the increase in the mobility of oxygen ions, electrons, and holes by factors of ~1.5, 1.3, and 1.7, respectively. The observed effect is assumed to be conditioned by a variation in the oxide structure under the action of the cationic vacancy formation. It was found that the cation deficiency limit in La0.5-xSr0.5FeO3-δ did not exceed 0.01. A small overstep of this limit was shown to result in the formation of (Sr,La)Fe12O19 impurity, which even in undetectable amounts reduced the conductivity of the material. The presence of (Sr,La)Fe12O19 impurity was revealed by X-ray diffraction on the ceramic surface after heat treatment at 1300 °C. It is most likely that the formation of traces of the liquid phase under these conditions is responsible for the impurity migration to the ceramic surface. The introduction of a cation deficiency of 0.01 into the A-sublattice of La0.5-xSr0.5FeO3-δ can be recommended as an effective means to enhance both the oxygen ion and the electron conductivity and improve ceramic sinterability.