ABSTRACT
We report a systematic study on the possibility of forming mixed-linker metal-organic frameworks (MOFs) spanning between the aluminum MOFs CAU-23 and MIL-160 with their 2,5-thiophenedicarboxylate (TDC) and 2,5-furandicarboxylate (FDC) linkers, respectively. The planned synthesis of a mixed-linker MOF, combining TDC and FDC in the framework turned out to yield a rather largely intricate mixture of CAU-23 and MIL-160. This is due to the different opening angles of 150° for TDC versus 120° for FDC and the concomitant cis-trans versus cis-only OH-bridges in the infinite secondary building unit {Al(µ-OH)(O2C-)} chains. At the same time, the CAU-23 phase is accompanied by the polymorphic MIL-53-TDC phase with trans-only OH-bridges. The measurement of water vapor sorption isotherms was the method of choice to confirm the formation of mixed MOFs instead of mixed-linker phases. Thereby, the water sorption isotherms indicate the simultaneous formation of both MOF phases, albeit they do not exclude mixed-linker MOFs which may have formed at low levels of substitution. The differentiation via powder X-ray diffractometry (PXRD), IR-spectroscopy and nitrogen sorption was either not conclusive enough or impossible, due to similarities of the neat MOF phases. The synthesized MOF mixtures within the TDC : FDC ratios of 38 : 62 up to 82 : 18 exhibit two or three uptake steps in the water sorption isotherm, with the first two corresponding to an overlay from the individual water sorption isotherm of CAU-23 and MIL-160 and a third one from the additional MIL-53-TDC.
ABSTRACT
In this work, we synthesized two tailored phosphorescent Pt(II) complexes bearing a cyclometalating tridentate thiazole-based C^N*N pincer luminophore (L) and exchangeable chlorido ([PtCl(L)]) or cyanido ([PtCN(L)]) coligands. While both complexes showed photoluminescence from metal-perturbed ligand-centered triplet states (3MP-LC), [PtCN(L)] reached the highest phosphorescence quantum yields and displayed a significant sensitivity toward quenching by 3O2. We encapsulated them into two Zn-based metal-organic frameworks, namely, MOF-5 and ZIF-8. The incorporation of the organometallic compounds in the resulting composites [PtCl(L)]@ZIF-8, [PtCN(L)]@ZIF-8, [PtCl(L)]@MOF-5, and [PtCN(L)]@MOF-5 was verified by powder X-ray diffractometry, scanning electron microscopy, time-resolved photoluminescence spectroscopy and microscopy, as well as N2- and Ar-gas sorption studies. The amount of encapsulated complex was determined by graphite furnace atomic absorption spectroscopy, showing a maximum loading of 3.7 wt %. If compared with their solid state forms, the solid-solution composites showed prolonged 3O2-sensitive excited state lifetimes for the complexes at room temperature, reaching up to 18.4 µs under an Ar atmosphere, which is comparable with the behavior of the complex in liquid solutions or even frozen glassy matrices at 77 K.
ABSTRACT
Bottom-up and top-down approaches are described for the challenging synthesis of Fe/Al nanoparticles (NPs) in ionic liquids (ILs) under mild conditions. The crystalline phase and morphology of the metal nanoparticles synthesized in three different ionic liquids were identified by powder X-ray diffractometry (PXRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), selected-area electron diffraction (SAED) and fast Fourier transform (FFT) of high-resolution TEM images. Characterization was completed by scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDX) for the analysis of the element composition of the whole sample consisting of the NPs and the amorphous background. The bottom-up approaches resulted in crystalline FeAl NPs on an amorphous background. The top-down approach revealed small NPs and could be identified as Fe4Al13 NPs which in the IL [OPy][NTf2] yield two absorption bands in the green-blue to green spectral region at 475 and 520 nm which give rise to a complementary red color, akin to appropriate Au NPs.
ABSTRACT
CgL1 laccase from Corynebacterium glutamicum was encapsulated into the metal-organic framework (MOF) ZIF-8 which was synthesized in a rapid enzyme friendly aqueous synthesis, the fastest inâ situ encapsulation of laccases reported to date. The obtained enzyme/MOF, i. e. laccase@ZIF-8 composite showed enhanced thermal (up to 70 °C) and chemical (N,N-dimethylformamide) stability, resulting in a stable heterogenous catalyst, suitable for high temperature reactions in organic solvents. Furthermore, the defined structure of ZIF-8 produced a size selective substrate specificity, so that substrates larger than the pore size were not accepted. Thereby, 2'-azino-bis(3-ethylbenzothiazoline-6-sulphonic acid) (ABTS) was used to verify that the enzyme is immobilized inside the MOF versus the outside surface. The enzyme@MOF composite was analyzed by atomic absorption spectroscopy (ASS) to precisely determine the enzyme loading to 2.1â wt%.
ABSTRACT
New acetylenedicarboxylate (ADC) and chlorofumarate (Fum-Cl) based hafnium-metal-organic frameworks have been synthesized by alternatively reacting acetylenedicarboxylic acid in DMF or water with appropriate hafnium salt, in the presence of acetic acid modulator. The two materials of respective ideal formulas [Hf6O4(OH)4(ADC)6] (Hf-HHU-1) and [Hf6O4(OH)4(Fum-Cl)6] (Hf-HHU-2) have been structurally characterized by powder X-ray diffraction to be UiO-66 isostructural, consisting of octahedral [Hf6O4(OH)4]12+ secondary building units each connected to other units by 12 ADC or Fum-Cl linkers into a microporous network with fcu topology. This structure was confirmed by Rietveld refinement. Hf-HHU-2 is formed by in situ hydrochlorination of acetylenedicarboxylic acid to chlorofumarate. Its presence has been determined by combined Raman spectroscopy, solid-state NMR, scanning electron microscopy, energy dispersive X-ray and X-ray photoelectron spectroscopies. Hf-HHU-1 and Hf-HHU-2 exhibit very high hydrophilicity as revealed by their water sorption profiles, meanwhile Hf-HHU-2 adsorbs CO2 with an isosteric heat of 39 kJ mol-1. Hf-HHU-2 also adsorbs molecular iodine vapor exclusively as polyiodide anions due to grafted chloro-functions on the pores surface. It has been observed that defective nanodomains with reo tolopology can be introduced in the structure of Hf-HHU-2 by variation of the linker to metal-salt molar ratio.
ABSTRACT
Two new rtl-MOFs rtl-[Cu(HIsa-az-dmpz)] and rtl-[Zn(HIsa-az-dmpz)] have been synthesized by using the new bifunctional ligand 5-(4-(3,5-dimethyl-1H-pyrazolyl)azo)isophthalic acid (H3Isa-az-dmpz). Both frameworks are potentially porous structures with DMF molecules included in the channels of the as synthesized materials. The flexible MOF rtl-[Cu(HIsa-az-dmpz)] undergoes a reversible phase change into a closed form upon activation. Consequently, rtl-[Cu(HIsa-az-dmpz)] shows S-shaped Type F-IV adsorption profiles or a gate-opening effect at cryogenic temperatures with high saturation uptakes of 360 cm3 g-1 for N2 at 77 K and 310 cm3 g-1 for CO2 at 195 K. These profiles together with the reversibility could be reproduced upon repeated measurements on the same materials. The gravimetric high-pressure CO2 adsorption shows a gate-opening at â¼10 bar with an uptake of 332 mg g-1. rtl-[Zn(HIsa-az-dmpz)] undergoes an irreversible transformation into a non-porous phase upon activation.
ABSTRACT
A strategy was developed to obtain from acetylenedicarboxylic acid either an acetylenedicarboxylate-based ZrIV metal-organic framework (MOF) with fcu topology or a halo-functionalized-MOF-801 through in situ ligand hydrohalogenation. The new materials feature exceptionally high hydrophilicity and CO2 /H2 adsorption energetics. The acetylenedicarboxylate linker and its functionalizable triple-bond discloses its potential in the engineering of microporous materials with targeted properties.