ABSTRACT
Compositional and structural elucidation of the materials is important to know their properties, chemical stability, and electro-photoactivity. The heterojunction electrocatalyst and photocatalyst activity could open a new window for solving the most urgent environmental and energy problems. Here, for the first time, we have designed and fabricated Bi2O3/bismuth titanates modified with MOF-In2S3/CdIn2S4 materials by a stepwise process. The detailed structural elucidation and formation of mixed composite phases were studied in detail. It has been found that the formed composite was efficiently utilized for the electrocatalytic H2 production reaction and the photocatalytic degradation of tetracycline. XRD patterns for the metal-organic framework-In2S3 showed a main compound of MOF, and it was assigned to a MIL-53 MOF phase, with a monoclinic structure. The addition of CdCl2 onto the MOF-In2S3 phase effectively produced a CdIn2S4 flower platform on the MOF rods. The uniform dispersion of the bismuth titanates in MOF-In2S3/CdIn2S4 materials is detected by mapping of elements obtained by dark-field HAADF-STEM. Finally, the predictions of how to integrate experiments and obtain structural results more effectively and their common development in new heterojunctions for electro-/photocatalytic applications are presented.
ABSTRACT
A gelatin-based hydrogel was infiltrated and degraded-released in two different titanium foams with porosities of 30 and 60 vol.% (Ti30 and Ti60 foams) and fabricated by the space holder technique to evaluate its potential to act as an innovative, alternative, and localised method to introduce both active pharmaceutical ingredients, such as antibiotics and non-steroidal anti-inflammatory drugs, and growth factors, such as morphogens, required after bone-tissue replacement surgeries. In addition, the kinetic behaviour was studied for both infiltration and degradation-release processes. A higher infiltration rate was observed in the Ti60 foam. The maximum infiltration hydrogel was achieved for the Ti30 and Ti60 foams after 120 min and 75 min, respectively. Further, both processes followed a Lucas-Washburn theoretical behaviour, typical for the infiltration of a fluid by capillarity in porous channels. Regarding the subsequent degradation-release process, both systems showed similar exponential degradation performance, with the full release from Ti60 foam (80 min), versus 45 min for Ti30, due to the greater interconnected porosity open to the surface of the Ti60 foam in comparison with the Ti30 foam. In addition, the optimal biocompatibility of the hydrogel was confirmed, with the total absence of cytotoxicity and the promotion of cell growth in the fibroblast cells evaluated.
ABSTRACT
The aim of this work was to study the effect of the particle size range, the freeze casting temperature and sintering temperature on the capillarity performance and mechanical properties of Ni wicks manufactured by freeze-casting. The use of Ni/camphene-polystyrene suspensions creates wicks with an open porosity above 80% and average pore sizes of 38 µm to 17 µm by tailoring the particle size ranges and freezing temperatures employed. The incorporation of PS and the use of a continuous freeze-casting process reduces the particle sedimentation and generates a highly interconnected pore structure with regular pore sizes across the sample. The capillarity performances exhibit a fast and complete water adsorption, especially in Ni wicks freeze-casted at 10 °C and sintered at 800 °C, but only when the smaller particle size range is used do Ni wicks achieve sufficient mechanical strength.