ABSTRACT
Successful protection of tissue properties against ionizing radiation effects could allow its use for terminal sterilization of musculoskeletal allografts. In this study we functionally evaluate Achilles tendon allografts processed with a previously developed radioprotective treatment based on (1-ethyl-3-(3-dimethylaminopropyl)carbodiimide) crosslinking and free radical scavenging using ascorbate and riboflavin, for ovine anterior cruciate ligament reconstruction. Arthroscopic anterior cruciate ligament (ACL) reconstruction was performed using double looped allografts, while comparing radioprotected irradiated and fresh frozen allografts after 12 and 24 weeks post-implantation, and to control irradiated grafts after 12 weeks. Radioprotection was successful at preserving early subfailure mechanical properties comparable to fresh frozen allografts. Twelve week graft stiffness and anterior-tibial (A-T) translation for radioprotected and fresh frozen allografts were comparable at 30 % of native stiffness, and 4.6 and 5 times native A-T translation, respectively. Fresh frozen allograft possessed the greatest 24 week peak load at 840 N and stiffness at 177 N/mm. Histological evidence suggested a delay in tendon to bone healing for radioprotected allografts, which was reflected in mechanical properties. There was no evidence that radioprotective treatment inhibited intra-articular graft healing. This specific radioprotective method cannot be recommended for ACL reconstruction allografts, and data suggest that future efforts to improve allograft sterilization procedures should focus on modifying or eliminating the pre-crosslinking procedure.
Subject(s)
Allografts/drug effects , Allografts/radiation effects , Anterior Cruciate Ligament Reconstruction , Radiation-Protective Agents/pharmacology , Tendons/drug effects , Wound Healing/drug effects , Animals , Biomechanical Phenomena/drug effects , Biomechanical Phenomena/radiation effects , Bone and Bones/drug effects , Bone and Bones/radiation effects , Gamma Rays , Sheep , Tendons/radiation effects , Wound Healing/radiation effectsABSTRACT
Terminal sterilization of tendon allografts with high dose gamma irradiation has deleterious effects on tendon mechanical properties and stability after implantation. Our goal is to minimize these effects with radio protective methods. We previously showed that radio protection via combined crosslinking and free radical scavenging maintained initial mechanical properties of tendon allografts after irradiation at 50 kGy. This study further evaluates the tissue response and simulated mechanical degradation of tendons processed with radio protective treatment, which involves crosslinking in 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide followed by soaking in an ascorbate/riboflavin-5-phosphate solution. Control untreated and treated tendons were irradiated at 50 kGy and implanted in New Zealand White rabbit knees within the joint capsule for four and 8 weeks. Tendons were also exposed to cyclic loading to 20 N at one cycle per 12 s in a collagenase solution for 150 cycles, followed by tension to failure. Control irradiated tendons displayed increased degradation in vivo, and failed prematurely during cyclic processing at an average of 25 cycles. In contrast, radio protected irradiated tendons displayed greater stability following implantation over 8 weeks, and possessed strength at 59 % of native tendons and modulus equivalent to that of native tendons after cyclic loading in collagenase. These results suggest that radio protective treatment improves the strength and the stability of tendon allografts.