Enhancing Surface Strain of Intermetallic Fuel Cell Catalysts by Composition-Induced Phase Transition.

The lattice parameter of platinum-based intermetallic compounds (IMCs), which correlates with the intrinsic activity of the oxygen reduction reaction (ORR), can be modulated by crystal phase engineering. However, the controlled preparation of IMCs with unconventional crystal structures remains highly challenging. Here, we demonstrate the synthesis of carbon-supported PtCu-based IMC catalysts with an unconventional L10 structure by a composition-regulated strategy. Experiment and machine learning reveal that the thermodynamically favorable structure changes from L11 to L10 when slight Cu atoms are substituted with Co. Benefiting from crystal-phase-induced strain enhancement, the prepared L10-type PtCu0.8Co0.2 catalyst exhibits much-enhanced mass and specific activities of 1.82 A mgPt-1 and 3.27 mA cmPt-2, which are 1.91 and 1.73 times higher than those of the L11-type PtCu catalyst, respectively. Our work highlights the important role of crystal phase in determining the surface strain of IMCs, and opens a promising avenue for the rational preparation of IMCs with different crystal phases by doping.

Air oxidation of carbon supports boosts the low-humidity fuel cell performance.

We introduce a straightforward, yet effective strategy to combat the performance decline of proton-exchange membrane fuel cells in low-humidity environments. Our method centers on air-oxidizing carbon supports, significantly improving proton and oxygen transport within the cathode catalyst layer.

Promoting ordering degree of intermetallic fuel cell catalysts by low-melting-point metal doping.

Carbon supported intermetallic compound nanoparticles with high activity and stability are promising cathodic catalysts for oxygen reduction reaction in proton-exchange-membrane fuel cells. However, the synthesis of intermetallic catalysts suffers from large diffusion barrier for atom ordering, resulting in low ordering degree and limited performance. We demonstrate a low-melting-point metal doping strategy for the synthesis of highly ordered L10-type M-doped PtCo (M = Ga, Pb, Sb, Cu) intermetallic catalysts. We find that the ordering degree of the M-doped PtCo catalysts increases with the decrease of melting point of M. Theoretic studies reveal that the low-melting-point metal doping can decrease the energy barrier for atom diffusion. The prepared highly ordered Ga-doped PtCo catalyst exhibits a large mass activity of 1.07 A mgPt-1 at 0.9 V in H2-O2 fuel cells and a rated power density of 1.05 W cm-2 in H2-air fuel cells, with a Pt loading of 0.075 mgPt cm-2.

Ordered Intermetallic PtCu Catalysts Made from Pt@Cu Core/Shell Structures for Oxygen Reduction Reaction.

Platinum-based ordered intermetallic compounds are promising low-Pt catalysts toward the oxygen reduction reaction (ORR) for high-performance fuel cells. However, the synthesis of ordered intermetallic catalysts usually requires high-temperature annealing to overcome the energy barrier for atom diffusion, which leads to inevitable sintering of catalysts and greatly reduced mass-specific activity. Herein, we developed a new strategy to synthesize PtCu-ordered intermetallic catalysts by the generation of the Pt@Cu core/shell nanoparticles (Pt@Cu NPs) by Pt-assisted H2 reduction of Cu2+ with subsequent annealing at 500-1000 °C. Compared to the commonly used wet-impregnation method, the core/shell structure starts to form ordered PtCu alloys at a lower annealing temperature (500 °C). The Pt@Cu core/shell structure avoids the necessary process of Cu atoms diffusing to Pt NPs across the carbon supports occurred during high-temperature annealing in the wet-impregnation method, which ensures the formation of PtCu NPs with higher ordering degree while annealing at the same temperature. The highly ordered small-sized PtCu catalysts prepared by the core/shell strategy exhibit higher mass activity and specific activity compared to those prepared by the wet-impregnation method. Moreover, a positive correlation between the ORR activity and the ordering degree of the intermetallic PtCu NPs is identified, which could be associated with the increase of compressive strain with the ordering degree.