ABSTRACT
In this study, Co/Ni-NC catalyst with hetero-diatomic Co/Ni active sites dispersed on nitrogen-doped carbon matrix is synthesized via the controlled pyrolysis of ZIF-8 containing Co2+ and Ni2+ compounds. Experimental characterizations and theoretical calculations reveal that Co and Ni are atomically and uniformly dispersed in pairs of CoN4-NiN4 with an intersite distance ≈0.41 nm, and there is long-range d-d coupling between Co and Ni with more electron delocalization for higher bifunctional activity. Besides, the in situ grown carbon nanotubes at the edges of the catalyst particles allow high electronic conductivity for electrocatalysis process. Electrochemical evaluations demonstrate the superior ORR and OER bifunctionality of Co/Ni-NC catalyst with a narrow potential gap of only 0.691 V and long-term durability, significantly prevailing over the single-atom Co-NC and Ni-NC catalysts and the benchmark Pt/C and RuO2 catalysts. Co/Ni-NC catalyzed Zn-air batteries achieve a high specific capacity of 771 mAh g-1 and a long continuous operation period up to 340 h with a small voltage gap of ≈0.65 V, also much superior to Pt/C-RuO2.
ABSTRACT
Monitoring non-contact high-frequency vibrations requires improving the sensitivity and linear response of iontronic pressure sensors (IPSs). In this study, we incorporate composite electrodes comprising silver nanowires (Ag NWs) and MXene into IPSs to enhance electronic conduction and pseudocapacitance. Moreover, we utilize a novel surface-pillar microstructure, along with an internally randomized multi-bubble structure within the dielectric layer, to significantly expand the linear response range of the sensor. The resulting IPS device demonstrates exceptional linear sensitivity, measuring approximately 153.83 kPa-1, across a broad pressure range of up to 260 kPa. Additionally, it exhibits long-term stability, rapid response and recovery characteristics, and remains functional underwater. Notably, these devices exhibit remarkable capabilities in monitoring ultrasonic vibrations and accurately identifying sound wave vibrations. The integration of composite electrodes, microstructure designs, and their compatibility with underwater applications positions these IPSs as highly promising tools for precise measurements and advancements in flexible electronics technology.
ABSTRACT
To enhance the connection of electroactive materials/current collector and accelerate the transport efficiency of the electrons, a binder-free electrode composed of nickel oxide anchored CoOx nanoparticles on modified commercial nickel foam (NF) was developed. The nickel oxide layer with lamellar structure which supplied skeleton to load CoOx electroactive materials directly grew on the NF surface, leading to a tight connection between the current collector and electroactive materials. The fabricated electrode exhibits a specific capacitance of 475 F/g at 1 mA/cm2. A high capacitance retention of 96% after 3000 cycles is achieved, attributed to the binding improvement at the current collector/electroactive materials interface. Moreover, an asymmetric supercapacitor with an operating voltage window of 1.4 V was assembled using oxidized NF anchored with cobalt oxide as the cathode and activated stainless steel wire mesh as the anode. The device achieves a maximum energy density of 2.43 Wh/kg and power density of 0.18 kW/kg, respectively. The modified NF substrate conducted by a facile and effective electrolysis process, which also could be applied to deposit other electroactive materials for the energy storage devices.
ABSTRACT
Transparent conductive films with hexagonal and square patterns were fabricated on poly(ethylene terephthalate) (PET) substrates by screen printing technology utilizing a poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate) (PEDOT:PSS) and silver nanowire (Ag NWs) composite ink. The printing parameters-mesh number, printing layer, mass ratio of PEDOT:PSS to Ag NWs and pattern shape-have a significant influence on the photoelectric properties of the composite films. The screen mesh with a mesh number of 200 possesses a suitable mesh size of 74 µm for printing clear and integrated grids with high transparency. With an increase in the printing layer and a decrease in the mass ratio of PEDOT:PSS to Ag NWs, the transmittance and resistance of the printed grids both decreased. When the printing layer is 1, the transmittance and resistance are 85.6% and 2.23 kΩ for the hexagonal grid and 77.3% and 8.78 kΩ for the square grid, indicating that the more compact arrangement of square grids reduces the transmittance, and the greater number of connections of the square grid increases the resistance. Therefore, it is believed that improved photoelectric properties of transparent electrodes could be obtained by designing a printing pattern with optimized printing parameters. Additionally, the Ag NWs/PEDOT:PSS composite films with hexagonal and square patterns exhibit high transparency and good uniformity, suggesting promising applications in large-area and uniform heaters.