A route for a strong increase of critical current in nanostrained iron-based superconductors.

The critical temperature Tc and the critical current density Jc determine the limits to large-scale superconductor applications. Superconductivity emerges at Tc. The practical current-carrying capability, measured by Jc, is the ability of defects in superconductors to pin the magnetic vortices, and that may reduce Tc. Simultaneous increase of Tc and Jc in superconductors is desirable but very difficult to realize. Here we demonstrate a route to raise both Tc and Jc together in iron-based superconductors. By using low-energy proton irradiation, we create cascade defects in FeSe0.5Te0.5 films. Tc is enhanced due to the nanoscale compressive strain and proximity effect, whereas Jc is doubled under zero field at 4.2 K through strong vortex pinning by the cascade defects and surrounding nanoscale strain. At 12 K and above 15 T, one order of magnitude of Jc enhancement is achieved in both parallel and perpendicular magnetic fields to the film surface.

High current superconductivity in FeSe0.5Te0.5-coated conductors at 30 tesla.

Although high-temperature superconductor cuprates have been discovered for more than 25 years, superconductors for high-field application are still based on low-temperature superconductors, such as Nb(3)Sn. The high anisotropies, brittle textures and high manufacturing costs limit the applicability of the cuprates. Here we demonstrate that the iron superconductors, without most of the drawbacks of the cuprates, have a superior high-field performance over low-temperature superconductors at 4.2 K. With a CeO(2) buffer, critical current densities >10(6) A cm(-2) were observed in iron-chalcogenide FeSe(0.5)Te(0.5) films grown on single-crystalline and coated conductor substrates. These films are capable of carrying critical current densities exceeding 10(5) A cm(-2) under 30 tesla magnetic fields, which are much higher than those of low-temperature superconductors. High critical current densities, low magnetic field anisotropies and relatively strong grain coupling make iron-chalcogenide-coated conductors particularly attractive for high-field applications at liquid helium temperatures.