Effect of multi-layer applications of self-etch universal bonding agents on the adhesion of resin composite to enamel.

To evaluate the effect of adhesive coats application on the enamel microtensile bond strength (µTBS) of universal adhesives, morphological etching pattern and their chemical interaction with hydroxyapatite (HA). Two universal adhesives were investigated: Scotchbond Universal (SBU, 3 M) and Prime&Bond Universal (PBU, Dentsply). The adhesives were applied in self-etching mode on bovine enamel (n = 8) in one (1L), two (2L) or three coats (3L) and light-cured as per manufacturers' instructions. As controls adhesives were applied to etched enamel (H3PO4-37% phosphoric acid). Bonded specimens were cut into sticks that were stored in deionized water for 24 h or 6 months prior to µTBS testing. Two-way ANOVA and Tukey's test were used for statistical analysis of bond strength with α = 5%. For morphological SEM analysis, enamel surfaces were treated as aforementioned and immediately rinsed with acetone. The intensity of monomer-calcium salt formation from each treatment was measured via infrared spectroscopy (ATR-FTIR). All treatments presented no significant reduction on µTBS after aging (p > 0.05). However, SBU attained highest µTBS when applied in 3L. PBU showed higher µTBS when applied to H3PO4 etched enamel than 1L or 2L. Etching pattern was enhanced by 3L application, particularly with PBU. Chemical interaction was notably higher for SBU than PBU, with no relevant differences with more layers or prior H3PO4-etching. The application of three adhesive coats of universal adhesives in self-etch mode using may enhance the bonding performance and etching pattern to enamel, surpassing the H3PO4-etched enamel bond for SBU. The chemical interaction with calcium from enamel is not affected by number of coats or prior phosphoric acid etching.

Preemptive use of ibuprofen and desensitizer decreases immediate tooth sensitivity after in-office bleaching: A triple-blind, randomized, placebo-controlled clinical trial.

BACKGROUND: The authors evaluated the synergistic analgesic effect of preemptive administration of 400 mg of ibuprofen (IBU) and potassium fluoride 2% (KF2), both in isolation or combination, on the painful perception of tooth sensitivity after tooth bleaching. METHODS: Fifteen patients participated in this triple-blind, randomized, placebo-controlled clinical trial. The study used a crossover design for drug administration and a split-mouth design for desensitizer agent. Four paired groups were formed: IBU plus KF2 (IBU + KF2); IBU (IBU + placebo KF); KF2 (placebo IBU + KF2), and placebo (placebo IBU + placebo KF). The outcome measure was the perception of tooth sensitivity, assessed using a visual analog scale. Data were collected at 4 different times: immediately after tooth bleaching (baseline) and after 6, 30, and 54 hours. Statistical analysis was performed using the Friedman test and relative risk. RESULTS: IBU plus KF2 was found to be more effective in reducing tooth sensitivity immediately after bleaching (baseline) compared with the placebo group (P < .05). The risk of experiencing moderate or severe tooth sensitivity was approximately 4 times higher in the placebo group than in the IBU plus KF2 group (relative risk, 4.00; 95% CI, 1.01 to 15.81; P = .025). CONCLUSIONS: The combined use of 400 mg of IBU and KF2 appears to be beneficial in managing postbleaching tooth sensitivity. It provides a superior analgesic effect compared with placebo. PRACTICAL IMPLICATIONS: The preemptive administration of IBU plus KF2 reduces tooth sensitivity after tooth whitening when compared with placebo. This clinical trial was registered in the Brazilian Clinical Trials Registry Platform. The registration number is U1111-1249-8191.

Association of solvents improves selected properties of experimental dental adhesives

Abstract: The aim of the study was to evaluate how the association of solvents (tetrahydrofuran [THF], dimethyl sulfoxide [DMSO], ethanol [ET] or acetone [ACT]) with experimental dental adhesives affects selected properties of experimental dental adhesives and dentin bond durability. Six adhesive combinations were prepared containing: 30 % ET, 30 % ACT, 30 % THF, 28 % ET + 2 % DMSO (ET+DMSO), 15 % ethanol + 15 % THF (ET+THF), or 28 % THF + 2 % DMSO (THF+DMSO). Thirty-six molars (n = 6) were cut to expose the coronary dentin, and were randomly divided according to the adhesives. They were restored, and then cut into resindentin sticks (1 mm²), and stored in distilled water for 24 h or 6 months, until conducting the microtensile bond strength and nanoleakage tests. Other experiments performed with adhesives included viscosity assessment using a rheometer, and degree of conversion using Fourier-transform infrared spectroscopy (FTIR). The data were analyzed statistically using two-way ANOVA and Tukey's test (p < 0.05). The adhesive formulated exclusively with THF showed the highest viscosity, followed by ET+THF, which obtained the highest degree of conversion compared to ET, and THF alone. ET+DMSO obtained the highest 24-h and aged bond strengths (p < 0.05). ET+THF increased the nanoleakage slightly after 6 months, but attained the only gap-free adhesive interface among all the groups. The combination of alternative solvents, particularly THF, with conventional ones (ET) has improved chemical properties, and the dentin bonding of experimental simplified adhesives.