ABSTRACT
Co-Zr amorphous alloys exhibit soft magnetic properties, whereas the Co-rich crystalline magnetic phases in this alloy system displayed a hard magnetic behavior. In this study, an initial two-phase Co-Zr composite with an overall composition of 75 at.% Co and 25 at.% Zr was processed by high-pressure torsion (HPT), and the effects of severe plastic deformation and subsequent thermal treatment on the composite's structural evolution and its magnetic properties were investigated. HPT processing allowed us to achieve an amorphous microstructure with low coercivity in its as-deformed state. To further tune the alloy's magnetic properties and study its crystallization behavior, various annealed states were investigated. The microstructural properties were correlated with the magnetic properties, and a decreasing coercivity with increasing annealing temperatures was observed despite the onset of crystallization in the amorphous alloy. At higher annealing temperatures, coercivity increased again. The results appear promising for obtaining tuneable rare-earth free magnetic materials by severe plastic deformation.
ABSTRACT
Exchange-coupling between soft- and hard-magnetic phases plays an important role in the engineering of novel magnetic materials. To achieve exchange coupling, a two-phase microstructure is necessary. This interface effect is further enhanced if both phase dimensions are reduced to the nanometer scale. At the same time, it is challenging to obtain large sample dimensions. In this study, powder blends and ball-milled powder blends of Fe-SmCo5 are consolidated and are deformed by high-pressure torsion (HPT), as this technique allows us to produce bulk magnetic materials of reasonable sizes. Additionally, the effect of severe deformation by ball-milling and severe plastic deformation by HPT on exchange coupling in Fe-SmCo5 composites is investigated. Due to the applied shear deformation, it is possible to obtain a texture in both phases, resulting in an anisotropic magnetic behavior and an improved magnetic performance.
ABSTRACT
The paper describes the capability of magnetic softening of a coarse-grained bulk material by a severe deformation technique. Connecting the microstructure with magnetic properties, the coercive field decreases dramatically for grains smaller than the magnetic exchange length. This makes the investigation of soft magnetic properties of severely drawn pearlitic wires very interesting. With the help of the starting two-phase microstructure, it is possible to substantially refine the material, which allows the investigation of magnetic properties for nanocrystalline bulk material. Compared to the coarse-grained initial, pearlitic state, the coercivities of the highly deformed wires decrease while the saturation magnetization values increase-even beyond the value expectable from the individual constituents. The lowest coercivity in the drawn state is found to be 520 A m-1 for a wire of 24-µm thickness and an annealing treatment has a further positive effect on it. The decreasing coercivity is discussed in the framework of two opposing models: grain refinement on the one hand and dissolution of cementite on the other hand. Auxiliary measurements give a clear indication for the latter model, delivering a sufficient description of the observed evolution of magnetic properties.
ABSTRACT
Samples consisting of one ferromagnetic and one diamagnetic component which are immiscible at the thermodynamic equilibrium (Co-Cu, Fe-Cu, Fe-Ag) are processed by high-pressure torsion at various compositions. The received microstructures are investigated by electron microscopy and synchrotron X-ray diffraction, showing a microstructural saturation. Results gained from microstructural investigations are correlated to magnetometry data. The Co-Cu samples show mainly ferromagnetic behavior and a decrease in coercivity with increasing Co-content. The saturation microstructure of Fe-Cu samples is found to be dual phase. Results of magnetic measurements also revealed the occurrence of two different magnetic phases in this system. For Fe-Ag, the microstructural and magnetic results indicate that no intermixing between the elemental phases takes place.