ABSTRACT
A new sample cell concept for the analysis of liquids or solid-liquid interfaces using soft X-ray spectroscopy is presented, which enables the complete sealing of the cell as well as the transport into vacuum via, for example, a load-lock system. The cell uses pressure monitoring and active as well as passive pressure regulation systems, thereby facilitating the full control over the pressure during filling, sealing, evacuation, and measurement. The cell design and sample preparation as well as the crucial sealing procedure are explained in detail. As a first proof-of-principle experiment, successful nitrogen K-edge fluorescence yield near-edge X-ray absorption fine structure experiments of a biomolecular solution are presented. For this purpose, it is shown that the careful evaluation of all involved parameters, such as window type or photon flux, is desirable for optimizing the experimental result.
ABSTRACT
X-ray fluorescence (XRF) analysis is one of the standard tools for the analysis of stratified materials and is widely applied for the investigation of electronics and coatings. The composition and thickness of the layers can be determined quantitatively and non-destructively. Recent work showed that these capabilities can be extended towards retrieving stratigraphic information like concentration depth profiles using angle-resolved XRF (ARXRF). This paper introduces an experimental sample chamber which was developed as a multi-purpose tool enabling different measurement geometries suited for transmission measurements, conventional XRF, ARXRF, etc. The chamber was specifically designed for attaching all kinds of laboratory X-ray sources for the soft and hard X-ray ranges as well as various detection systems. In detail, a setup for ARXRF using an X-ray tube with a polycapillary X-ray lens as source is presented. For such a type of setup, both the spectral and lateral characterizations of the radiation field are crucial for quantitative ARXRF measurements. The characterization is validated with the help of a stratified validation sample.
ABSTRACT
Organosilanes are used routinely to functionalize various support materials for further modifications. Nevertheless, reliable quantitative information about surface functional group densities after layer formation is rarely available. Here, we present the analysis of thin organic nanolayers made from nitrogen containing silane molecules on naturally oxidized silicon wafers with reference-free total reflection X-ray fluorescence (TXRF) and X-ray photoelectron spectroscopy (XPS). An areic density of 2-4 silane molecules per nm(2) was calculated from the layer's nitrogen mass deposition per area unit obtained by reference-free TXRF. Complementary energy and angle-resolved XPS (ER/AR-XPS) in the Si 2p core-level region was used to analyze the outermost surface region of the organic (silane layer)-inorganic (silicon wafer) interface. Different coexisting silicon species as silicon, native silicon oxide, and silane were identified and quantified. As a result of the presented proof-of-concept, absolute and traceable values for the areic density of silanes containing nitrogen as intrinsic marker are obtained by calibration of the XPS methods with reference-free TXRF. Furthermore, ER/AR-XPS is shown to facilitate the determination of areic densities in (mono)layers made from silanes having no heteroatomic marker other than silicon. After calibration with reference-free TXRF, these areic densities of silane molecules can be determined when using the XPS component intensity of the silane's silicon atom.
ABSTRACT
The present work shows results on elemental distribution analyses in Cu(In,Ga)Se2 thin films for solar cells performed by use of wavelength-dispersive and energy-dispersive X-ray spectrometry (EDX) in a scanning electron microscope, EDX in a transmission electron microscope, X-ray photoelectron, angle-dependent soft X-ray emission, secondary ion-mass (SIMS), time-of-flight SIMS, sputtered neutral mass, glow-discharge optical emission and glow-discharge mass, Auger electron, and Rutherford backscattering spectrometry, by use of scanning Auger electron microscopy, Raman depth profiling, and Raman mapping, as well as by use of elastic recoil detection analysis, grazing-incidence X-ray and electron backscatter diffraction, and grazing-incidence X-ray fluorescence analysis. The Cu(In,Ga)Se2 thin films used for the present comparison were produced during the same identical deposition run and exhibit thicknesses of about 2 µm. The analysis techniques were compared with respect to their spatial and depth resolutions, measuring speeds, availabilities, and detection limits.