ABSTRACT
Adsorption of model polar (water) and non-polar (n-hexane) compounds on the surface of oxidized and non-oxidized carbon nanotube (CNT) supports at different stages of Co/CNT catalyst preparation has been studied to reveal the influence of the surface functionalization of the CNT support on the catalyst selectivity in Fischer-Tropsch synthesis (FTS). Dynamic vapor sorption experiments showed that defunctionalization of the surface of the CNT support during catalyst annealing and reduction led to its hydrophobization and, as a result, no noticeable difference was observed between the adsorption properties of the oxidized and non-oxidized supports towards water and hydrocarbons. Therefore, oxidation of the CNT support does not significantly affect the adsorption properties of the supported catalyst and it is not a crucial factor for the catalyst selectivity in FTS.
ABSTRACT
Thermal defunctionalization of oxidized jellyfish-like few-layer graphene nanoflakes was studied under non-isothermal conditions by simultaneous thermal analysis. Activation energies for thermal decomposition of different oxygen functional groups were calculated by the Kissinger method and compared with those for oxidized carbon nanotubes. Oxygen content in graphene nanoflakes was found to significantly affect the decomposition activation energies of carboxylic and keto/hydroxy acids because of their acceptor properties and strong distortion of the graphene layers at the edges of the nanoflakes. The structure of the carbon material and the oxygen chemical state significantly influence the decomposition kinetics of thermally stable oxygen-containing groups. The activation energy for thermal decomposition of phenol groups (110-150 kJ mol-1) is close to that for graphene oxide reduction.